Abstract: Slag sample from copper smelting operation in a
water jacket furnace from DRC plant was used. The study intends to
determine the effect of cooling in the extraction of base metals. The
cooling methods investigated were water quenching, air cooling and
furnace cooling. The latter cooling ways were compared to the
original as received slag. It was observed that, the cooling rate of the
slag affected the leaching of base metals as it changed the phase
distribution in the slag and the base metals distribution within the
phases. It was also found that fast cooling of slag prevented
crystallization and produced an amorphous phase that encloses the
base metals. The amorphous slags from the slag dumps were more
leachable in acidic medium (HNO3) which leached 46%Cu, 95% Co,
85% Zn, 92% Pb and 79% Fe with no selectivity at pH0, than in
basic medium (NH4OH). The leachability was vice versa for the
modified slags by quenching in water which leached 89%Cu with a
high selectivity as metal extractions are less than 1% for Co, Zn, Pb
and Fe at ambient temperature and pH12. For the crystallized slags,
leaching of base metals increased with the increase of temperature
from ambient temperature to 60°C and decreased at the higher
temperature of 80°C due to the evaporation of the ammonia solution
used for basic leaching, the total amounts of base metals that were
leached in slow cooled slags were very low compared to the
quenched slag samples.
Abstract: An experimental study is presented on the effect
of microstructural change on the Portevin-Le Chatelier effect
behaviour of Al-2.5%Mg alloy. Tensile tests are performed on
the as received and heat treated (at 400 ºC for 16 hours)
samples for a wide range of strain rates. The serrations
observed in the stress-time curve are investigated from
statistical analysis point of view. Microstructures of the
samples are characterized by optical metallography and X-ray
diffraction. It is found that the excess vacancy generated due
to heat treatment leads to decrease in the strain rate sensitivity
and the increase in the number of stress drop occurrences per
unit time during the PLC effect. The microstructural
parameters like domain size, dislocation density have no
appreciable effect on the PLC effect as far as the statistical
behavior of the serrations is considered.
Abstract: Homogeneous composites of alumina and zirconia
with a small amount of MgO (99%) were obtained for ZTA ceramic containing 0.05 wt% MgO in
1500 °C.
Abstract: We report here, the results of molecular dynamics
simulation of p-doped (Ga-face)GaN over n-doped (Siface)(
0001)4H-SiC hetero-epitaxial material system with one-layer
each of Ga-flux and (Al-face)AlN, as the interface materials, in the
form of, the total Density of States (DOS). It is found that the total
DOS at the Fermi-level for the heavily p-doped (Ga-face)GaN and ndoped
(Si-face)4H-SiC hetero-epitaxial system, with one layer of
(Al-face)AlN as the interface material, is comparatively higher than
that of the various cases studied, indicating that there could be good
vertical conduction across the (Ga-face)GaN over (Si-face)(0001)4HSiC
hetero-epitaxial material system.
Abstract: In this paper, the solubility of CO2 in AMP solution
have been measured at temperature range of ( 293, 303 ,313,323)
K.The amine concentration ranges studied are (2.0, 2.8, and 3.4) M.
A solubility apparatus was used to measure the solubility of CO2 in
AMP solution on samples of flue gases from Thermal and Central
Power Plants of Esfahan Steel Company. The modified Kent
Eisenberg model was used to correlate and predict the vapor-liquid
equilibria of the (CO2 + AMP + H2O) system. The model predicted
results are in good agreement with the experimental vapor-liquid
equilibrium measurements.
Abstract: Plastics occupy wide place in the applications of
automotive, electronics and house goods. Especially reinforced
plastics become popular because of their high strength besides their
advantages of low weight and easy manufacturability. In this study,
mechanical and morphological properties of polypropylene (PP) and
high density polyethylene (HDPE) matrix composites reinforced with
surface modified nano titan dioxide (TiO2) particles were
investigated. Surface modification was made by coating the nano
powders with maleic anhydride grafted styrene ethylene butylene
styrene (SEBS-g-MA) and silane, respectively. After surface
modification, PP/TiO2 and HDPE/TiO2 composites were obtained by
using twin screw extruder at titan dioxide loading of 1 wt.%, 3 wt.%
and 5 wt.%. Effects of surface modification were determined by
thermal and morphological analysis. SEBS-g-MA provided bridging
effect between TiO2 particles and polymer matrix while silane was
effective as a dispersant. Depending on that, homogenous structures
without agglomeration were obtained. Mechanical tests were
performed on the injection moldings of the composites for obtaining
the impact strength, tensile strength, stress at break, elongation and
elastic modulus. Reinforced HDPE and PP moldings gave higher
tensile strength and elastic modulus due to the rigid structure of TiO2.
Slight increment was seen in stress at break. Elongation and impact
strength decreased due to the stiffness of the nano titan dioxide.
Abstract: This paper presents the results of an experimental study on the performance of a triboelectric separator of plastic mixtures used for recycling. The separator consists of four cylindrical electrodes. The principle behind the separation technique is based on the difference in the Coulomb force acting on the plastic particles after triboelectric charging. The separation of mixtures of acrylonitrile butadiene styrene (ABS) and polystyrene (PS) using this method was studied. The effects of the triboelectric charging time and applied voltage on the separation efficiency were investigated. The experimental results confirm that it is possible to obtain a high purity and recovery rate for the initial compositions considered in this study.
Abstract: This research was conducted to develop a correlation
between microstructure of HSLA steel and the mechanical properties
that occur as a result of both laser and mechanical forming processes
of the metal. The technique of forming flat metals by applying laser
beams is a relatively new concept in the manufacturing industry.
However, the effects of laser energy on the stability of metal alloy
phases have not yet been elucidated in terms of phase
transformations and microhardness. In this work, CO2 laser source
was used to irradiate the surface of a flat metal then the
microstructure and microhardness of the metal were studied on the
formed specimen. The extent to which the microstructure changed
depended on the heat inputs of up to 1000 J/cm2 with cooling rates of
about 4.8E+02 K/s. Experimental results revealed that the irradiated
surface of a HSLA steel had transformed to austenitic structure
during the heating process.
Abstract: Adsorption of Toluidine blue dye from aqueous solutions onto Neem Leaf Powder (NLP) has been investigated. The surface characterization of this natural material was examined by Particle size analysis, Scanning Electron Microscopy (SEM), Fourier Transform Infrared (FTIR) spectroscopy and X-Ray Diffraction (XRD). The effects of process parameters such as initial concentration, pH, temperature and contact duration on the adsorption capacities have been evaluated, in which pH has been found to be most effective parameter among all. The data were analyzed using the Langmuir and Freundlich for explaining the equilibrium characteristics of adsorption. And kinetic models like pseudo first- order, second-order model and Elovich equation were utilized to describe the kinetic data. The experimental data were well fitted with Langmuir adsorption isotherm model and pseudo second order kinetic model. The thermodynamic parameters, such as Free energy of adsorption (AG"), enthalpy change (AH') and entropy change (AS°) were also determined and evaluated.