Abstract: Scatter behavior of fatigue life in die-cast AM60B
alloy was investigated. For comparison, those in rolled AM60B alloy
and die-cast A365-T5 aluminum alloy were also studied. Scatter
behavior of pore size was also investigated to discuss dominant
factors for fatigue life scatter in die-cast materials. Three-parameter
Weibull function was suitable to explain the scatter behavior of both
fatigue life and pore size. The scatter of fatigue life in die-cast
AM60B alloy was almost comparable to that in die-cast A365-T5
alloy, while it was significantly large compared to that in the rolled
AM60B alloy. Scatter behavior of pore size observed at fracture
nucleation site on the fracture surface was comparable to that
observed on the specimen cross-section and also to that of fatigue
life. Therefore, the dominant factor for large scatter of fatigue life in
die-cast alloys would be the large scatter of pore size. This
speculation was confirmed by the fracture mechanics fatigue life
prediction, where the pore observed at fatigue crack nucleation site
was assumed as the pre-existing crack.