Abstract: Unwanted sound reflection can create acoustic discomfort and lead to problems of speech comprehensibility. Contemporary building techniques enable highly finished internal walls resulting in sound reflective surfaces. In contrast, sustainable construction materials using natural and vegetal materials, are often more porous and absorptive. Hemp shiv is used as an aggregate and when mixed with lime binder creates a low-embodied-energy concrete. Cement replacements such as ground granulated blast slag (GGBS), a byproduct of other industrial processes, are viewed as more sustainable alternatives to high-embodied-energy cement. Hemp concretes exhibit good hygrothermal performance. This has focused much research attention on them as natural and sustainable low-energy alternatives to standard concretes. A less explored benefit is the acoustic absorption capability of hemp-based concretes. This work investigates hemp-lime-GGBS concrete specifically, and shows that it exhibits high levels of sound absorption.
Abstract: A large amount of blast furnace slag is generated in
China. Most ground granulated blast furnace slag (GGBS) however
ends up in low-grade applications. Blast furnace slag, ground to an
appropriate fineness, can be used as a partial replacement of
cementitious material in concrete. The potential for using GGBS in
structural concrete, e.g. concrete beams and columns is investigated
at Xi’an Jiaotong-Liverpool University (XJTLU). With 50% of CEM
I cement replaced with GGBS, peak hydration temperatures
determined in a suspended concrete slab reduced by 20%. This
beneficiary effect has not been further improved with 70% of CEM I
replaced with GGBS. Partial replacement of CEM I with GGBS has a
retardation effect on the early-age strength of concrete. More GGBS
concrete mixes will be conducted to identify an ‘optimum’
replacement level which will lead to a reduced thermal loading,
without significantly compromising the early-age strength of
concrete.
Abstract: This paper presents a study on use of alkali activated bottom ash (BA) and ground granulated blast furnace slag (GGBS) blend in paver blocks. A preliminary effort on alkali-activated bottom ash, blast furnace slag based geopolymer (BA-GGBS-GP) mortar with river sand was carried out to identify the suitable mix for paver block. Several mixes were proposed based on the combination of BA-GGBS. The percentage ratio of BA: GGBS was selected as 100:0, 75:25, 50:50, 25:75 and 0:100 for the source material. Sodium based alkaline activators were used for activation. The molarity of NaOH was considered as 8M. The molar ratio of SiO2 to Na2O was varied from 1 to 4. Two curing mode such as ambient and steam curing 60°C for 24 hours were selected. The properties of paver block such as compressive strength split tensile strength, flexural strength and water absorption were evaluated as per IS15658:2006. Based on the preliminary study on BA-GGBS-GP mortar, the combinations of 25% BA with 75% GGBS mix for M30 and 75% BA with 25% GGBS mix for M35 grade were identified for paver block. Test results shows that the combination of BA-GGBS geopolymer paver blocks attained remarkable compressive strength under steam curing as well as in ambient mode at 3 days. It is noteworthy to know BA-GGBS-GP has promising future in the construction industry.