Abstract: This paper represents the results of long term strength of mortar incorporating Rice Husk Ash (RHA). For these work mortar samples were made according to ASTM standard C 109/C. OPC cement was partially replaced by RHA at 0, 10, 15, 20, 25 and 30 percent replacement level. After casting all samples were kept in controlled environment and curing was done up to 90 days. Test of mortar was performed on 3, 7, 28, 90, 365 and 700 days. It is noticed that OPC mortar shows better strength at early age than mortar having RHA but at 90 days and onward the picture is different. At 700 days it is observed that mortar containing 20% RHA shows better result than any other samples.
Abstract: Rice husk is a lignocellulosic source that can be
converted to ethanol. Three hundreds grams of rice husk was mixed
with 1 L of 0.18 N sulfuric acid solutions then was heated in an
autoclave. The reaction was expected to be at constant temperature
(isothermal), but before that temperature was achieved, reaction has
occurred. The first liquid sample was taken at temperature of 140 0C
and repeated every 5 minute interval. So the data obtained are in the
regions of non-isothermal and isothermal. It was observed that the
degradation has significant effects on the ethanol production. The
kinetic constants can be expressed by Arrhenius equation with the
frequency factors for hydrolysis and sugar degradation of 1.58 x 105
1/min and 2.29 x 108 L/mole/min, respectively, while the activation
energies are 64,350 J/mole and 76,571 J/mole. The highest ethanol
concentration from fermentation is 1.13% v/v, attained at 220 0C.
Abstract: The compressive strength development through
polymerization process of alkaline solution and fly ash blended with Microwave Incinerated Rice Husk Ash (MIRHA) is described in this
paper. Three curing conditions, which are hot gunny curing, ambient
curing, and external humidity curing are investigated to obtain the suitable curing condition for cast in situ provision. Fly ash was
blended with MIRHA at 3%, 5%, and 7% to identify the effect of blended mixes to the compressive strength and microstructure
properties of geopolymer concrete. Compressive strength results
indicated an improvement in the strength development with external humidity curing concrete samples compared to hot gunny curing and
ambient curing. Blended mixes also presented better performance
than control mixes. Improvement of interfacial transition zone (ITZ)
and micro structure in external humidity concrete samples were also
identified compared to hot gunny and ambient curing.
Abstract: In the modern construction practices, industrial wastes
or by-products are largely used as raw materials in cement and
concrete. These impart many benefits to the environment and bringabout
an economic impact because the cost of waste disposal is
constantly increasing due to strict environmental regulations. It was
reported in literature that the leakage of oil onto concrete element in
older cement grinding unit resulted in concrete with greater resistance
to freezing and thawing. This effect was thought to be similar to
adding an air-entraining chemical admixture to concrete. This paper
presents an investigation on the load deflection behaviour and crack
patterns of reinforced concrete (RC) beams subjected to four point
loading. Ten 120x260x1900 mm beams were cast with 100%
ordinary Portland cement (OPC) concrete, 20% fly ash (FA) and 20%
rice husk ash (RHA) blended cement concrete. 0.15% dosage of
admixtures (used engine oil, new engine oil, and superplasticizer)
was used throughout the experiment. Results show that OPC and
OPC/RHA RC beams containing used engine oil and superplasticizer
exhibit higher capacity, 18-26% than their corresponding control
mix.
Abstract: The potential of economically cheaper cellulose
containing natural materials like rice husk was assessed for nickel
adsorption from aqueous solutions. The effects of pH, contact time,
sorbent dose, initial metal ion concentration and temperature on the
uptake of nickel were studied in batch process. The removal of nickel
was dependent on the physico-chemical characteristics of the
adsorbent, adsorbate concentration and other studied process
parameters. The sorption data has been correlated with Langmuir,
Freundlich and Dubinin-Radush kevich (D-R) adsorption models. It
was found that Freundlich and Langmuir isotherms fitted well to the
data. Maximum nickel removal was observed at pH 6.0. The
efficiency of rice husk for nickel removal was 51.8% for dilute
solutions at 20 g L-1 adsorbent dose. FTIR, SEM and EDAX were
recorded before and after adsorption to explore the number and
position of the functional groups available for nickel binding on to
the studied adsorbent and changes in surface morphology and
elemental constitution of the adsorbent. Pseudo-second order model
explains the nickel kinetics more effectively. Reusability of the
adsorbent was examined by desorption in which HCl eluted 78.93%
nickel. The results revealed that nickel is considerably adsorbed on
rice husk and it could be and economic method for the removal of
nickel from aqueous solutions.
Abstract: The abundance and availability of rice husk, an agricultural waste, make them as a good source for precursor of activated carbon. In this work, rice husk-based activated carbons were prepared via base treated chemical activation process prior the carbonization process. The effect of carbonization temperatures (400, 600 and 800oC) on their pore structure was evaluated through morphology analysis using scanning electron microscope (SEM). Sample carbonized at 800oC showed better evolution and development of pores as compared to those carbonized at 400 and 600oC. The potential of rice husk-based activated carbon as an alternative adsorbent was investigated for the removal of Ni(II), Zn(II) and Pb(II) from single metal aqueous solution. The adsorption studies using rice husk-based activated carbon as an adsorbent were carried out as a function of contact time at room temperature and the metal ions were analyzed using atomic absorption spectrophotometer (AAS). The ability to remove metal ion from single metal aqueous solution was found to be improved with the increasing of carbonization temperature. Among the three metal ions tested, Pb(II) ion gave the highest adsorption on rice husk-based activated carbon. The results obtained indicate the potential to utilize rice husk as a promising precursor for the preparation of activated carbon for removal of heavy metals.
Abstract: Rice husk is a lignocellulosic source that can be
converted to ethanol. Three hundreds grams of rice husk was mixed
with 1 L of 0.18 N sulfuric acid solutions then was heated in an
autoclave. The reaction was expected to be at constant temperature
(isothermal), but before that temperature was achieved, reaction has
occurred. The first liquid sample was taken at temperature of 140 0C
and repeated every 5 minute interval. So the data obtained are in the
regions of non-isothermal and isothermal. It was observed that the
degradation has significant effects on the ethanol production. The
kinetic constants can be expressed by Arrhenius equation with the
frequency factors for hydrolysis and sugar degradation of 1.58 x 105
min-1 and 2.29 x 108 L/mole-min, respectively, while the activation
energies are 64,350 J/mole and 76,571 J/mole. The highest ethanol
concentration from fermentation is 1.13% v/v, attained at 220 0C.
Abstract: Self-compacting concrete (SCC), a new kind of high
performance concrete (HPC) have been first developed in Japan in
1986. The development of SCC has made casting of dense
reinforcement and mass concrete convenient, has minimized noise.
Fresh self-compacting concrete (SCC) flows into formwork and
around obstructions under its own weight to fill it completely and
self-compact (without any need for vibration), without any
segregation and blocking. The elimination of the need for
compaction leads to better quality concrete and substantial
improvement of working conditions. SCC mixes generally have a
much higher content of fine fillers, including cement, and produce
excessively high compressive strength concrete, which restricts its
field of application to special concrete only. To use SCC mixes in
general concrete construction practice, requires low cost materials to
make inexpensive concrete.
Rice husk ash (RHA) has been used as a highly reactive
pozzolanic material to improve the microstructure of the interfacial
transition zone (ITZ) between the cement paste and the aggregate in
self compacting concrete. Mechanical experiments of RHA blended
Portland cement concretes revealed that in addition to the pozzolanic
reactivity of RHA (chemical aspect), the particle grading (physical
aspect) of cement and RHA mixtures also exerted significant
influences on the blending efficiency.
The scope of this research was to determine the usefulness of Rice
husk ash (RHA) in the development of economical self compacting
concrete (SCC). The cost of materials will be decreased by reducing
the cement content by using waste material like rice husk ash instead
of.
This paper presents a study on the development of Mechanical
properties up to 180 days of self compacting and ordinary concretes
with rice-husk ash (RHA), from a rice paddy milling industry in
Rasht (Iran). Two different replacement percentages of cement by
RHA, 10%, and 20%, and two different water/cementicious material
ratios (0.40 and 0.35), were used for both of self compacting and
normal concrete specimens. The results are compared with those of
the self compacting concrete without RHA, with compressive,
flexural strength and modulus of elasticity. It is concluded that RHA
provides a positive effect on the Mechanical properties at age after
60 days.
Base of the result self compacting concrete specimens have higher
value than normal concrete specimens in all test except modulus of
elasticity. Also specimens with 20% replacement of cement by RHA
have the best performance.
Abstract: Low silica type X (LSX) Zeolite is one of useful
material in many manufacturing due to the advantage properties
including high surface area, stability, microporous crystalline
aluminosilicates and positive ion in an extra–framework. The LSX
was used rice husk silica source which obtained by leaching with
hydrochloric acid and calcination at 500C. To improve the
synthesis method, the LSX was crystallizated in Teflon–lined
autoclave will expedite deceasing of the amorphous particles. The
mixed gel with composition of 5.5 Na2O : 1.65 K2O : Al2O3 : 2.2
SiO2 : 122 H2O was crystallized in different container
(Polypropylene bottom and Teflon–lined autoclave). The obtained
powder was characterized by X–ray diffraction (XRD), X–ray
fluorescence spectrometry, N2 adsorption-desorption analysis BET
surface area Scanning electron microscopy (SEM) and Fourier
transform infrared spectroscopy to justify the quality of zeolite. The
results showed the crystallized zeolite in Teflon lined autoclave has
102.8 nm of crystal size, 286 m2/g of surface area and fewer amounts
of round amorphous particles when compared with the crystallized
zeolite in Polypropylene.
Abstract: The characterisation of agro-wastes fibres for composite applications from Nigeria using X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM) has been done. Fibres extracted from groundnut shell, coconut husk, rice husk, palm fruit bunch and palm fruit stalk are processed using two novel cellulose fibre production methods developed by the authors. Cellulose apparent crystallinity calculated using the deconvolution of the diffractometer trace shows that the amorphous portion of cellulose was permeable to hydrolysis yielding high crystallinity after treatment. All diffratograms show typical cellulose structure with well-defined 110, 200 and 040 peaks. Palm fruit fibres had the highest 200 crystalline cellulose peaks compared to others and it is an indication of rich cellulose content. Surface examination of the resulting fibres using SEM indicates the presence of regular cellulose network structure with some agglomerated laminated layer of thin leaves of cellulose microfibrils. The surfaces were relatively smooth indicating the removal of hemicellulose, lignin and pectin.
Abstract: The purpose of this paper is to investigate the
durability of cement mortar in presence of Rice Husk Ash (RHA).
The strength and durability of mortar with different replacement
level (0%, 10%, 15%, 20%, 25% and 30%) of Ordinary Portland
Cement (OPC) by RHA is investigated here. RHA was
manufactured from an uncontrolled burning process. Test samples
were prepared with river sand of FM 2.73. Samples were kept in
controlled environment up to test time. The results show that
addition of RHA was shown better results for 20% replacement
level than OPC at 90 days. In durability test all samples passed for
20 cycles except 25% and 30% replacement level.
Abstract: Many non-conventional adsorbent have been studied
as economic alternative to commercial activated carbon and mostly
agricultural waste have been introduced such as rubber leaf powder
and hazelnut shell. Microwave Incinerated Rice Husk Ash
(MIRHA), produced from the rice husk is one of the low-cost
materials that were used as adsorbent of heavy metal. The aim of
this research was to study the feasibility of using MIRHA500 and
MIRHA800 as adsorbent for the removal of Cu(II) metal ions from
aqueous solutions by the batch studies. The adsorption of Cu(II) into
MIRHA500 and MIRH800 favors Fruendlich isotherm and imply
pseudo – kinetic second order which applied chemisorptions
Abstract: The performance of mortar subjected to high
temperature and cooled in normal ambient temperature was examined
in the laboratory to comply with the situation of burning & cooling of
a structure. Four series of cubical (5 X 5 X 5 cm) mortar specimens
were made from OPC, and partial replacement (10, 15, 20, 25 &
30%) of OPC by Rice Husk Ash (RHA) produced in the uncontrolled
environment. These specimens were heated in electric furnace to 200,
300, 400, 500 and 7000C. The specimens were kept in normal room
temperature for cooling. They were then tested for mechanical
properties and the results shows that particular 20% RHA mixed
mortar shows better fire performance.
Abstract: Fixed-bed slow pyrolysis experiments of rice husk
have been conducted to determine the effect of pyrolysis
temperature, heating rate, particle size and reactor length on the
pyrolysis product yields. Pyrolysis experiments were performed at
pyrolysis temperature between 400 and 600°C with a constant
heating rate of 60°C/min and particle sizes of 0.60-1.18 mm. The
optimum process conditions for maximum liquid yield from the rice
husk pyrolysis in a fixed bed reactor were also identified. The highest
liquid yield was obtained at a pyrolysis temperature of 500°C,
particle size of
1.18-1.80 mm, with a heating rate of 60°C/min in a 300 mm length
reactor. The obtained yield of, liquid, gas and solid were found be in
the range of 22.57-31.78 %, 27.75-42.26 % and 34.17-42.52 % (all
weight basics) respectively at different pyrolysis conditions. The
results indicate that the effects of pyrolysis temperature and particle
size on the pyrolysis yield are more significant than that of heating
rate and reactor length. The functional groups and chemical
compositions present in the liquid obtained at optimum conditions
were identified by Fourier Transform-Infrared (FT-IR) spectroscopy
and Gas Chromatography/ Mass Spectroscopy (GC/MS) analysis
respectively.
Abstract: Rice husk is one of the alternative fuels for Thailand because of its high potential and environmental benefits. Nonetheless, the environmental profile of the electricity production from rice husk must be assessed to ensure reduced environmental damage. A 10 MW pilot plant using rice husk as feedstock is the study site. The environmental impacts from rice husk power plant are evaluated by using the Life Cycle Assessment (LCA) methodology. Energy, material and carbon balances have been determined for tracing the system flow. Carbon closure has been used for describing of the net amount of CO2 released from the system in relation to the amount being recycled between the power plant and the CO2 adsorbed by rice husk. The transportation of rice husk to the power plant has significant on global warming, but not on acidification and photo-oxidant formation. The results showed that the impact potentials from rice husk power plant are lesser than the conventional plants for most of the categories considered; except the photo-oxidant formation potential from CO. The high CO from rice husk power plant may be due to low boiler efficiency and high moisture content in rice husk. The performance of the study site can be enhanced by improving the combustion efficiency.