Abstract: This paper presents an experimental investigation on
the machinability of laser-sintered material using small ball end mill focusing on wear mechanisms. Laser-sintered material was produced
by irradiating a laser beam on a layer of loose fine SCM-Ni-Cu powder. Bulk carbon steel JIS S55C was selected as a reference steel.
The effects of powder consolidation mechanisms and unsintered
powder on the tool life and wear mechanisms were carried out. Results indicated that tool life in cutting laser-sintered material is
lower than that in cutting JIS S55C. Adhesion of the work material and chipping were the main wear mechanisms of the ball end mill in
cutting laser-sintered material. Cutting with the unsintered powder
surrounding the tool and laser-sintered material had caused major fracture on the cutting edge.
Abstract: In this paper, the wear of high speed steel hobs during
hobbing has been studied. The wear mechanisms are strongly
influenced by the choice of cutting speed. At moderate and high
cutting speeds three major wear mechanisms were identified:
abrasion, mild adhesive and severe adhesive. The microstructure and
wear behavior of two high speed steel grades (M2 and ASP30) has
been compared. In contrast, a variation in chemical composition or
microstructure of HSS tool material generally did not change the
dominant wear mechanism. However, the tool material properties
determine the resistance against the operating wear mechanism and
consequently the tool life. The metallographic analysis and wear
measurement at the tip of hob teeth included scanning electron
microscopy and stereoscope microscopy. Roughness profilometery is
used for measuring the gear surface roughness.