Abstract: The goal of this work is to develop sustainable and durable ceramic cellular structures using widely available natural resources- clay and milled waste glass. Present paper describes method of obtaining clay ceramic foam (CCF) with addition of milled waste glass in 5, 7 and 10 wt% by direct foaming with high speed mixer-disperser (HSMD). For more efficient clay and waste glass milling and mixing, the high velocity disintegrator was used. The CCF with 5, 7, and 10 wt% were obtained at 900, 950, 1000 and 1050 °C firing temperature and they have demonstrated mechanical compressive strength for all 12 samples ranging from 3.8 to 14.3 MPa and porosity 76-65%. Obtained CCF has compressive strength 14.3 MPa and porosity 65.3%.
Abstract: Present paper describes method of obtaining clay
ceramic foam (CCF) and foam concrete (FC), by direct foaming with
high speed mixer-disperser (HSMD). Three foaming agents (FA) are
compared for the FC and CCF production: SCHÄUMUNGSMITTEL
W 53 FLÜSSIG (Zschimmer & Schwarz Gmbh, Germany), SCF-
1245 (Sika, test sample, Latvia) and FAB-12 (Elade, Latvija). CCF
were obtained at 950, 1000°C, 1150°C and 1150°C firing temperature
and have mechanical compressive strength 1.2, 2.55 and 4.3 MPa and
porosity 79.4, 75.1, 71.6%, respectively. Obtained FC has 6-14 MPa
compressive strength and porosity 44-55%. The goal of this work
was development of a sustainable and durable ceramic cellular
structures using HSMD.
Abstract: Corrugated wire mesh laminates (CWML) are a class
of engineered open cell structures that have potential for applications
in many areas including aerospace and biomedical engineering. Two
different methods of fabricating corrugated wire mesh laminates from
stainless steel, one using a high temperature Lithobraze alloy and the
other using a low temperature Eutectic solder for joining the
corrugated wire meshes are described herein. Their implementation is
demonstrated by manufacturing CWML samples of 304 and 316
stainless steel (SST). It is seen that due to the facility of employing
wire meshes of different densities and wire diameters, it is possible to
create CWML laminates with a wide range of effective densities. The
fabricated laminates are tested under uniaxial compression. The
variation of the compressive yield strength with relative density of the
CWML is compared to the theory developed by Gibson and Ashby for
open cell structures [22]. It is shown that the compressive strength of
the corrugated wire mesh laminates can be described using the same
equations by using an appropriate value for the linear coefficient in the
Gibson-Ashby model.