Abstract: An experimental program is conducted in this research to investigate the influence of basalt fibers and steel fibers on the flexural behavior of RC beams. Reinforced concrete beams are constructed using steel fiber concrete and basalt fiber concrete. Steel and basalt fibers are included in a percentage of 15% and 2.5% of the total cement weight, respectively. Test results have shown that basalt fibers have increased the load carrying capacity of the beams up to 30% and the maximum deflection to almost 2.4 times that measured in the control specimen. It has also shown that steel fibers have increased the load carrying capacity of the beams up to 47% and the ultimate deflection is almost duplicated compared to the control beam. Steel and basalt fibers have increased the ductility of the reinforced concrete beams.
Abstract: Due to the aging of bridges, increasing of maintenance costs and decreasing of structural safety is occurred. The steel corrosion of reinforced concrete bridge is the most common problem and this phenomenon is accelerating due to abnormal weather and increasing CO2 concentration due to climate change. To solve these problems, composite members using textile have been studied. A textile reinforced concrete can reduce carbon emissions by reduced concrete and without steel bars, so a lot of structural behavior studies are needed. Therefore, in this study, textile reinforced concrete beam was made and flexural test was performed. Also, the change of flexural strength according to the prestressing was conducted. As a result, flexural strength of TRC with prestressing was increased compared and flexural behavior was shown as reinforced concrete.
Abstract: This study presents an overview of the work carried out by the use of wood waste as coarse aggregate in mortar. The paper describes experimental and numerical investigations carried on pervious concrete made of wood chips and also sheds lights on the mechanical properties of this new product. The properties of pervious wood-concrete such as strength, elastic modulus, and failure modes are compared and evaluated. The characterization procedure of the mechanical properties of wood waste ash are presented and discussed. The numerical and tested load–deflection response results are compared. It was observed that the numerical results are in good agreement with the experimental results.
Abstract: Non-crimp three-dimensional (3D) orthogonal carbon fabrics are one of the useful textiles reinforcements in composites. In this paper, flexural and bending properties of a carbon non-crimp 3D orthogonal woven reinforcement are experimentally investigated. The present study is focused on the understanding and measurement of the main bending parameters including flexural stress, strain, and modulus. For this purpose, the three-point bending test method is used and the load-displacement curves are analyzed. The influence of some weave's parameters such as yarn type, geometry of structure, and fiber volume fraction on bending behavior of non-crimp 3D orthogonal carbon fabric is investigated. The obtained results also represent a dataset for the simulation of flexural behavior of non-crimp 3D orthogonal weave carbon composite reinforcement.
Abstract: Promotion of the Fiber Reinforced Concrete (FRC) as a construction material for civil engineering projects has invoked numerous researchers to investigate their mechanical behavior. Even though there is satisfactory information about the effects of fiber type and length, concrete mixture, casting type and other variables on the strength and deformability parameters of FRC, the numerical modeling of such materials still needs research attention. The focus of this study is to investigate the feasibility of Concrete Damaged Plasticity (CDP) model in prediction of Macro-synthetic FRC structures behavior. CDP model requires the tensile behavior of concrete to be well characterized. For this purpose, a series of uniaxial direct tension and four point bending tests were conducted on the notched specimens to define bilinear tension softening (post-peak tension stress-strain) behavior. With these parameters obtained, the flexural behavior of macro-synthetic FRC beams were modeled and the results showed a good agreement with the experimental measurements.
Abstract: Natural fibers are used in polymer composites to
improve mechanical properties to replace inorganic reinforcing
agents produced by non-renewable resources. The present study
investigates the tensile and flexural behaviors of palm fibers-high
density polyethylene (HDPE) composite as a function of volume
fraction. The surface of the fibers was treated by mercerization
treatments to improve the wetting behavior of the apolar HDPE. The
treatment characterization was obtained by scanning electron
microscopy, X-Ray diffraction and infrared spectroscopy. Results
evidences that a good adhesion interfacial between fibers-matrix
caused an increase strength and modulus flexural as well as tensile
strength in the modified fibers/HDPE composites when compared to
the pure HDPE and untreated fibers reinforced composites.
Abstract: The aesthetic qualities and the versatility of reinforced
concrete have made it a popular choice for many architects and
structural engineers. Therefore, the exploration of natural materials
such as gravels and sands as well as lime-stone for cement production
is increasing to produce a concrete material. The exploration must
affect to the environment. Therefore, the using of the concrete
materials should be as efficient as possible. According to its natural
behavior of the concrete material, it is strong in compression and weak
in tension. Therefore the contribution of the tensile stresses of the
concrete to the flexural capacity of the beams is neglected. However,
removing of concrete on tension zone affects to the decreasing of
flexural capacity. Introduce the strut action of truss structures may an
alternative to solve the decreasing of flexural capacity. A series of
specimens were prepared to clarify the effect of the truss structures in
the concrete beams without concrete on the tension zone. Results
indicated that the truss system is necessary for the external reinforced
concrete beams. The truss system of concrete beam without concrete
on tension zone (BR) could develop almost same capacity to the
normal beam (BN). It can be observed also that specimens BR has
lower number of cracks than specimen BN. This may be caused by the
fact that there was no bonding effect on the tensile reinforcement on
specimen BR to distribute the cracks.
Abstract: The aim of this work is to use an environmental, cheap; organic non-traditional admixture to improve the structural behavior of sustainable reinforced concrete beams contains different ratios of recycled concrete aggregate. The used admixture prepared by using wastes from vegetable oil industry. Under and over reinforced concrete beams made from natural aggregate and different ratios of recycled concrete aggregate were tested under static load until failure. Eight beams were tested to investigate the performance and mechanism effect of admixture on improving deformation characteristics, modulus of elasticity and toughness of tested beams. Test results show efficiency of organic admixture on improving flexural behavior of beams contains 20% recycled concrete aggregate more over the other ratios.
Abstract: An experimental study was conducted to investigate the effect of hooked-end steel fibers on the flexural behavior of normal and high strength concrete matrices. The fibers content appropriate for the concrete matrices investigated was also determined based on flexural tests on standard prisms. Parameters investigated include: matrix compressive strength ranging from 45 MPa to 70 MPa, corresponding to normal and high strength concrete matrices respectively; fibers volume fraction including 0, 0.5%, 0.76% and 1%, equivalent to 0, 40, 60, and 80 kg/m3 of hooked-end steel fibers respectively. Test results indicated that flexural strength and toughness of normal and high strength concrete matrices were significantly improved with the increase in the fibers content added; whereas a slight improvement in compressive strength was observed for the same matrices. Furthermore, the test results indicated that the effect of increasing the fibers content was more pronounced on increasing the flexural strength of high strength concrete than that of normal concrete.
Abstract: Existing underground pipe jacking methods use a
reinforcing rod in a steel tube to obtain structural stiffness. However,
some problems such as inconvenience of works and expensive
materials resulted from limited working space and reinforcing works
are existed. To resolve these problems, a new pipe jacking method,
namely PST (Prestressed Segment Tunnel) method, was developed
which used joint to connect the steel segment and form erection
structure. For evaluating the flexural capacity of the PST method
structure, a experimental test was conducted. The parameters
considered in the test were span-to-depth ratio of segment, diameter of
steel tube at the corner, prestressing force, and welding of joint. The
flexural behaviours with the effect of load capacity in serviceability
state according to different parameters were examined.. The frame
with long segments could increase flexural stiffness and the specimen
with large diameter of concave corner showed excellent resistance
ability to the negative moment. In addition, welding of joints increased
the flexural capacity.
Abstract: This article presents the analysis of experimental values regarding cracking pattern, specific strains and deformability for reinforced high strength concrete beams. The beams have the concrete class C80/95 and a longitudinal reinforcement ratio of 2.01%, respectively 3.39%. The elements were subjected to flexure under static short-term and long-term loading. The experimental values are compared with calculation values using the design relationships according to Eurocode 2.