Abstract: Wastes from a vegetal extracts industry (cocoa, oak, Guarana and mate) were characterized by particle size, proximate and ultimate analysis, lignocellulosic fractions, high heating value, thermal analysis (Thermogravimetric analysis – TGA, and Differential thermal analysis - DTA) and energy density to evaluate their potential as biomass in the form of briquettes for power generation. All wastes presented adequate particle sizes to briquettes production. The wastes showed high moisture content, requiring previous drying for use as briquettes. Cocoa and oak wastes had the highest volatile matter contents with maximum mass loss at 310 ºC and 450 ºC, respectively. The solvents used in the aroma extraction process influenced in the moisture content of the wastes, which was higher for mate due to water has been used as solvent. All wastes showed an insignificant loss mass after 565 °C, hence resulting in low ash content. High carbon and hydrogen contents and low sulfur and nitrogen contents were observed ensuring a low generation of sulfur and nitrous oxides. Mate and cocoa exhibited the highest carbon and lignin content, and high heating value. The dried wastes had high heating value, from 17.1 MJ/kg to 20.8 MJ/kg. The results indicate the energy potential of wastes for use as fuel in power generation.
Abstract: Unwanted sound reflection can create acoustic discomfort and lead to problems of speech comprehensibility. Contemporary building techniques enable highly finished internal walls resulting in sound reflective surfaces. In contrast, sustainable construction materials using natural and vegetal materials, are often more porous and absorptive. Hemp shiv is used as an aggregate and when mixed with lime binder creates a low-embodied-energy concrete. Cement replacements such as ground granulated blast slag (GGBS), a byproduct of other industrial processes, are viewed as more sustainable alternatives to high-embodied-energy cement. Hemp concretes exhibit good hygrothermal performance. This has focused much research attention on them as natural and sustainable low-energy alternatives to standard concretes. A less explored benefit is the acoustic absorption capability of hemp-based concretes. This work investigates hemp-lime-GGBS concrete specifically, and shows that it exhibits high levels of sound absorption.
Abstract: This work presents an improved single fiber pull-out
test for fiber/matrix interface characterization. This test has been
used to study the Inter-Facial Shear Strength ‘IFSS’ of hemp fibers
reinforced polypropylene (PP). For this aim, the fiber diameter
has been carefully measured using a tomography inspired method.
The fiber section contour can then be approximated by a circle
or a polygon. The results show that the IFSS is overestimated if
the circular approximation is used. The Influence of the molding
temperature on the IFSS has also been studied. We find that a molding
temperature of 183◦C leads to better interfacial properties. Above or
below this temperature the interface strength is reduced.
Abstract: Conventional materials like glass, wood or metals
replacement with polymer materials is still continuing. More simple
thus cheaper production is the main reason. However due to high
energy and petrochemical prices are polymer prices increasing too.
That´s why various kinds of fillers are used to make polymers
cheaper. Of course target is to maintain or improve properties of
these compounds. In this paper are solved rheology issues of
polymers compounded with vegetal origin fibers.
Abstract: Polyurethane foam (PUF) is formed by a chemical
reaction of polyol and isocyanate. The aim is to understand the
impact of Silicone on synthesizing polyurethane in differentiate
volume of molding. The method used was one step process, which is
simultaneously caried out a blending polyol (petroleum polyol and
soybean polyol), a TDI (2,4):MDI (4,4-) (80:20), a distilled water,
and a silicone. The properties of the material were measured via a
number of parameters, which are polymer density, compressive
strength, and cellular structures. It is found that density of
polyurethane using silicone with volume of molding either 250 ml or
500 ml is lower than without using silicone.