Abstract: The advancement in various concrete ingredients like plasticizers, additives and fibers, etc. has enabled concrete technologists to develop many viable varieties of special concretes in recent decades. Such various varieties of concrete have significant enhancement in green as well as hardened properties of concrete. A prudent selection of appropriate type of concrete can resolve many design and application issues in construction projects. This paper focuses on usage of self-compacting concrete, high early strength concrete, structural lightweight concrete, fiber reinforced concrete, high performance concrete and ultra-high strength concrete in the structures. The modified properties of strength at various ages, flowability, porosity, equilibrium density, flexural strength, elasticity, permeability etc. need to be carefully studied and incorporated into the design of the structures. The paper demonstrates various mixture combinations and the concrete properties that can be leveraged. The selection of such products based on the end use of structures has been proposed in order to efficiently utilize the modified characteristics of these concrete varieties. The study involves mapping the characteristics with benefits and savings for the structure from design perspective. Self-compacting concrete in the structure is characterized by high shuttering loads, better finish, and feasibility of closer reinforcement spacing. The structural design procedures can be modified to specify higher formwork strength, height of vertical members, cover reduction and increased ductility. The transverse reinforcement can be spaced at closer intervals compared to regular structural concrete. It allows structural lightweight concrete structures to be designed for reduced dead load, increased insulation properties. Member dimensions and steel requirement can be reduced proportionate to about 25 to 35 percent reduction in the dead load due to self-weight of concrete. Steel fiber reinforced concrete can be used to design grade slabs without primary reinforcement because of 70 to 100 percent higher tensile strength. The design procedures incorporate reduction in thickness and joint spacing. High performance concrete employs increase in the life of the structures by improvement in paste characteristics and durability by incorporating supplementary cementitious materials. Often, these are also designed for slower heat generation in the initial phase of hydration. The structural designer can incorporate the slow development of strength in the design and specify 56 or 90 days strength requirement. For designing high rise building structures, creep and elasticity properties of such concrete also need to be considered. Lastly, certain structures require a performance under loading conditions much earlier than final maturity of concrete. High early strength concrete has been designed to cater to a variety of usages at various ages as early as 8 to 12 hours. Therefore, an understanding of concrete performance specifications for special concrete is a definite door towards a superior structural design approach.
Abstract: Polymer concrete (PC) is a distinct concrete with superior characteristics in comparison to ordinary cement concrete. It has become well-known for its applications in thin overlays, floors and precast components. In this investigation, the mechanical properties of PC with different epoxy resin contents, ordinary cement concrete (OCC) and lightweight concrete (LC) have been studied under uniaxial compression test. The study involves five types of concrete, with each type being tested four times. Their complete elastic-plastic behavior was compared with each other through the measurement of volumetric strain during the tests. According to the results, PC showed higher strength, ductility and energy absorption with respect to OCC and LC.
Abstract: In this study, the effects of waste marbles as aggregate material on workability and hardened concrete characteristics of self compacting lightweight concrete are investigated. For this purpose, self compacting light weight concrete are produced by waste marble aggregates are replaced with fine aggregate at 5%, 7.5%, and 10% ratios. Fresh concrete properties, slump flow, T50 time, V funnel, compressive strength and ultrasonic pulse velocity of self compacting lightweight concrete are determined. It is concluded from the test results that using waste marbles as aggregate material by replacement with fine aggregate slightly affects fresh and hardened concrete characteristics of self compacting lightweight concretes.
Abstract: Lightweight concrete is being used in the construction industry as a building material in its own right. Ultra-lightweight concrete can be applied as a filler and support material for the manufacturing of composite building materials. This paper is about the development of a stable and reproducible ultra-lightweight concrete with the inclusion of poly-lactic acid (PLA) beads and assessing the feasibility of PLA as a lightweight aggregate that will deliver advantages such as a more eco-friendly concrete and a non-petroleum polymer aggregate. In total, sixty-three samples were prepared and the effectiveness of mineral admixture, curing conditions, water-cement ratio, PLA ratio, EPS ratio and perlite ratio on compressive strength of perlite concrete are studied. The results show that PLA particles are sensitive to alkali environment of cement paste and considerably shrank and lost their strength. A higher compressive strength and a lower density was observed when expanded polystyrene (EPS) particles replaced PLA beads. In addition, a set of equations is proposed to estimate the water-cement ratio, cement content and compressive strength of perlite concrete.
Abstract: This study investigates the suitability of using plastic,
such as polyethylene terephthalate (PET), as a partial replacement of
natural coarse and fine aggregates (for example, brick chips and
natural sand) to produce lightweight concrete for load bearing
structural members. The plastic coarse aggregate (PCA) and plastic
fine aggregate (PFA) were produced from melted polyethylene
terephthalate (PET) bottles. Tests were conducted using three
different water–cement (w/c) ratios, such as 0.42, 0.48, and 0.57,
where PCA and PFA were used as 50% replacement of coarse and
fine aggregate respectively. Fresh and hardened properties of
concrete have been compared for natural aggregate concrete (NAC),
PCA concrete (PCC) and PFA concrete (PFC). The compressive
strength of concrete at 28 days varied with the water–cement ratio for
both the PCC and PFC. Between PCC and PFC, PFA concrete
showed the highest compressive strength (23.7 MPa) at 0.42 w/c ratio
and also the lowest compressive strength (13.7 MPa) at 0.57 w/c
ratio. Significant reduction in concrete density was mostly observed
for PCC samples, ranging between 1977–1924 kg/m³. With the
increase in water–cement ratio PCC achieved higher workability
compare to both NAC and PFC. It was found that both the PCA and
PFA contained concrete achieved the required compressive strength
to be used for structural purpose as partial replacement of the natural
aggregate; but to obtain the desired lower density as lightweight
concrete the PCA is most suited.
Abstract: This paper is concerning the issues of behaviour of
lightweight expanded clay aggregates concrete exposed to high
temperature. Lightweight aggregates from expanded clay are
produced by firing of row material up to temperature 1050°C.
Lightweight aggregates have suitable properties in terms of volume
stability, when exposed to temperatures up to 1050°C, which could
indicate their suitability for construction applications with higher risk
of fire. The test samples were exposed to heat by using the standard
temperature-time curve ISO 834. Negative changes in resulting
mechanical properties, such as compressive strength, tensile strength,
and flexural strength were evaluated. Also visual evaluation of the
specimen was performed. On specimen exposed to excessive heat, an
explosive spalling could be observed, due to evaporation of
considerable amount of unbounded water from the inner structure of
the concrete.
Abstract: Well-designed composite steel and concrete structures
highlight the good material properties and lower the deficiencies of
steel and concrete, in particular they make use of high tensile strength
of steel and high stiffness of concrete. The most common composite
steel and concrete structure is a simply supported beam, which
concrete slab transferring the slab load to a beam is connected to the
steel cross-section. The aim of this paper is to find the most adequate
numerical model of a simply supported composite beam with the
cross-sectional and material parameters based on the results of a
processed parametric study and numerical analysis. The paper also
evaluates the suitability of using compact concrete with the
lightweight aggregates for composite steel and concrete beams. The
most adequate numerical model will be used in the resent future to
compare the results of laboratory tests.
Abstract: Structural lightweight concrete is used primarily to reduce the dead-load weight in concrete members such as floors in high-rise buildings and bridge decks. With given materials, it is generally desired to have the highest possible strength/unit weight ratio with the lowest cost of concrete. The work presented herein is part of an ongoing research project that investigates the properties of concrete mixes containing locally available Scoria lightweight aggregates and mineral admixtures. Properties considered included: workability, unit weight, compressive strength, and splitting tensile strength. Test results indicated that developing structural lightweight concretes (SLWC) using locally available Scoria lightweight aggregates and specific blends of silica fume and fly ash seems to be feasible. The stress-strain diagrams plotted for the structural LWC mixes developed in this investigation were comparable to a typical stress-strain diagram for normal weight concrete with relatively larger strain capacity at failure in case of LWC.
Abstract: The main objective of this paper is to determine the
isolated effect of silica fume on tensile, compressive and flexure strengths on high strength lightweight concrete. Many experiments
were carried out by replacing cement with different percentages of silica fume at different constant water-binder ratio keeping other mix
design variables constant. The silica fume was replaced by 0%, 5%,
10%, 15%, 20% and 25% for a water-binder ratios ranging from 0.26
to 0.42. For all mixes, split tensile, compressive and flexure strengths
were determined at 28 days. The results showed that the tensile, compressive and flexure strengths increased with silica fume incorporation but the optimum replacement percentage is not
constant because it depends on the water–cementitious material (w/cm) ratio of the mix. Based on the results, a relationship between
split tensile, compressive and flexure strengths of silica fume concrete was developed using statistical methods.