Abstract: In this research, zinc coatings were fabricated by electroplating process in a sulfate solution under direct and pulse current conditions. In direct and pulse current conditions, effect of maximum current was investigated on the coating properties. Also a comparison was made between the obtained coatings under direct and pulse current. Morphology of the coatings was investigated by scanning electron microscopy (SEM). Corrosion behavior of the coatings was investigated by potentiodynamic polarization test. In pulse current conditions, the effect of pulse frequency and duty cycle was also studied. The effect of these conditions and parameters were also investigated on morphology and corrosion behavior. All of DC plated coatings are showing a distinct passivation area in -1 to -0.4 V range. Pulsed current coatings possessed a higher corrosion resistance. The results showed that current density is the most important factor regarding the fabrication process. Furthermore, a rise in duty cycle deteriorated corrosion resistance of coatings. Pulsed plated coatings performed almost 10 times better than DC plated coatings.
Abstract: The present paper aims to investigate the effects of the welding process parameters and cooling state on the weld bead geometry, mechanical properties and microstructure characteristics for weldments of AISI 304L stainless steel. The welding process was carried out using TIG welding with pulsed/non-pulsed current techniques. The cooling state was introduced as an input parameter to investigate the main effects on the structure morphology and thereby the mechanical property. This paper clarifies microstructure- mechanical property relationship of the welded specimens. In this work, the selected pulse frequency levels were 5-500 Hz in order to study the effect of low and high frequencies on the weldment characteristics using filler metal of ER 308LSi. The key findings of this work clarified that the pulse frequency has a significant effect on the breaking of the dendrite arms during the welding process and so strongly influences on the tensile strength and microhardness. The cooling state also significantly affects on the microstructure texture and thereby, the mechanical properties. The most important factor affects the bead geometry and aspect ratio is the travel speed and pulse frequency.
Abstract: Pure nickel coatings have been successfully
electrodeposited on copper substrates by the pulse plating technique.
The influence of current density, duty cycle and pulse frequency on
the surface morphology, crystal orientation, and microhardness was
determined. It was found that the crystallite size of the deposit
increases with increasing current density and duty cycle. The crystal
orientation progressively changed from a random texture at 1 A/dm2
to (200) texture at 10 A/dm2. Increasing pulse frequency resulted in
increased texture coefficient and peak intensity of (111) reflection.
An increase in duty cycle resulted in considerable increase in texture
coefficient and peak intensity of (311) reflection. Coatings obtained
at high current densities and duty cycle present a mixed morphology
of small and large grains. Maximum microhardness of 193 Hv was
achieved at 4 A/dm2, 10 Hz and duty cycle of 50%. Nickel coatings
with (200) texture are ductile while (111) texture improves the
microhardness of the coatings.
Abstract: Taguchi approach was applied to determine the most influential control factors which will yield better tensile strength of the joints of pulse TIG welded 70/30 Cu-Ni alloy. In order to evaluate the effect of process parameters such as pulse frequency, peak current, base current and welding speed on tensile strength of Pulsed current TIG welded 70/30 Cu-Ni alloy of 5 mm thickness, Taguchi parametric design and optimization approach was used. Through the Taguchi parametric design approach, the optimum levels of process parameters were determined at 95% confidence level. The results indicate that the Pulse frequency, peak current, welding speed and base current are the significant parameters in deciding the tensile strength of the joint. The predicted optimal values of tensile strength of Pulsed current Gas tungsten arc welding (PC GTAW) of 70/30 Cu-Ni alloy welds are 368.8MPa.
Abstract: Laser engraving is a manufacturing method for those applications where previously Electrical Discharge Machining (EDM) was the only choice. Laser engraving technology removes material layer-by-layer and the thickness of layers is usually in the range of few microns. The aim of the present work is to investigate the influence of the process parameters on the surface quality when machined by laser engraving. The examined parameters were: the pulse frequency, the beam speed and the layer thickness. The surface quality was determined by the surface roughness for every set of parameters. Experimental results on Al7075 material showed that the surface roughness strictly depends on the process parameters used.