Abstract: Biocomposites is a field that has gained much scientific attention due to the current substantial consumption of non-renewable resources and the environmentally harmful disposal methods required for traditional polymer composites. Research on natural fiber reinforced polyhydroxyalkanoates (PHAs) has gained considerable momentum over the past decade. There is little work on PHAs reinforced with unidirectional (UD) natural fibers and little work on using epoxidized natural rubber (ENR) as a toughening agent for PHA-based biocomposites. In this work, we prepared polyhydroxybutyrate-co-valerate (PHBV) biocomposites reinforced with UD 30 wt.% flax fibers and evaluated the use of ENR with 50% epoxidation (ENR50) as a toughening agent for PHBV biocomposites. Quasi-unidirectional flax/PHBV composites were prepared by hand layup, powder impregnation followed by compression molding. Toughening agents – polybutylene adiphate-co-terephthalate (PBAT) and ENR50 – were cryogenically ground into powder and mechanically mixed with main matrix PHBV to maintain the powder impregnation process. The tensile, flexural and impact properties of the biocomposites were measured and morphology of the composites examined using optical microscopy (OM) and scanning electron microscopy (SEM). The UD biocomposites showed exceptionally high mechanical properties as compared to the results obtained previously where only short fibers have been used. The improved tensile and flexural properties were attributed to the continuous nature of the fiber reinforcement and the increased proportion of fibers in the loading direction. The improved impact properties were attributed to a larger surface area for fiber-matrix debonding and for subsequent sliding and fiber pull-out mechanisms to act on, allowing more energy to be absorbed. Coating cryogenically ground ENR50 particles with PHBV powder successfully inhibits the self-healing nature of ENR-50, preventing particles from coalescing and overcoming problems in mechanical mixing, compounding and molding. Cryogenic grinding, followed by powder impregnation and subsequent compression molding is an effective route to the production of high-mechanical-property biocomposites based on renewable resources for high-obsolescence applications such as plastic casings for consumer electronics.
Abstract: This work presents an improved single fiber pull-out
test for fiber/matrix interface characterization. This test has been
used to study the Inter-Facial Shear Strength ‘IFSS’ of hemp fibers
reinforced polypropylene (PP). For this aim, the fiber diameter
has been carefully measured using a tomography inspired method.
The fiber section contour can then be approximated by a circle
or a polygon. The results show that the IFSS is overestimated if
the circular approximation is used. The Influence of the molding
temperature on the IFSS has also been studied. We find that a molding
temperature of 183◦C leads to better interfacial properties. Above or
below this temperature the interface strength is reduced.
Abstract: Post cracking behavior and load –bearing capacity of
the steel fiber reinforced high-strength concrete (SFRHSC) are
dependent on the number of fibers are crossing the weakest crack
(bridged the crack) and their orientation to the crack surface. Filling
the mould by SFRHSC, fibers are moving and rotating with the
concrete matrix flow till the motion stops in each internal point of the
concrete body. Filling the same mould from the different ends
SFRHSC samples with the different internal structures (and different
strength) can be obtained. Numerical flow simulations (using Newton
and Bingham flow models) were realized, as well as single fiber
planar motion and rotation numerical and experimental investigation
(in viscous flow) was performed. X-ray pictures for prismatic
samples were obtained and internal fiber positions and orientations
were analyzed. Similarly fiber positions and orientations in cracked
cross-section were recognized and were compared with numerically
simulated. Structural SFRHSC fracture model was created based on
single fiber pull-out laws, which were determined experimentally.
Model predictions were validated by 15x15x60cm prisms 4 point
bending tests.
Abstract: Fracture process in mechanically loaded steel fiber
reinforced high-strength (SFRHSC) concrete is characterized by
fibers bridging the crack providing resistance to its opening.
Structural SFRHSC fracture model was created; material fracture
process was modeled, based on single fiber pull-out laws, which were
determined experimentally (for straight fibers, fibers with end hooks
(Dramix), and corrugated fibers (Tabix)) as well as obtained
numerically ( using FEM simulations). For this purpose experimental
program was realized and pull-out force versus pull-out fiber length
was obtained (for fibers embedded into concrete at different depth
and under different angle). Model predictions were validated by
15x15x60cm prisms 4 point bending tests. Fracture surfaces analysis
was realized for broken prisms with the goal to improve elaborated
model assumptions. Optimal SFRHSC structures were recognized.