Abstract: Green concrete are generally composed of recycling
materials as hundred or partial percent substitutes for aggregate,
cement, and admixture in concrete. To reduce greenhouse gas
emissions, efforts are needed to develop environmentally friendly
construction materials. Using of fly ash based geopolymer as an
alternative binder can help reduce CO2 emission of concrete. The
binder of geopolymer concrete is different from the ordinary Portland
cement concrete. Geopolymer Concrete specimens were prepared
with different concentration of NaOH solution M10, M14, and, M16
and cured at 60ºC in duration of 24 hours and 8 hours, in addition to
the curing in direct sunlight. Thus, it is necessary to study the effects
of the geopolymer binder on the behavior of concrete. Concrete is
made by using geopolymer technology is environmental friendly and
could be considered as part of the sustainable development. In this
study, the Local Alkaline Activator in Egypt and crashed stone as
coarse aggregate in fly ash based-geopolymer concrete was
investigated. This paper illustrates the development of mechanical
properties. Since the gained compressive strength for geopolymer
concrete at 28 days was in the range of 22.5MPa – 43.9MPa.
Abstract: Local steel slag is produced as a by-product during the
oxidation of steel pellets in an electric arc furnace. Using local steel
slag waste as a hundred substitutes of crashed stone in construction
materials would resolve the environmental problems caused by the
large-scale depletion of the natural sources of crashed stone. This
paper reports the experimental study to investigate the influence of a
hundred replacement of crashed stone as a coarse aggregate with
local steel slag, on the fresh and hardened geopolymer concrete
properties. The investigation includes traditional testing of hardening
concrete, for selected mixes of cement and geopolymer concrete. It
was found that local steel slag as a coarse aggregate enhanced the
slump test of the fresh state of cement and geopolymer concretes.
Nevertheless, the unit weight of concretes was affected. Meanwhile,
the good performance was observed when fly ash used as geopolymer
concrete based.
Abstract: It is quite essential to investigate the causes of
pavement deterioration in order to select the proper maintenance
technique. The objective of this study was to identify factors cause
deterioration of recently constructed roads in Khartoum state. A
comprehensive literature concerning the factors of road deterioration,
common road defects and their causes were reviewed. Three major
road projects with different deterioration reasons were selected for
this study. The investigation involved field survey and laboratory
testing on those projects to examine the existing pavement
conditions. The results revealed that the roads investigated
experienced severe failures in the forms of cracks, potholes, and
rutting in the wheel path. The causes of those failures were found
mainly linked to poor drainage, traffic overloading, expansive
subgrade soils, and the use of low quality materials in construction.
Based on the results, recommendations were provided to help
highway engineers in selecting the most effective repair techniques
for specific kinds of distresses.
Abstract: The purposes of hydraulic gate are to maintain the
functions of storing and draining water. It bears long-term hydraulic
pressure and earthquake force and is very important for reservoir and
waterpower plant. The high tensile strength of steel plate is used as
constructional material of hydraulic gate. The cracks and rusts,
induced by the defects of material, bad construction and seismic
excitation and under water respectively, thus, the mechanics
phenomena of gate with crack are probing into the cause of stress
concentration, induced high crack increase rate, affect the safety and
usage of hydroelectric power plant. Stress distribution analysis is a
very important and essential surveying technique to analyze
bi-material and singular point problems. The finite difference
infinitely small element method has been demonstrated, suitable for
analyzing the buckling phenomena of welding seam and steel plate
with crack. Especially, this method can easily analyze the singularity
of kink crack. Nevertheless, the construction form and deformation
shape of some gates are three-dimensional system. Therefore, the
three-dimensional Digital Image Correlation (DIC) has been
developed and applied to analyze the strain variation of steel plate with
crack at weld joint. The proposed Digital image correlation (DIC)
technique is an only non-contact method for measuring the variation of
test object. According to rapid development of digital camera, the cost
of this digital image correlation technique has been reduced.
Otherwise, this DIC method provides with the advantages of widely
practical application of indoor test and field test without the restriction
on the size of test object. Thus, the research purpose of this research is
to develop and apply this technique to monitor mechanics crack
variations of weld steel hydraulic gate and its conformation under
action of loading. The imagines can be picked from real time
monitoring process to analyze the strain change of each loading stage.
The proposed 3-Dimensional digital image correlation method,
developed in the study, is applied to analyze the post-buckling
phenomenon and buckling tendency of welded steel plate with crack.
Then, the stress intensity of 3-dimensional analysis of different
materials and enhanced materials in steel plate has been analyzed in
this paper. The test results show that this proposed three-dimensional
DIC method can precisely detect the crack variation of welded steel
plate under different loading stages. Especially, this proposed DIC
method can detect and identify the crack position and the other flaws
of the welded steel plate that the traditional test methods hardly detect
these kind phenomena. Therefore, this proposed three-dimensional
DIC method can apply to observe the mechanics phenomena of
composite materials subjected to loading and operating.
Abstract: The laser-ultrasonic method is realized for
quantifying the influence of porosity on the local Young’s
modulus of isotropic composite materials. The method is based on
a laser thermooptical method of ultrasound generation combined
with measurement of the phase velocity of longitudinal and shear
acoustic waves in samples. The main advantage of this method
compared with traditional ultrasonic research methods is the
efficient generation of short and powerful probing acoustic pulses
required for reliable testing of ultrasound absorbing and
scattering heterogeneous materials. Using as an example samples
of a metal matrix composite with reinforcing microparticles of
silicon carbide in various concentrations, it is shown that to
provide an effective increase in Young’s modulus with increasing
concentration of microparticles, the porosity of the final sample
should not exceed 2%.
Abstract: Polycyclic Aromatic Hydrocarbons (PAHs) are
formed mainly because of incomplete combustion of organic
materials during industrial, domestic activities or natural occurrence.
Their toxicity and contamination of terrestrial and aquatic ecosystem
have been established. However, with limited validity index, previous
research has focused on PAHs isomer pair ratios of variable
physicochemical properties in source identification. The objective of
this investigation was to determine the empirical validity of Pearson
Correlation Coefficient (PCC) and Cluster Analysis (CA) in PAHs
source identification along soil samples of different land uses.
Therefore, 16 PAHs grouped, as Endocrine Disruption Substances
(EDSs) were determined in 10 sample stations in top and sub soils
seasonally. PAHs was determined the use of Varian 300 gas
chromatograph interfaced with flame ionization detector. Instruments
and reagents used are of standard and chromatographic grades
respectively. PCC and CA results showed that the classification of
PAHs along pyrolitic and petrogenic organics used in source
signature is about the predominance PAHs in environmental matrix.
Therefore, the distribution of PAHs in the studied stations revealed
the presence of trace quantities of the vast majority of the sixteen
PAHs, which may ultimately inhabit the actual source signature
authentication. Therefore, factors to be considered when evaluating
possible sources of PAHs could be; type and extent of bacterial
metabolism, transformation products/substrates, and environmental
factors such as salinity, pH, oxygen concentration, nutrients, light
intensity, temperature, co-substrates, and environmental medium are
hereby recommended as factors to be considered when evaluating
possible sources of PAHs.
Abstract: At the present work, highly transparent strip type
quasi-solid state dye-sensitized solar cells (DSSCs) were fabricated
through inkjet printing using nanocomposite TiO2 inks as raw
materials and tested under outdoor illumination conditions. The cells,
which can be considered as the structural units of large area modules,
were fully characterized electrically and electrochemically and after
the evaluation of the received results a large area DSSC module was
manufactured. The module design was a sandwich Z-interconnection
where the working electrode is deposited on one conductive glass and
the counter electrode on a second glass. Silver current collective
fingers were printed on the conductive glasses to make the internal
electrical connections and the adjacent cells were connected in series
and finally insulated using a UV curing resin to protect them from the
corrosive (I-/I3-) redox couple of the electrolyte. Finally, outdoor tests
were carried out to the fabricated dye-sensitized solar module and its
performance data were collected and assessed.
Abstract: Cryosorption pumps are considered safe, quiet, and
ultra-high vacuum production pumps which have their application
from Semiconductor industries to ITER [International Thermonuclear
Experimental Reactor] units. The principle of physisorption of gases
over highly porous materials like activated charcoal at cryogenic
temperatures (below -1500°C) is involved in determining the
pumping speed of gases like Helium, Hydrogen, Argon, and
Nitrogen. This paper aims at providing detailed overview of
development of Cryosorption pump and characterization of different
activated charcoal materials that optimizes the performance of the
pump. Different grades of charcoal were tested in order to determine
the pumping speed of the pump and were compared with
commercially available Varian cryopanel. The results for bare panel,
bare panel with adhesive, cryopanel with pellets, and cryopanel with
granules were obtained and compared. The comparison showed that
cryopanel adhered with small granules gave better pumping speeds
than large sized pellets.
Abstract: Revenue leakages are one of the major challenges
manufacturers face in production processes, as most of the input
materials that should emanate as products from the lines are lost as
waste. Rather than generating income from material input which is
meant to end-up as products, losses are further incurred as costs in
order to manage waste generated. In addition, due to the lack of a
clear view of the flow of resources on the lines from input to output
stage, acquiring information on the true cost of waste generated have
become a challenge. This has therefore given birth to the
conceptualization and implementation of waste minimization
strategies by several manufacturing industries. This paper reviews the
principles and applications of three environmental management
accounting tools namely Activity-based Costing (ABC), Life-Cycle
Assessment (LCA) and Material Flow Cost Accounting (MFCA) in
the manufacturing industry and their effectiveness in curbing revenue
leakages. The paper unveils the strengths and limitations of each of
the tools; beaming a searchlight on the tool that could allow for
optimal resource utilization, transparency in production process as
well as improved cost efficiency. Findings from this review reveal
that MFCA may offer superior advantages with regards to the
provision of more detailed information (both in physical and
monetary terms) on the flow of material inputs throughout the
production process compared to the other environmental accounting
tools. This paper therefore makes a case for the adoption of MFCA as
a viable technique for the identification and reduction of waste in
production processes, and also for effective decision making by
production managers, financial advisors and other relevant
stakeholders.
Abstract: Polylactic acid (PLA) is the most commercially
available bio-based and biodegradable plastic at present. PLA has
been used in plastic related industries including single-used
containers, disposable and environmentally friendly packaging owing
to its renewability, compostability, biodegradability, and safety.
Although PLA demonstrates reasonably good optical, physical,
mechanical and barrier properties comparable to the existing
petroleum-based plastics, its brittleness and mold shrinkage as well as
its price are the points to be concerned for the production of rigid and
semi-rigid packaging. Blending PLA with other bio-based polymers
including thermoplastic starch (TPS) is an alternative not only to
achieve a complete bio-based plastic, but also to reduce the
brittleness, shrinkage during molding and production cost of the
PLA-based products. TPS is a material produced mainly from starch
which is cheap, renewable, biodegradable, compostable, and nontoxic.
It is commonly prepared by a plasticization of starch under
applying heat and shear force. Although glycerol has been reported as
one of the most plasticizers used for preparing TPS, its migration
caused the surface stickiness of the TPS products. In some cases,
mixed plasticizers or natural fibers have been applied to impede the
retrogradation of starch or reduce the migration of glycerol. The
introduction of fibers into TPS-based materials could reinforce the
polymer matrix as well. Therefore, the objective of the present
research is to study the effect of starch type (i.e. native starch and
phosphate starch), plasticizer type (i.e. glycerol and xylitol with a
weight ratio of glycerol to xylitol of 100:0, 75:25, 50:50, 25:75 and
0:100) and fiber content (i.e. in the range of 1-25 %wt) on properties
of PLA/TPS blend and composite. PLA/TPS blends and composites
were prepared using a twin-screw extruder and then converted into
dumbbell-shaped specimens using an injection molding machine. The
PLA/TPS blends prepared by using phosphate starch showed higher
tensile strength and stiffness than the blends prepared by using native
one. In contrast, the blends from native starch exhibited higher
extensibility and heat distortion temperature (HDT) than those from
the modified starch. Increasing xylitol content resulted in enhanced
tensile strength, stiffness and water resistance, but decreased
extensibility and HDT of the PLA/TPS blend. Tensile properties and
hydrophobicity of the blend could be improved by incorporating
silane treated-jute fibers.
Abstract: The development of composite materials and the
related design and manufacturing technologies is one of the most
important advances in the history of materials. Composites are
multifunctional materials having unprecedented mechanical and
physical properties that can be tailored to meet the requirements of a
particular application. Some composites also exhibit great resistance
to high-temperature corrosion, oxidation, and wear. Polymers are
widely used indoors and outdoors, therefore they are exposed to a
chemical environment which may include atmospheric oxygen, acidic
fumes, acidic rain, moisture heat and thermal shock, ultra-violet light,
high energy radiation, etc. Different polymers are affected differently
by these factors even though the amorphous polymers are more
sensitive. Ageing is also important and it is defined as the process of
deterioration of engineering materials resulting from the combined
effects of atmospheric radiation, heat, oxygen, water, microorganisms
and other atmospheric factors.
Abstract: The study conducted a simulation of the effect of sea
water to the bonding capacity of GFRP sheet on the concrete beams
using a simulation tank. Fiber reinforced polymer (FRP) has been
developed and applied in many fields civil engineering structures on
the new structures and also for strengthening of the deteriorated
structures. The FRP has advantages such as its corrosion resistance as
well as high tensile strength to weight ratio. Compared to the other
FRP materials, Glass composed FRP (GFRP) is relatively cheaper.
GFRP sheet is applied externally by bonding it on the concrete surface.
The studies regarding the application of GFRP sheet have been
conducted such as strengthening system, bonding behavior of GFRP
sheet including the application as reinforcement in new structures. For
application to the structures with direct contact to sea environment, a
study regarding the effect of sea water to the bonding capacity of
GFRP sheet is important to be clarified. To achieve the objective of the
study, a series of concrete beams strengthened with GFRP sheet on
extreme tension surface were prepared. The beams then were stored on
the sea water tank for six months. Results indicated the bonding
capacity decreased after six month exposed to the sea water.
Abstract: Rapid prototyping is a new group of manufacturing
processes, which allows fabrication of physical of any complexity
using a layer by layer deposition technique directly from a computer
system. The rapid prototyping process greatly reduces the time and
cost necessary to bring a new product to market. The prototypes
made by these systems are used in a range of industrial application
including design evaluation, verification, testing, and as patterns for
casting processes. These processes employ a variety of materials and
mechanisms to build up the layers to build the part. The present work
was to build a FDM prototyping machine that could control the X-Y
motion and material deposition, to generate two-dimensional and
three-dimensional complex shapes. This study focused on the
deposition of wax material. This work was to find out the properties
of the wax materials used in this work in order to enable better
control of the FDM process. This study will look at the integration of
a computer controlled electro-mechanical system with the traditional
FDM additive prototyping process. The characteristics of the wax
were also analysed in order to optimise the model production process.
These included wax phase change temperature, wax viscosity and
wax droplet shape during processing.
Abstract: The activation volume of 6082T6 aluminum is
investigated at different temperatures for grain size variants. The
deformation activation volume was computed on the basis of the
relationship between the Boltzmann’s constant k, the testing
temperatures, the material strain rate sensitivity and the material yield
stress grain size variants. The material strain rate sensitivity is
computed as a function of yield stress and strain rate grain size
variants. The effect of the material strain rate sensitivity and the
deformation activation volume of 6082T6 aluminum at different
temperatures of 3-D grain are discussed. It is shown that the strain rate sensitivities and activation volume
are negative for the grain size variants during the deformation of
nanostructured materials. It is also observed that the activation
volume vary in different ways with the equivalent radius, semi minor
axis radius, semi major axis radius and major axis radius. From the
obtained results it is shown that the variation of activation volume
increase and decrease with the testing temperature. It was revealed
that, increase in strain rate sensitivity led to decrease in activation
volume whereas increase in activation volume led to decrease in
strain rate sensitivity.
Abstract: A problem of complex mineral resources development is urgent and priority, it is aimed at realization of the processes of their ecologically safe development, one of its components is revealing the influence of the forms of element compounds in raw materials and in the processing products. In view of depletion of the precious metal reserves at the traditional deposits in the XXI century the large-size open cast deposits, localized in black shale strata begin to play the leading role. Carbonaceous (black) shales carry a heightened metallogenic potential. Black shales with high content of carbon are widely distributed within the scope of Bureinsky massif. According to academician Hanchuk`s data black shales of Sutirskaya series contain generally PGEs native form. The presence of high absorptive towards carbonaceous matter gold and PGEs compounds in crude ore results in decrease of valuable components extraction because of their sorption into dissipated carbonaceous matter.
Abstract: Objectives: To determine the nutritional status and
risk factors associated with women practicing geophagia in QwaQwa,
South Africa. Materials and Methods: An observational epidemiological study
design was adopted which included an exposed (geophagia) and nonexposed
(control) group. A food frequency questionnaire, anthropometric measurements and blood sampling were applied to
determine nutritional status of participants. Logistic regression
analysis was performed in order to identify factors that were likely to
be associated with the practice of geophagia. Results: The mean total energy intake for the geophagia group (G)
and control group (C) were 10324.31 ± 2755.00 kJ and 10763.94 ±
2556.30 kJ respectively. Both groups fell within the overweight
category according to the mean Body Mass Index (BMI) of each
group (G= 25.59 kg/m2; C= 25.14 kg/m2). The mean serum iron
levels of the geophagia group (6.929 μmol/l) were significantly lower
than that of the control group (13.75 μmol/l) (p = 0.000). Serum
transferrin (G=3.23g/l; C=2.7054g/l) and serum transferrin saturation
(G=8.05%; C=18.74%) levels also differed significantly between
groups (p=0.00). Factors that were associated with the practice of
geophagia included haemoglobin (Odds ratio (OR):14.50), serumiron
(OR: 9.80), serum-ferritin (OR: 3.75), serum-transferrin (OR:
6.92) and transferrin saturation (OR: 14.50). A significant negative
association (p=0.014) was found between women who were wageearners
and those who were not wage-earners and the practice of
geophagia (OR: 0.143; CI: 0.027; 0.755). These findings seem to
indicate that a permanent income may decrease the likelihood of
practising geophagia. Key Findings: Geophagia was confirmed to be a risk factor for
iron deficiency in this community. The significantly strong
association between geophagia and iron deficiency emphasizes the
importance of identifying the practice of geophagia in women,
especially during their child bearing years.
Abstract: Processing of high-silicon bauxite on the base of the
traditional clinkering method is related to high power consumption
and capital investments, which makes production of alumina from
those ores non-competitive in terms of basic economic showings. For
these reasons, development of technological solutions enabling to
process bauxites with various chemical and mineralogical structures
efficiently with low level of thermal power consumption is important.
Flow sheet of the studies on washability of ores from the Timanskoe
and the Severo-Onezhskoe deposits is on the base of the flotation
method.
Abstract: Zinc borate is an important inorganic hydrate borate
material, which can be used as a flame retardant agent and corrosion
resistance material. This compound can loss its structural water
content at higher than 290°C. Due to thermal stability; Zinc Borate
can be used as flame retardant at high temperature process of plastic
and gum. In this study, the ultrasonic reaction of zinc borates were
studied using hydrozincite (Zn5(CO3)2·(OH)6) and boric acid
(H3BO3) raw materials. Before the synthesis raw materials were
characterized by X-Ray Diffraction (XRD) and Fourier Transform
Infrared Spectroscopy (FT-IR). Ultrasonic method is a new
application on the zinc borate synthesis. The synthesis parameters
were set to 90°C reaction temperature and 55 minutes of reaction
time, with 1:1, 1:2, 1:3, 1:4 and 1:5 molar ratio of starting materials
(Zn5(CO3)2·(OH)6 : H3BO3). After the zinc borate synthesis, the
products were analyzed by XRD and FT-IR. As a result, optimum
molar ratio of 1:5 is determined for the synthesis of zinc borates with
ultrasonic method.
Abstract: Ceramic obtained on the base of aluminum oxide has
wide application range, because it has unique properties, for example,
wear-resistance, dielectric characteristics, and exploitation ability at
high temperatures and in corrosive atmosphere. Low temperature
synthesis of α-Al2O3 is energo-economical process and it is topical
for developing technologies of corundum ceramics fabrication. In the present work possibilities of low temperature transformation
of oxyhydroxides in α-Al2O3, during the presence of small amount of
rare–earth elements compounds (also Th, Re), have been discussed.
Aluminum unstable oxyhydroxides have been obtained by hydrolysis
of aluminium isopropoxide, nitrates, sulphate, and chloride in
alkaline environment at 80-90ºC temperatures. β-Al(OH)3 has been
received from aluminum powder by ultrasonic development. Drying
of oxyhydroxide sol has been conducted with presence of various
types seeds, which amount reaches 0,1-0,2% (mas). Neodymium,
holmium, thorium, lanthanum, cerium, gadolinium, disprosium
nitrates and rhenium carbonyls have been used as seeds and they
have been added to the sol specimens in amount of 0.1-0.2% (mas)
calculated on metals. Annealing of obtained gels is carried out at 70–
1100ºC for 2 hrs. The same specimen transforms in α-Al2O3 at
1100ºC. At this temperature in case of presence of lanthanum and
gadolinium transformation takes place by 70-85%. In case of
presence of thorium stabilization of γ-and θ-phases takes place. It is
established, that thorium causes inhibition of α-phase generation at
1100ºC, and at the time when in all other doped specimens α-phase is
generated at lower temperatures (1000-1050ºC). Synthesis of various
type compounds and simultaneous consolidation has developed in the
furnace of OXY-GON. Composite materials containing oxide and
non-oxide components close to theoretical data have been obtained in
this furnace respectively. During the work the following devices have
been used: X-ray diffractometer DRON-3M (Cu-Kα, Ni filter,
2º/min), High temperature vacuum furnace OXY-GON, electronic
scanning microscopes Nikon ECLIPSE LV 150, NMM-800TRF,
planetary mill Pulverisette 7 premium line, SHIMADZU Dynamic
Ultra Micro Hardness Tester, DUH-211S, Analysette 12 Dyna sizer.
Abstract: Nonlinear evolution of broadband ultrasonic pulses
passed through the rock specimens is studied using the apparatus
“GEOSCAN-02M”. Ultrasonic pulses are excited by the pulses of Qswitched
Nd:YAG laser with the time duration of 10 ns and with the
energy of 260 mJ. This energy can be reduced to 20 mJ by some light
filters. The laser beam radius did not exceed 5 mm. As a result of the
absorption of the laser pulse in the special material – the optoacoustic
generator–the pulses of longitudinal ultrasonic waves are excited with
the time duration of 100 ns and with the maximum pressure
amplitude of 10 MPa. The immersion technique is used to measure
the parameters of these ultrasonic pulses passed through a specimen,
the immersion liquid is distilled water. The reference pulse passed
through the cell with water has the compression and the rarefaction
phases. The amplitude of the rarefaction phase is five times lower
than that of the compression phase. The spectral range of the
reference pulse reaches 10 MHz. The cubic-shaped specimens of the
Karelian gabbro are studied with the rib length 3 cm. The ultimate
strength of the specimens by the uniaxial compression is (300±10)
MPa. As the reference pulse passes through the area of the specimen
without cracks the compression phase decreases and the rarefaction
one increases due to diffraction and scattering of ultrasound, so the
ratio of these phases becomes 2.3:1. After preloading some horizontal
cracks appear in the specimens. Their location is found by one-sided
scanning of the specimen using the backward mode detection of the
ultrasonic pulses reflected from the structure defects. Using the
computer processing of these signals the images are obtained of the
cross-sections of the specimens with cracks. By the increase of the
reference pulse amplitude from 0.1 MPa to 5 MPa the nonlinear
transformation of the ultrasonic pulse passed through the specimen
with horizontal cracks results in the decrease by 2.5 times of the
amplitude of the rarefaction phase and in the increase of its duration
by 2.1 times. By the increase of the reference pulse amplitude from 5
MPa to 10 MPa the time splitting of the phases is observed for the
bipolar pulse passed through the specimen. The compression and
rarefaction phases propagate with different velocities. These features
of the powerful broadband ultrasonic pulses passed through the rock
specimens can be described by the hysteresis model of Preisach-
Mayergoyz and can be used for the location of cracks in the optically
opaque materials.