Abstract: This paper reports an experimental work that aimed to investigate the effects of clay brick waste, as part of fine aggregate, on rendering mortar performance. The brick, in crushed form, was from a local brick manufacturer that was rejected due to being of-standard. It was used to replace 33.33 %, 50 %, 66.66 % and 100 % by weight of the quarry sand in mortar. Effects of the brick replacement on the mortar key properties intended for wall plastering were investigated; these are workability, compressive strength, flexural strength, linear shrinkage, water absorption by total immersion and by capillary suction. The results showed that as the brick replacement level increased, the mortar workability reduced. The linear shrinkage increases over time and decreases with the introduction of brick waste. The compressive and flexural strengths decrease with the increase of brick waste because of their great water absorption.
Abstract: In this study, the possibility of using unground oil palm ash (UOPA) for producing foamed concrete is investigated. The UOPA used in this study is produced by incinerating palm oil biomass at a temperature exceeding 1000ºC. A semi-structural density of 1300kg/m3 was used with filler to binder ratio of 1.5 and preliminary water to binder ratio of 0.45. Cement was replaced by UOPA at replacement levels of 0, 25, 35, 45, 55 and 65% by weight of binder. Properties such as density, compressive strength, drying shrinkage and water absorption were investigated to the age of 90 days. The mix with a 35% of UOPA content was chosen to be used as the base material of a newly designed interlocking, mortar-less block system.
Abstract: Geopolymer (cement-free) concrete is the most promising green alternative to ordinary Portland cement concrete and other cementitious materials. While a range of different geopolymer concretes have been produced, a common feature of these concretes is heat curing treatment which is essential in order to provide sufficient mechanical properties in the early age. However, there are several practical issues with the application of heat curing in large-scale structures. The purpose of this study is to develop cement-free concrete without heat curing treatment. Experimental investigations were carried out in two phases. In the first phase (Phase A), the optimum content of water, polycarboxylate based superplasticizer contents and potassium silicate activator in the mix was determined. In the second stage (Phase B), the effect of ground granulated blast furnace slag (GGBFS) incorporation on the compressive strength of fly ash (FA) and Slag based geopolymer mixtures was evaluated. Setting time and workability were also conducted alongside with compressive tests. The results showed that as the slag content was increased the setting time was reduced while the compressive strength was improved. The obtained compressive strength was in the range of 40-50 MPa for 50% slag replacement mixtures. Furthermore, the results indicated that increment of water and superplasticizer content resulted to retarding of the setting time and slight reduction of the compressive strength. The compressive strength of the examined mixes was considerably increased as potassium silicate content was increased.
Abstract: In this paper, shear behavior of reconstituted clay reinforced with varying diameter of sand compaction piles with area replacement-ratio (as) of 6.25, 10.24, 16, 20.25 and 64% in 100mm diameter and 200mm long clay specimens is modeled using consolidated drained and undrained triaxial tests under different confining pressures ranging from 50kPa to 575kPa. The test results show that the stress-strain behavior of the clay was highly influenced by the presence of SCP. The insertion of SCPs into soft clay has shown to have a positive effect on the load carrying capacity of the clay, resulting in a composite soil mass that has greater shear strength and improved stiffness compared to the unreinforced clay due to increased reinforcement area ratio. In addition, SCP also acts as vertical drain in the clay thus accelerating the dissipation of excess pore water pressures that are generated during loading by shortening the drainage path and activating radial drainage, thereby reducing post-construction settlement. Thus, sand compaction piles currently stand as one of the most viable and practical techniques for improving the mechanical properties of soft clays.
Abstract: This study investigated the differences in the objective parameters of sound depending on the changes in the lengths of the lateral surfaces of a space and on the replacement of the sound absorbers that are placed on these surfaces. To this end, three models of room were chosen. The widths and heights of these rooms were the same but the lengths of the rooms were changed. The smallest room was 8 m. wide and 10 m. long. The lengths of the other two rooms were 15 m. and 20 m. For each model, the differences in the objective parameters of sound were determined by keeping all the material in the space intact and by changing only the positions of the sound absorbers that were placed on the walls. The sound absorbers that were used on the walls were of two different sizes. The sound absorbers that were placed on the walls were 4 m and 8 m. long and story-height (3 m.). In all model room types, the sound absorbers were placed on the long walls in three different ways: at the end of the long walls where the long walls meet the front wall; at the end of the long walls where the long walls meet the back wall; and in the middle part of the long walls. Except for the specially placed sound absorbers, the ground, wall and ceiling surfaces were covered with three different materials. There were no constructional elements such as doors and windows on the walls. On the surfaces, the materials specified in the Odeon 10 material library were used as coating material. Linoleum was used as flooring material, painted plaster as wall coating material and gypsum boards as ceiling covering (2 layers with a total of 32 mm. thickness). These were preferred due to the fact that they are the commonly used materials for these purposes. This study investigated the differences in the objective parameters of sound depending on the changes in the lengths of the lateral surfaces of a space and on the replacement of the sound absorbers that are placed on these surfaces. To this end, three models of room were chosen. The widths and heights of these rooms were the same but the lengths of the rooms were changed. The smallest room was 8 m. wide and 10 m. long. The lengths of the other two rooms were 15 m. and 20 m. For each model, the differences in the objective parameters of sound were determined by keeping all the material in the space intact and by changing only the positions of the sound absorbers that were placed on the walls. The sound absorbers that were used on the walls were of two different sizes. The sound absorbers that were placed on the walls were 4 m and 8 m. long and story-height (3 m.). In all model room types, the sound absorbers were placed on the long walls in three different ways: at the end of the long walls where the long walls meet the front wall; at the end of the long walls where the long walls meet the back wall; and in the middle part of the long walls. Except for the specially placed sound absorbers, the ground, wall and ceiling surfaces were covered with three different materials. There were no constructional elements such as doors and windows on the walls. On the surfaces, the materials specified in the Odeon 10 material library were used as coating material. Linoleum was used as flooring material, painted plaster as wall coating material and gypsum boards as ceiling covering (2 layers with a total of 32 mm. thickness). These were preferred due to the fact that they are the commonly used materials for these purposes.
Abstract: The objective of this research is to mitigate and prevent
the alkali silica reactivity (ASR) in highway construction projects.
ASR is a deleterious reaction initiated when the silica content of the
aggregate reacts with alkali hydroxides in cement in the presence of
relatively high moisture content. The ASR results in the formation of
an expansive white colored gel-like material which forms the
destructive tensile stresses inside hardened concrete. In this research, different types of local aggregates available in the
State of Arkansas were mixed and mortar bars were poured according
to the ASTM specifications. Mortar bars expansion was measured
versus time and aggregates with potential ASR problems were
detected. Different types of supplementary cementitious materials
(SCMs) were used in remixing mortar bars with highly reactive
aggregates. Length changes for remixed bars proved that different
types of SCMs can be successfully used in reducing the expansive
effect of ASR. SCMs percentage by weight is highly dependent on
the SCM type. The result of this study will help avoiding future
losses due to ASR cracking in construction project and reduce the
maintenance, repair, and replacement budgets required for highways
network.
Abstract: The cumulative costs for O&M may represent as
much as 65%-90% of the turbine's investment cost. Nowadays the
cost effectiveness concept becomes a decision-making and
technology evaluation metric. The cost of energy metric accounts for
the effect replacement cost and unscheduled maintenance cost
parameters. One key of the proposed approach is the idea of
maintaining the WTs which can be captured via use of a finite state
Markov chain. Such a model can be embedded within a probabilistic
operation and maintenance simulation reflecting the action to be
done. In this paper, an approach of estimating the cost of O&M is
presented. The finite state Markov model is used for decision
problems with number of determined periods (life cycle) to predict
the cost according to various options of maintenance.
Abstract: Concrete is an essential building material which is
widely used in construction industry all over the world due to its
compressible strength. Curing of concrete plays a vital role in
durability and other performance necessities. Improper curing can
affect the concrete performance and durability easily. When areas
like scarcity of water, structures is not accessible by humans external
curing cannot be performed, so we opt for internal curing. Internal
curing (or) self curing plays a major role in developing the concrete
pore structure and microstructure. The concept of internal curing is to
enhance the hydration process to maintain the temperature uniformly.
The evaporation of water in the concrete is reduced by self curing
agent (Super Absorbing Polymer – SAP) there by increasing the
water retention capacity of the concrete. The research work was
carried out to reduce water, which is prime material used for concrete
in the construction industry. Concrete curing plays a major role in
developing hydration process. Concept of self curing will reduce the
evaporation of water from concrete. Self curing will increase water
retention capacity as compared to the conventional concrete. Proper
self curing (or) internal curing increases the strength, durability and
performance of concrete. Super absorbing Polymer (SAP) used as
internal curing agent. In this study 0.2% to 0.4% of SAP was varied
in different grade of high strength concrete. In the experiment
replacement of cement by silica fumes with 5%, 10% and 15% are
studied. It is found that replacement of silica fumes by 10 % gives
more strength and durability when compared to others.
Abstract: In the present research, whole meal barley flour
(WBF) was supplemented with gelatinized corn flour (GCF) in 0 and
30%. Whole meal wheat flour (WWF) was mixed with defatted rice
bran (DRB) to produce 0, 20, 25, and 30% replacement levels.
Rheological properties of dough were studied. Thermal properties
and starch crystallinity of flours were evaluated. Flat bread, balady
bread and pie were prepared from the different flour blends. The
different bakeries were sensory evaluated. Color of raw materials and
crust of bakery products were determined. Nutrients contents of raw
flours and food products were assessed. Results showed that addition
of GCF to WBF increased the viscosity and falling number of the
produced dough. Water absorption, dough development time and
dough stability increased with increasing the level of DRB in dough
while, weakening and mixing tolerance index decreased.
Extensibility and energy decreased, while, resistance to extension
increased as DRB level increased. Gelatinized temperature of WWF,
WBF, GCF, and DRB were 13.26, 35.09, 28.33, and 39.63,
respectively. Starch crystallinity was affected when DRB was added
to WWF. The highest protein content was present in balady bread
made from 70% WWF and 30% DRB. The highest calcium,
phosphorus, and potassium levels were present in products made
from 100% WBF. Sensory attributes of the products were slightly
affected by adding DRB and GCF. Conclusion: Addition of DRB or
GCF to WWF or WBF, respectively affect the physical, chemical,
rheological and sensory properties of balady bread, flat bread, and pie
while improved their nutritive values.
Abstract: Fresh concrete has one of dynamic properties known
as slump. Slump of concrete is design to compatible with placing
method. Due to hydration reaction of cement, the slump of concrete
is loss through time. Therefore, delayed concrete probably get reject
because slump is unacceptable. In order to recover the slump of
delayed concrete the second dose of superplasticizer (naphthalene
based type F) is added into the system, the slump recovery can be
done as long as the concrete is not setting. By adding superplasticizer
as solution for recover unusable slump loss concrete may affects
other concrete properties. Therefore, this paper was observed setting
times and compressive strength of concrete after being re-dose with
chemical admixture type F (superplasticizer, naphthalene based) for
slump recovery. The concrete used in this study was fly ash concrete
with fly ash replacement of 0%, 30% and 50% respectively. Concrete
mix designed for test specimen was prepared with paste content (ratio
of volume of cement to volume of void in the aggregate) of 1.2 and
1.3, water-to-binder ratio (w/b) range of 0.3 to 0.58, initial dose of
superplasticizer (SP) range from 0.5 to 1.6%. The setting times of
concrete were tested both before and after re-dosed with different
amount of second dose and time of dosing. The research was
concluded that addition of second dose of superplasticizer would
increase both initial and final setting times accordingly to dosage of
addition. As for fly ash concrete, the prolongation effect was higher
as the replacement of fly ash increase. The prolongation effect can
reach up to maximum about 4 hours. In case of compressive strength,
the re-dosed concrete has strength fluctuation within acceptable range
of ±10%.
Abstract: Coal fly ash, an industrial by product of coal
combustion thermal power plants is considered as a hazardous
material and its improper disposal has become an environmental
issue. On the other hand, manufacturing conventional clay bricks
involves on consumption of large amount of clay and leads
substantial depletion of topsoil. This paper unveils the possibility of
using fly ash as a partial replacement of clay for brick manufacturing
considering the local technology practiced in Bangladesh. The effect
of fly ash with different replacing ratio (0%, 20%, 30%, 40%, and
50% by volume) of clay on properties of bricks was studied. Bricks
were made in the field parallel to ordinary bricks marked with
specific number for different percentage to identify them at time of
testing. No physical distortion is observed in fly ash brick after
burning in the kiln. Results from laboratory test show that
compressive strength of brick is decreased with the increase of fly
ash and maximum compressive strength is found to be 19.6 MPa at
20% of fly ash. In addition, water absorption of fly ash brick is
increased with the increase of fly ash. The abrasion value and
Specific gravity of coarse aggregate prepared from brick with fly ash
also studied and the results of this study suggests that 20% fly ash
can be considered as the optimum fly ash content for producing good
quality bricks utilizing present practiced technology.
Abstract: Local steel slag is produced as a by-product during the
oxidation of steel pellets in an electric arc furnace. Using local steel
slag waste as a hundred substitutes of crashed stone in construction
materials would resolve the environmental problems caused by the
large-scale depletion of the natural sources of crashed stone. This
paper reports the experimental study to investigate the influence of a
hundred replacement of crashed stone as a coarse aggregate with
local steel slag, on the fresh and hardened geopolymer concrete
properties. The investigation includes traditional testing of hardening
concrete, for selected mixes of cement and geopolymer concrete. It
was found that local steel slag as a coarse aggregate enhanced the
slump test of the fresh state of cement and geopolymer concretes.
Nevertheless, the unit weight of concretes was affected. Meanwhile,
the good performance was observed when fly ash used as geopolymer
concrete based.
Abstract: A clay soil classified as A-7-6 and CH soil according
to AASHTO and unified soil classification system respectively, was
stabilized using A-3 soil (AASHTO soil classification system). The
clay soil was replaced with 0%, 10%, 20%, to 100% A-3 soil,
compacted at both British Standard Light (BSL) and British Standard
Heavy (BSH) compaction energy levels and using Unconfined
Compressive Strength (UCS) as evaluation criteria. The Maximum
Dry Density (MDD) of the treated soils at both the BSL and BSH
compaction energy levels showed increase from 0% to 40% A-3 soil
replacement after which the values reduced to 100% replacement.
The trend of the Optimum Moisture Content (OMC) with varied A-3
soil replacement was similar to that of MDD but in a reversed order.
The OMC reduced from 0% to 40% A-3 soil replacement after which
the values increased to 100% replacement. This trend was attributed
to the observed reduction in void ratio from 0% to 40% replacement
after which the void ratio increased to 100% replacement. The
maximum UCS for the soil at varied A-3 soil replacement increased
from 272 and 770 kN/m2 for BSL and BSH compaction energy level
at 0% replacement to 295 and 795 kN/m2 for BSL and BSH
compaction energy level respectively at 10% replacement after which
the values reduced to 22 and 60 kN/m2 for BSL and BSH compaction
energy level respectively at 70% replacement. Beyond 70%
replacement, the mixtures could not be moulded for UCS test.
Abstract: The need to save time and cost of soil testing at the
planning stage of road work has necessitated developing predictive
models. This study proposes a model for predicting the dry density of
lateritic soils stabilized with corn cob ash (CCA) and blended cement
- CCA. Lateritic soil was first stabilized with CCA at 1.5, 3.0, 4.5 and
6% of the weight of soil and then stabilized with the same
proportions as replacement for cement. Dry density, specific gravity,
maximum degree of saturation and moisture content were determined
for each stabilized soil specimen, following standard procedure.
Polynomial equations containing alpha and beta parameters for CCA
and blended CCA-cement were developed. Experimental values were
correlated with the values predicted from the Matlab curve fitting
tool, and the Solver function of Microsoft Excel 2010. The correlation
coefficient (R2) of 0.86 was obtained indicating that the model could
be accepted in predicting the maximum dry density of CCA stabilized
soils to facilitate quick decision making in roadworks.
Abstract: Cortisol is essential to the regulation of the immune
system and pathological yawning is a symptom of multiple sclerosis
(MS). Electromyography activity (EMG) in the jaw muscles typically
rises when the muscles are moved – extended or flexed; and yawning
has been shown to be highly correlated with cortisol levels in healthy
people as shown in the Thompson Cortisol Hypothesis. It is likely
that these elevated cortisol levels are also seen in people with MS.
The possible link between EMG in the jaw muscles and rises in saliva
cortisol levels during yawning were investigated in a randomized
controlled trial of 60 volunteers aged 18-69 years who were exposed
to conditions that were designed to elicit the yawning response.
Saliva samples were collected at the start and after yawning, or at the
end of the presentation of yawning-provoking stimuli, in the absence
of a yawn, and EMG data was additionally collected during rest and
yawning phases. Hospital Anxiety and Depression Scale, Yawning
Susceptibility Scale, General Health Questionnaire, demographic,
and health details were collected and the following exclusion criteria
were adopted: chronic fatigue, diabetes, fibromyalgia, heart
condition, high blood pressure, hormone replacement therapy,
multiple sclerosis, and stroke. Significant differences were found
between the saliva cortisol samples for the yawners, t (23) = -4.263, p
= 0.000, as compared with the non-yawners between rest and poststimuli,
which was non-significant. There were also significant
differences between yawners and non-yawners for the EMG
potentials with the yawners having higher rest and post-yawning
potentials. Significant evidence was found to support the Thompson
Cortisol Hypothesis suggesting that rises in cortisol levels are
associated with the yawning response. Further research is underway
to explore the use of cortisol as a potential diagnostic tool as an assist
to the early diagnosis of symptoms related to neurological disorders.
Bournemouth University Research & Ethics approval granted:
JC28/1/13-KA6/9/13. Professional code of conduct, confidentiality,
and safety issues have been addressed and approved in the Ethics
submission. Trials identification number: ISRCTN61942768.
http://www.controlled-trials.com/isrctn/
Abstract: This paper investigates the effectiveness of two
natural zeolites in reducing expansion of concrete due to alkali-silica
reaction. These natural zeolites have different reactive silica content.
Three aggregates; two natural sands and one crushed stone aggregate
were used while preparing mortar bars in accordance with accelerated
mortar bar test method, ASTM C1260. Performances of natural
zeolites are compared by examining the expansions due to alkali
silica reaction. Natural zeolites added to the mixtures at 10% and
20% replacement levels by weight of cement. Natural zeolite with
high reactive silica content had better performance on reducing
expansions due to ASR. In this research, using high reactive zeolite at
20% replacement levels was effective in mitigating expansions.
Abstract: In this paper, relationship between different properties
of IC concrete and water cement ratio, obtained from a
comprehensive experiment conducted on IC using local materials
(Burnt clay chips- BC) is presented. In addition, saturated SAP was
used as an IC material in some cases. Relationships have been
developed through regression analysis. The focus of this analysis is
on developing relationship between a dependent variable and an
independent variable. Different percent replacements of BC and
water cement ratios were used. Compressive strength, modulus of
elasticity, water permeability and chloride permeability were tested
and variations of these parameters were analyzed with respect to
water cement ratio.
Abstract: Useful lifetime evaluation of chevron rubber spring
was very important in design procedure to assure the safety and
reliability. It is, therefore, necessary to establish a suitable criterion
for the replacement period of chevron rubber spring. In this study, we
performed characteristic analysis and useful lifetime prediction of
chevron rubber spring. Rubber material coefficient was obtained by
curve fittings of uniaxial tension equibiaxial tension and pure shear
test. Computer simulation was executed to predict and evaluate the
load capacity and stiffness for chevron rubber spring. In order to
useful lifetime prediction of rubber material, we carried out the
compression set with heat aging test in an oven at the temperature
ranging from 50°C to 100°C during a period 180 days. By using the
Arrhenius plot, several useful lifetime prediction equations for rubber
material was proposed.
Abstract: Ceramic Waste Aggregates (CWAs) were made from
electric porcelain insulator wastes supplied from an electric power
company, which were crushed and ground to fine aggregate sizes. In
this study, to develop the CWA mortar as an eco–efficient, ground
granulated blast–furnace slag (GGBS) as a Supplementary
Cementitious Material (SCM) was incorporated. The water–to–binder
ratio (W/B) of the CWA mortars was varied at 0.4, 0.5, and 0.6. The
cement of the CWA mortar was replaced by GGBS at 20 and 40% by
volume (at about 18 and 37% by weight). Mechanical properties of
compressive and splitting tensile strengths, and elastic modulus were
evaluated at the age of 7, 28, and 91 days. Moreover, the chloride
ingress test was carried out on the CWA mortars in a 5.0% NaCl
solution for 48 weeks. The chloride diffusion was assessed by using an
electron probe microanalysis (EPMA). To consider the relation of the
apparent chloride diffusion coefficient and the pore size, the pore size
distribution test was also performed using a mercury intrusion
porosimetry at the same time with the EPMA. The compressive
strength of the CWA mortars with the GGBS was higher than that
without the GGBS at the age of 28 and 91 days. The resistance to the
chloride ingress of the CWA mortar was effective in proportion to the
GGBS replacement level.
Abstract: The article describes the effect of the replacement of
the used reference coordinate system in the georeferencing of an old
map of Europe. The map was georeferenced into three types of
projection – the equal-area conic (original cartographic projection),
cylindrical Plate Carrée and cylindrical Mercator map projection. The
map was georeferenced by means of the affine and the second-order
polynomial transformation. The resulting georeferenced raster
datasets from the Plate Carrée and Mercator projection were
projected into the equal-area conic projection by means of projection
equations. The output is the comparison of drawn graphics, the
magnitude of standard deviations for individual projections and types
of transformation.