Abstract: Alumina matrix composites with addition of hexagonal boron nitride (hBN), acting as solid lubricant, were produced. Main purpose of solid lubricants is to dispose the necessity of using cooling lubricants in machining process. Hot pressing was used as a consolidating process for Al2O3-x%wt.hBN (x=1/ 2,5/ 5 /7,5 /10) composites. Properties of sinters such as relative density, hardness, Young-s modulus and fracture toughness were examined. Obtained samples characterize by high relative density. Hardness and fracture toughness values allow the use of alumina – hBN composites for machining steels even in hardened condition. However it was observed that high weight content of hBN can negatively influence the mechanical properties of composites.
Abstract: The influence of extrusion parameters on surface
quality and properties of AA6061+x% vol. SiC (x = 0; 2,5; 5; 7,5;10)
composites was discussed in this paper. The averages size of
AA6061 and SiC particles were 10.6 μm and 0.42 μm, respectively.
Two series of composites (I - compacts were preheated at extrusion
temperature through 0.5 h and cooled by water directly after process;
II - compacts were preheated through 3 hours and were not cooled)
were consolidated via powder metallurgy processing and extruded by
KoBo method. High values of density for both series of composites
were achieved. Better surface quality was observed for II series of
composites. Moreover, for these composites lower (compared to I
series) but more uniform strength properties over the cross-section of
the bar were noticed. Microstructure and Young-s modulus
investigations were made.