Abstract: The main aim of the presented experiments is to
improve behaviour of sandwich structures under dynamic loading,
such as crash or explosion. This paper describes experimental
investigation on the response of new advanced materials to low and
high velocity load. Blast wave energy absorbers were designed using
two types of porous lightweight raw particle materials based on
expanded glass and ceramics with dimensions of 0.5-1 mm,
combined with polymeric binder. The effect of binder amount on the
static and dynamic properties of designed materials was observed.
Prism shaped specimens were prepared and loaded to obtain physicomechanical
parameters – bulk density, compressive and flexural
strength under quasistatic load, the dynamic response was determined
using Split Hopkinson Pressure bar apparatus. Numerical
investigation of the material behaviour in sandwich structure was
performed using implicit/explicit solver LS-Dyna. As the last step,
the developed material was used as the interlayer of blast resistant
litter bin, and it´s functionality was verified by real field blast tests.
Abstract: The main aim of the presented experiments is to
improve behaviour of sandwich structures under dynamic loading,
such as crash or explosion. Several cellular materials are widely used
as core of the sandwich structures and their properties influence
the response of the entire element under impact load. To optimize
their performance requires the characterisation of the core material
behaviour at high strain rates and identification of the underlying
mechanism. This work presents the study of high strain-rate
characteristics of a specific porous lightweight blast energy absorbing
foam using a Split Hopkinson Pressure Bar (SHPB) technique
adapted to perform tests on low strength materials. Two different
velocities, 15 and 30 m.s-1 were used to determine the strain
sensitivity of the material. Foams were designed using two types of
porous lightweight spherical raw materials with diameters of 30-
100 *m, combined with polymer matrix. Cylindrical specimens with
diameter of 15 mm and length of 7 mm were prepared and loaded
using a Split Hopkinson Pressure Bar apparatus to assess the relation
between the composition of the material and its shock wave
attenuation capacity.