Abstract: This paper presents the experimental results of high-density polyethylene cable spacers for 22 kV distribution systems under salt water dip wheel test based on IEC 62217. The strength of anti-tracking and anti-erosion of cable spacer surface was studied in this study. During the test, dry band arc and corona discharge were observed on cable spacer surface. After 30,000 cycles of salt water dip wheel test, obviously surface erosion and tracking were observed especially on the ground end. Chemical analysis results by fourier transforms infrared spectroscopy showed chemical changed from oxidation and carbonization reaction on tested cable spacer. Increasing of C=O and C=C bonds confirmed occurrence of these reactions.
Abstract: This paper presents the experimental results on
ageing deterioration of silicone rubber outdoor polymer insulator
under salt water dip wheel test based on IEC 62217. In order to comparison effect of chemical contents, silicone rubber outdoor
polymer insulators having same configuration and leakage distant
from two manufactures were tested together continuously 30,000 test cycles. Many discharge activities were observed in during the test.
After 30,000 test cycles, in spite of same configuration, differences in
degree of surface aging were observed. Physical analysis such as
decreasing in hydrophobicity and increasing in hardness
measurement were measured on two-type tested specimen surface in order to confirm degree of surface ageing. Furthermore, chemical
analysis by ATR-FTIR to diagnose the chemical change of tested
specimen surface was conducted to confirm the physical analysis results.
Abstract: This paper presents the experimental results of silicone rubber polymer insulators for 22 kV systems under salt water dip wheel test based on IEC 62217. Straight shed silicone rubber polymer insulators having leakage distance 685 mm were tested continuously 30,000 cycles. One test cycle includes 4 positions, energized, de-energized, salt water dip and deenergized, respectively. For one test cycle, each test specimen remains stationary for about 40 second in each position and takes 8 second for rotate to next position. By visual observation, sever surface erosion was observed on the trunk near the energized end of tested specimen. Puncture was observed on the upper shed near the energized end. In addition, decreasing in hydrophobicity and increasing in hardness were measured on tested specimen comparing with new specimen. Furthermore, chemical analysis by ATR-FTIR was conducted in order to elucidate the chemical change of tested specimens comparing with new specimen.