Abstract: Increase in population has increased the demand of energy to fulfill all its needs. This will result in burden on fossil fuels especially crude oil. Waste oil due to its disposal problem creates environmental degradation. In this context, this paper studies utilization of waste cooking oil and waste motor sludge for making lubricating grease. Experimental studies have been performed by variation in time and concentration of mixture of waste cooking oil and waste motor sludge. The samples were analyzed using penetration test (ASTM D-217), dropping point (ASTM D-566), work penetration (ASTM D-217) and copper strip test (ASTM D-408). Among 6 samples, sample 6 gives the best results with a good drop point and a fine penetration value. The dropping point and penetration test values were found to be 205 °C and 315, respectively. The penetration value falls under the category of NLGI (National Lubricating Grease Institute) consistency number 1.
Abstract: One of the important factors of cracks on the asphalt
pavements is bitumen aging that associated with the loss of volatile
components and oxidation of asphalt binder. This paper is about
effect of Styrene-Butadiene-Styrene (SBS) polymer on asphalt aging
In order to decrease asphalt aging effects. For this purpose samples of
base bitumen and SBS modified bitumen aged according to the
rolling thin film oven test (RTFOT) and pressure aging vessel (PAV),
respectively. Properties of each sample were evaluated using Fourier
Transform Infrared (FTIR) spectroscopy, n-heptane precipitation,
viscosity test, softening point test and penetration test. FT-IR
Analysis, showed lower oxidation of SBS modified bitumen than
base bitumen, after aging.