Abstract: In the present study, fracture behavior of woven
fabric-reinforced glass/epoxy composite laminates under mode III
crack growth was experimentally investigated and numerically
modeled. Two methods were used for the calculation of the strain
energy release rate: the experimental compliance calibration (CC)
method and the Virtual Crack Closure Technique (VCCT). To
achieve this aim ECT (Edge Crack Torsion) was used to evaluate
fracture toughness in mode III loading (out of plane-shear) at
different crack lengths. Load–displacement and associated energy
release rates were obtained for various case of interest. To
calculate fracture toughness JIII, two criteria were considered
including non-linearity and maximum points in load-displacement
curve and it is observed that JIII increases with the crack length
increase. Both the experimental compliance method and the virtual
crack closure technique proved applicable for the interpretation of the
fracture mechanics data of woven glass/epoxy laminates in mode III.
Abstract: In this study the elastic-plastic stress distribution in
weld-bonded joint, fabricated from austenitic stainless steel (AISI
304) sheet of 1.00 mm thickness and Epoxy adhesive Araldite 2011,
subjected to axial loading is investigated. This is needed to improve
design procedures and welding codes, and saving efforts in the
cumbersome experiments and analysis. Therefore, a complete 3-D
finite element modelling and analysis of spot welded, bonded and
weld-bonded joints under axial loading conditions is carried out. A
comprehensive systematic experimental program is conducted to
determine many properties and quantities, of the base metals and the
adhesive, needed for FE modelling, such like the elastic – plastic
properties, modulus of elasticity, fracture limit, the nugget and heat
affected zones (HAZ) properties, etc. Consequently, the finite
element models developed, for each case, are used to evaluate
stresses distributions across the entire joint, in both the elastic and
plastic regions. The stress distribution curves are obtained,
particularly in the elastic regions and found to be consistent and in
excellent agreement with the published data. Furthermore, the
stresses distributions are obtained in the weld-bonded joint and
display the best results with almost uniform smooth distribution
compared to spot and bonded cases. The stress concentration peaks at
the edges of the weld-bonded region, are almost eliminated resulting
in achieving the strongest joint of all processes.