Abstract: An ion implantation technique was used for designing the surface area of a titanium alloy and for irradiation-enhanced hardening of the surface. The Ti6Al4V alloy was treated by nitrogen ion implantation at fluences of 2·1017 and 4·1017 cm-2 and at ion energy 90 keV. The depth distribution of the nitrogen was investigated by Rutherford Backscattering Spectroscopy. The gradient of mechanical properties was investigated by nanoindentation. The continuous measurement mode was used to obtain depth profiles of the indentation hardness and the reduced storage modulus of the modified surface area. The reduced storage modulus and the hardness increase with increasing fluence. Increased fluence shifts the peak of the mechanical properties as well as the peak of nitrogen concentration towards to the surface. This effect suggests a direct relationship between mechanical properties and nitrogen distribution.
Abstract: Vancron 40, a nitrided powder metallurgical tool
Steel, is used in cold work applications where the predominant failure
mechanisms are adhesive wear or galling. Typical applications of
Vancron 40 are among others fine blanking, cold extrusion, deep
drawing and cold work rolls for cluster mills. Vancron 40 positive
results for cold work rolls for cluster mills and as a tool for some
severe metal forming process makes it competitive compared to other
type of work rolls that require higher precision, among others in cold
rolling of thin stainless steel, which required high surface finish
quality. In this project, three roll materials for cold rolling of stainless
steel strip was examined, Vancron 40, Narva 12B (a high-carbon,
high-chromium tool steel alloyed with tungsten) and Supra 3 (a
Chromium-molybdenum tungsten-vanadium alloyed high speed
steel). The purpose of this project was to study the depth profiles of
the ironed stainless steel strips, emergence of galling and to study the
lubrication performance used by steel industries. Laboratory
experiments were conducted to examine scratch of the strip, galling
and surface roughness of the roll materials under severe tribological
conditions. The critical sliding length for onset of galling was
estimated for stainless steel with four different lubricants. Laboratory
experiments result of performance evaluation of resistance capability
of rolls toward adhesive wear under severe conditions for low and
high reductions. Vancron 40 in combination with cold rolling
lubricant gave good surface quality, prevents galling of
metal surfaces and good bearing capacity.
Abstract: Cd1−xZnxS thins films have been fabricated from ZnS/CdS/ZnS multilayer thin film systems, by using the vacuum deposition method; the Rutherford backscattering (RBS) technique have been applied in order to determine the: structure, composition, depth profile, and stoichiometric of these films. The influence of the chemical and heat treatments on the produced films also have been investigated; the RBS spectra of the films showed that homogenous Cd1−xZnxS can be synthesized with x=0.45.