Abstract: Alkali-active sandstone aggregate was ground by vertical and ball mill into particles with residue over 45 μm less than 12%, and investigations have been launched on particles distribution and characterization of ground sandstone powder, fluidity, heat of hydration, strength as well as hydration products morphology of pastes with incorporation of ground sandstone powder. Results indicated that ground alkali-active sandstone powder with residue over 45 μm less than 8% was easily obtainable, and specific surface area was more sensitive to characterize its fineness with extension of grinding length. Incorporation of sandstone powder resulted in higher water demand and lower strength, advanced hydration of C3A and C2S within 3days and refined pore structure. Based on its manufacturing, characteristics and influence on properties of pastes, it was concluded that sandstone powder was a good selection for use in concrete as mineral admixture.
Abstract: This paper reports the strength and durability properties of high strength high performance concrete incorporating rice husk ash (RHA) having high silica, low carbon content and appropriate fineness. In this study concrete containing 10%, 15% and 20% RHA as cement replacement and water to binder ratio of 0.25 were investigated. The results show that increasing amount of RHA increases the dosage of superplasticizer to maintain similar workability. Partial replacement of cement with RHA did not increase the early age compressive strength of concrete. However, concrete containing RHA showed higher compressive strength at later ages. The results showed that compressive strength of concrete in the 90-115 MPa range can be obtained at 28 curing days and the durability properties of RHA concrete performed better than that of control concrete. The water absorption of concrete incorporating 15% RHA exhibited the lowest value. The porosity of concrete is consistent with water absorption whereby higher replacement of RHA decreased the porosity of concrete. There is a positive correlation between reducing porosity and increasing compressive strength of high strength high performance concrete. The results also indicate that up to 20% of RHA incorporation could be advantageously blended with cement without adversely affecting the strength and durability properties of concrete.
Abstract: This paper represents the results of experimental work to investigate the suitability of a waste material (WM) for soft soil stabilisation. In addition, the effect of particle size distribution (PSD) of the waste material on its performance as a soil stabiliser was investigated. The WM used in this study is produced from the incineration processes in domestic energy power plant and it is available in two different grades of fineness (coarse waste material (CWM) and fine waste material (FWM)). An intermediate plasticity silty clayey soil with medium organic matter content has been used in this study. The suitability of the CWM and FWM to improve the physical and engineering properties of the selected soil was evaluated dependant on the results obtained from the consistency limits, compaction characteristics (optimum moisture content (OMC) and maximum dry density (MDD)); along with the unconfined compressive strength test (UCS). Different percentages of CWM were added to the soft soil (3, 6, 9, 12 and 15%) to produce various admixtures. Then the UCS test was carried out on specimens under different curing periods (zero, 7, 14, and 28 days) to find the optimum percentage of CWM. The optimum and other two percentages (either side of the optimum content) were used for FWM to evaluate the effect of the fineness of the WM on UCS of the stabilised soil. Results indicated that both types of the WM used in this study improved the physical properties of the soft soil where the index of plasticity (IP) was decreased significantly. IP was decreased from 21 to 13.64 and 13.10 with 12% of CWM and 15% of FWM respectively. The results of the unconfined compressive strength test indicated that 12% of CWM was the optimum and this percentage developed the UCS value from 202kPa to 500kPa for 28 days cured samples, which is equal, approximately 2.5 times the UCS value for untreated soil. Moreover, this percentage provided 1.4 times the value of UCS for stabilized soil-CWA by using FWM which recorded just under 700kPa after 28 days curing.
Abstract: Fly ash (FA) thanks to the significant presence of SiO2
and Al2O3 as the main components is a potential raw material for
geopolymers production. Mechanical activation is a method for
improving FA reactivity and also the porosity of final mixture; those
parameters can be analysed through sorption properties. They have
direct impact on the durability of fly ash based geopolymer mortars.
In the paper, effect of FA fineness on sorption properties of
geopolymers based on sodium silicate, as well as relationship
between fly ash fineness and apparent density, compressive and
flexural strength of geopolymers are presented. The best results in the
evaluated area reached the sample H1, which contents the highest
portion of particle under 20μm (100% of GFA). The interdependence
of individual tested properties was confirmed for geopolymer
mixtures corresponding to those in the cement based mixtures: higher
is portion of fine particles < 20μm, higher is strength, density and
lower are sorption properties. The compressive strength as well as
sorption parameters of the geopolymer can be reasonably controlled
by grinding process and also ensured by the higher share of fine
particle (to 20μm) in total mass of the material.
Abstract: A large amount of blast furnace slag is generated in
China. Most ground granulated blast furnace slag (GGBS) however
ends up in low-grade applications. Blast furnace slag, ground to an
appropriate fineness, can be used as a partial replacement of
cementitious material in concrete. The potential for using GGBS in
structural concrete, e.g. concrete beams and columns is investigated
at Xi’an Jiaotong-Liverpool University (XJTLU). With 50% of CEM
I cement replaced with GGBS, peak hydration temperatures
determined in a suspended concrete slab reduced by 20%. This
beneficiary effect has not been further improved with 70% of CEM I
replaced with GGBS. Partial replacement of CEM I with GGBS has a
retardation effect on the early-age strength of concrete. More GGBS
concrete mixes will be conducted to identify an ‘optimum’
replacement level which will lead to a reduced thermal loading,
without significantly compromising the early-age strength of
concrete.
Abstract: Properties of Portland cement mixtures with various
fractions of metakaolin were studied. 10% of Portland cement CEM I
42.5 R was replaced by different fractions of high reactivity
metakaolin with defined chemical and mineralogical properties.
Various fractions of metakaolin were prepared by jet mill classifying
system. There is a clear trend between fineness of metakaolin and
hydration heat development. Due to metakaolin presence in mixtures
the compressive strength development of mortars is rather slower for
coarser fractions but 28-day flexural strengths are improved for all
fractions of metakaoline used in mixtures compared to reference
sample of pure Portland cement. Yield point, plastic viscosity and
adhesion of fresh pastes are considerably influenced by fineness of
metakaolin used in cement pastes.
Abstract: Paper focuses on experimental testing of possibilities of mechanical activation of fly ash and observation of influence of specific surface and granulometry on final properties of fresh and hardened concrete. Mechanical grinding prepared various fineness of fly ash, which was classed by specific surface in accordance with Blain and their granulometry was determined by means of laser granulometer. Then, sets of testing specimens were made from mix designs of identical composition with 25% or Portland cement CEM I 42.5 R replaced with fly ash with various specific surface and granulometry. Mix design with only Portland cement was used as reference. Mix designs were tested on consistency of fresh concrete and compressive strength after 7, 28, 60 and 90 days.
Abstract: Our objectives were to evaluate the effects of sire
breed, type of protein supplement, level of supplementation and sex
on wool spinning fineness (SF), its correlations with other wool
characteristics and prediction accuracy in F1 Merino crossbred lambs.
Texel, Coopworth, White Suffolk, East Friesian and Dorset rams
were mated with 500 purebred Merino dams at a ratio of 1:100 in
separate paddocks within a single management system. The F1
progeny were raised on ryegrass pasture until weaning, before forty
lambs were randomly allocated to treatments in a 5 x 2 x 2 x 2
factorial experimental design representing 5 sire breeds, 2
supplementary feeds (canola or lupins), 2 levels of supplementation
(1% or 2% of liveweight) and sex (wethers or ewes). Lambs were
supplemented for six weeks after an initial three weeks of adjustment,
wool sampled at the commencement and conclusion of the feeding
trial and analyzed for SF, mean fibre diameter (FD), coefficient of
variation (CV), standard deviation, comfort factor (CF), fibre
curvature (CURV), and clean fleece yield. Data were analyzed using
mixed linear model procedures with sire fitted as a random effect,
and sire breed, sex, supplementary feed type, level of
supplementation and their second-order interactions as fixed effects.
Sire breed (P
Abstract: In this paper, the effect of addition the dune sand powder (DSP) on development of compressive strength and hydration of cement pastes was investigated as a function of water/binder ratio, was varied, on the one hand, the percentage of DSP and on the other, the fineness of DSP. In order to understand better the pozzolanic effect of dune sand powder in cement pastes, we followed the mixtures hydration (50% Pure Lime + 50% DSP) by X-ray diffraction. These mixtures the pastes present a hydraulic setting which is due to the formation of a C-S-H phase (calcium silicate hydrate). The latter is semi-crystallized. This study is a simplified approach to that of the mixtures (80% ordinary Portland cement + 20% DSP), in which the main reaction is the fixing of the lime coming from the cement hydration in the presence of DSP, to form calcium silicate hydrate semi-crystallized of second generation. The results proved that up to (20% DSP) as Portland cement replacement could be used with a fineness of 4000 cm²/g without affecting adversely the compressive strength. After 28 days, the compressive strength at 5, 10 and 15% DSP is superior to Portland cement, with an optimum effect for a percentage of the order of 5% to 10% irrespective of the w/b ratio and fineness of DSP.
Abstract: The setting agent Ca(OH)2 for activation of slag
cement is used in the proportions of 0%, 2%, 4%, 6%, 8% and 10%
by various methods (substitution and addition by mass of slag
cement). The physical properties of slag cement activated by the
calcium hydroxide at anhydrous and hydrated states (fineness,
particle size distribution, consistency of the cement pastes and setting
times) were studied. The activation method by the mineral activator
of slag cement (latent hydraulicity) accelerates the hydration process
and reduces the setting times of the cement activated.
Abstract: The effect of artificial pozzolan (waste brick) on the
physico-chemical properties of cement manufactured was
investigated. The waste brick is generated by the manufacture of
bricks. It was used in the proportions of 0%, 5%, 10%, 15% and 20%
by mass of cement to study its effect on the physico-chemical
properties of cement incorporating artificial pozzolan. The physicochemical
properties of cement at anhydrous state and the hydrated
state (chemical composition, specific weight, fineness, consistency of
the cement paste and setting times) were studied. The experimental
results obtained show that the quantity of pozzolanic admixture
(waste brick) of cement manufactured is the principal parameter who
influences on the variation of the physico-chemical properties of the
cement tested.
Abstract: Demolitions of buildings have created a lot of waste
and one of it is clay bricks. The waste clay bricks were ground to
roughly cement fineness and used to partially replaced cement at
10%, 20% and 30% with w/b ratio of 0.6 and tested at 7, 28, 60, 90
and 120 days. The result shows that the compressive strength of GCB
concrete increases over age however, decreases as the level of
replacements increases. It was also found that 10% replacement of
GCB gave the highest compressive strength, however for optimum
replacement, 30% was chosen as it still attained strength of grade 30
concrete. In terms of durability performances, results show that GCB
replacement up to 30% was found to be efficient in reducing water
absorption as well as water permeability. These studies show that
GCB has the potential to be used as partial cement replacement in
making concrete.
Abstract: Biodiesel production results in glycerol production as
the main by-product in biodiesel industry.One of the utilizations of
glycerol obtained from biodiesel production is as a cement grinding
aid (CGA). Results showed that crude glycerol content was 40.19%
whereas pure glycerol content was 82.15%. BSS value of the cement
with CGA supplementation was higher than that of nonsupplemented
cement (blank) indicating that CGA-supplemented
cement had higher fineness than the non-supplemented one. It was
also found that pure glycerol 95% and TEA 5% at 80ºC was the
optimum CGA used to result in finest cement with BSS value of
4.836 cm2/g. Residue test showed that the smallest percent residue
value (0.11%) was obtained in cement with supplementation of pure
glycerol 95% and TEA 5%. Results of residue test confirmed those of
BSS test showing that cement with supplementation of pure glycerol
95% and TEA 5% had the finest particle size.