Abstract: This paper reports the fatigue crack growth behaviour
of gas tungsten arc, electron beam and laser beam welded Ti-6Al-4V
titanium alloy. Centre cracked tensile specimens were prepared to
evaluate the fatigue crack growth behaviour. A 100kN servo
hydraulic controlled fatigue testing machine was used under constant
amplitude uniaxial tensile load (stress ratio of 0.1 and frequency of
10 Hz). Crack growth curves were plotted and crack growth
parameters (exponent and intercept) were evaluated. Critical and
threshold stress intensity factor ranges were also evaluated. Fatigue
crack growth behaviour of welds was correlated with mechanical
properties and microstructural characteristics of welds. Of the three
joints, the joint fabricated by laser beam welding exhibited higher
fatigue crack growth resistance due to the presence of fine lamellar
microstructure in the weld metal.
Abstract: This paper presents the results of a study aimed at
establishing the temperature distribution during the welding of
magnesium alloy sheets by Pulsed Current Gas Tungsten Arc
Welding (PCGTAW) and Constant Current Gas Tungsten Arc
Welding (CCGTAW) processes. Pulsing of the GTAW welding
current influences the dimensions and solidification rate of the fused
zone, it also reduces the weld pool volume hence a narrower bead. In
this investigation, the base material considered was 2mm thin AZ 31
B magnesium alloy, which is finding use in aircraft, automobile and
high-speed train components. A finite element analysis was carried
out using ANSYS, and the results of the FEA were compared with
the experimental results. It is evident from this study that the finite
element analysis using ANSYS can be effectively used to model
PCGTAW process for finding temperature distribution.