Abstract: Pseudomonas putida is a potential strain in biological treatment to remove mercury contained in the effluent of petrochemical industry due to its mercury reductase enzyme that able to reduce ionic mercury to elementary mercury. Freeze-dried P. putida allows easy, inexpensive shipping, handling and high stability of the product. This study was aimed to freeze dry P. putida cells with addition of lyoprotectant. Lyoprotectant was added into the cells suspension prior to freezing. Dried P. putida obtained was then mixed with synthetic mercury. Viability of recovery P. putida after freeze dry was significantly influenced by the type of lyoprotectant. Among the lyoprotectants, tween 80/ sucrose was found to be the best lyoprotectant. Sucrose able to recover more than 78% (6.2E+09 CFU/ml) of the original cells (7.90E+09CFU/ml) after freeze dry and able to retain 5.40E+05 viable cells after 4 weeks storage in 4oC without vacuum. Polyethylene glycol (PEG) pre-treated freeze dry cells and broth pre-treated freeze dry cells after freeze-dry recovered more than 64% (5.0 E+09CFU/ml) and >0.1% (5.60E+07CFU/ml). Freeze-dried P. putida cells in PEG and broth cannot survive after 4 weeks storage. Freeze dry also does not really change the pattern of growth P. putida but extension of lag time was found 1 hour after 3 weeks of storage. Additional time was required for freeze-dried P. putida cells to recover before introduce freeze-dried cells to more complicated condition such as mercury solution. The maximum mercury reduction of PEG pre-treated freeze-dried cells after freeze dry and after storage 3 weeks was 56.78% and 17.91%. The maximum of mercury reduction of tween 80/sucrose pre-treated freeze-dried cells after freeze dry and after storage 3 weeks were 26.35% and 25.03%. Freeze dried P. putida was found to have lower mercury reduction compare to the fresh P. putida that has been growth in agar. Result from this study may be beneficial and useful as initial reference before commercialize freeze-dried P. putida.
Abstract: Magnesium is used implant material potentially for
non-toxicity to the human body. Due to the excellent
bio-compatibility, Mg alloys is applied to implants avoiding removal
second surgery. However, it is found commercial magnesium alloys
including aluminum has low corrosion resistance, resulting
subcutaneous gas bubbles and consequently the approach as
permanent bio-materials. Generally, Aluminum is known to pollution
substance, and it raises toxicity to nervous system. Therefore
especially Mg-35Zn-3Ca alloy is prepared for new biodegradable
materials in this study. And the pulsed power is used in
constant-current mode of DC power kinds of anodization. Based on
the aforementioned study, it examines corrosion resistance and
biocompatibility by effect of current and frequency variation. The
surface properties and thickness were compared using scanning
electronic microscopy. Corrosion resistance was assessed via
potentiodynamic polarization and the effect of oxide layer on the body
was assessed cell viability. Anodized Mg-35Zn-3Ca alloy has good
biocompatibility in vitro by current and frequency variation.