Abstract: This paper present some preliminary work on the
preparation and physicochemical caracterization of nanocomposite
MFI-alumina structures based on alumina hollow fibres. The fibers
are manufactured by a wet spinning process. α-alumina particles were
dispersed in a solution of polysulfone in NMP. The resulting slurry is
pressed through the annular gap of a spinneret into a precipitation
bath. The resulting green fibres are sintered. The mechanical strength
of the alumina hollow fibres is determined by a three-point-bending
test while the pore size is characterized by bubble-point testing. The
bending strength is in the range of 110 MPa while the average pore
size is 450 nm for an internal diameter of 1 mm and external diameter
of 1.7 mm. To characterize the MFI membranes various techniques
were used for physicochemical characterization of MFI–ceramic
hollow fibres membranes: The nitrogen adsorption, X-ray
diffractometry, scanning electron microscopy combined with X
emission microanalysis. Scanning Electron Microscopy (SEM) and
Energy Dispersive Microanalysis by the X-ray were used to observe
the morphology of the hollow fibre membranes (thickness,
infiltration into the carrier, defects, homogeneity). No surface film,
has been obtained, as observed by SEM and EDX analysis and
confirmed by high temperature variation of N2 and CO2 gas
permeances before cation exchange. Local analysis and characterise
(SEM and EDX) and overall (by ICP elemental analysis) were
conducted on two samples exchanged to determine the quantity and
distribution of the cation of cesium on the cross section fibre of the
zeolite between the cavities.
Abstract: New design of a grid for preparation of high density
granules with enhanced mechanical strength by granulation of
dispersed materials is suggested.
A method for hydrodynamic dimensioning of the grid depending
on granulation conditions, hydrodynamic regime of the operation,
dispersity and physicochemical characteristics of the materials to be
granulated was suggested.
The aim of the grid design is to solve the problems arising by the
granulation of disperse materials.
Abstract: Carbon nanotubes (CNTs) are attractive because of
their excellent chemical durability mechanical strength and electrical
properties. Therefore there is interest in CNTs for not only electrical
and mechanical application, but also biological and medical
application.
In this study, the dispersion power of surfactant-treated multiwalled
carbon nanotubes (MWCNTs) and their effect on the antibacterial
activity were examined. Surfactant was used sodium
dodecyl-benzenesulfonate (SDBS). UV-vis absorbance and
transmission electron microscopy(TEM) were used to characterize the
dispersion of MWCNTs in the aqueous phase, showing that the
surfactant molecules had been adsorbed onto the MWCNTs surface.
The surfactant-treated MWCNTs exhibited antimicrobial activities
to streptococcus mutans. The optical density growth curves and viable
cell number determined by the plating method suggested that the
antimicrobial activity of surfactant-treated MWCNTs was both
concentration and treatment time-dependent.
Abstract: This paper presents the experiment results of investigating the effects of adding various types and proportions of fibre on mechanical strength and permeability characteristics of recycled aggregate concrete (RAC), which was produced with treated coarse recycled concrete aggregate (RCA). Two types of synthetic fibres (i.e., barchip and polypropylene fibre) with various volume fractions were added to the RAC, which was calculated by the weight of the cement. The hardened RAC properties such as compressive strength, flexural strength, ultrasonic pulse velocity, water absorption and total porosity at the curing ages of 7 and 28 days were evaluated and compared with the properties of the control specimens. Results indicate that the treated coarse RCA enhances the mechanical strength and permeability properties of RAC and adding barchip fibre further optimises the results. Adding 1.2% barchip fibre has the best effect on the mechanical strength performance of the RAC.