Abstract: The microstructure, mechanical properties and metalgraphic characteristics of Ni plated AlN-Astaloy Cr-M powders were investigated using specimens produced by tube furnace sintering at 1000-1400 °C temperature. A uniform nickel layer on AlN powders was deposited prior to sintering using electroless plating technique. A composite consisting of ternary additions, metallic phase, Ni and ceramic phase AlN within a matrix of Astaloy Cr-M had been prepared under Ar shroud and then tube furnace sintered. The experimental results carried out by using XRD (X-Ray Diffraction) and SEM (Scanning Electron Microscope) for composition (10% AlN-Astaloy Cr-M) 10% Ni at 1400 °C suggest that the best properties as 132.45HB and permittivity were obtained at 1400 °C.
Abstract: The main objective of this study was to remove and recover Ni, Cu and Fe from a mixed metal system using sodium hypophosphite as a reducing agent and nickel powder as seeding material. The metal systems studied consisted of Ni-Cu, Ni-Fe and Ni-Cu-Fe solutions. A 5 L batch reactor was used to conduct experiments where 100 mg/l of each respective metal was used. It was found that the metals were reduced to their elemental form with removal efficiencies of over 80%. The removal efficiency decreased in the order Fe>Ni>Cu. The metal powder obtained contained between 97-99% Ni and was almost spherical and porous. Size enlargement by aggregation was the dominant particulate process.