Abstract: The present study is based on the three-dimensional digital analysis by the finite elements method of the mechanical loading effect on the delamination of unidirectional and multidirectional stratified composites. The aim of this work is the determination of the release energy rate G in mode I and the Von Mises equivalent constraint distribution along the damaged area under the influence of several parameters such as the applied load and the delamination size. The results obtained in this study show that the unidirectional composite laminates have better mechanical resistance one the loading line than the multidirectional composite laminates.
Abstract: A composite material with carbon fiber and polymer
matrix has been used as adherent for manufacturing adhesive joints.
In order to evaluate different fiber orientations on joint performance,
the adherents with the 0°, ±15°, ±30°, ±45° fiber orientations were
used in the single lap joint configuration. The joints with an overlap
length of 25 mm were prepared according to the ASTM 1002
specifications and subjected to tensile loadings. The structural
adhesive used was a two-part epoxy to be cured at 70°C for an hour.
First, mechanical behaviors of the adherents were measured using
three point bending test. In the test, considerations were given to
stress to failure and elastic modulus. The results were compared with
theoretical ones using rule of mixture. Then, the joints were
manufactured in a specially prepared jig, after a proper surface
preparation. Experimental results showed that the fiber orientations
of the adherents affected the joint performance considerably; the
joints with ±45° adherents experienced the worst shear strength, half
of those with 0° adherents, and in general, there was a great
relationship between the fiber orientations and failure mechanisms.
Delamination problems were observed for many joints, which were
thought to be due to peel effects at the ends of the overlap. It was
proved that the surface preparation applied to the adherent surface
was adequate. For further explanation of the results, a numerical
work should be carried out using a possible non-linear analysis.
Abstract: Government reports and published research have
flagged and brought to public attention the deteriorating condition of
a large percentage of bridges in Canada and the United States. With
the increasing number of deteriorated bridges in the US, Canada, and
around the globe, condition assessment techniques of concrete
bridges are evolving. Investigation for bridges’ defects such as
cracks, spalls, and delamination and their level of severity are the
main objectives of condition assessment. Inspection and
rehabilitation programs are being implemented to monitor and
maintain deteriorated bridge infrastructure. This paper highlights the
state-of-the art of current practices being performed for concrete
bridge inspection. The information is gathered from the literature and
through a distributed questionnaire. The current practices in concrete
bridge inspection rely on the use of hummer sounding and chain
dragging tests. Non-Destructive Testing (NDT) techniques are not
being utilized fully in the process. Nonetheless, they are being
partially utilized by the recommendation of the bridge inspector after
conducting visual inspection. Lanes are usually closed during the
performance of visual inspection and bridge inspection in general.
Abstract: Aim of this work is to determine the theoretical and
experimental properties of filament wound glass fiber/epoxy resin
composite pipes with different winding design subjected under
bending. For determination of bending strength of composite samples
three point bending tests were conducted. Good correlation between
theoretical and experimental results has been obtained, where sample
No4 has shown the highest value of bending strength. All samples
have demonstrated matrix cracking and fiber failure followed by
layers delamination during testing. Also, it was found that smaller
winding angles lead to an increase in bending stress. From presented
results good merger between glass fibers and epoxy resin was
confirmed by SEM analysis.
Abstract: An Australian manufacturer has fabricated an
innovative GFRP sandwich panel made from E-glass fiber skin and a
modified phenolic core for structural applications. Debonding, which
refers to separation of skin from the core material in composite
sandwiches, is one of the most common types of damage in
composites. The presence of debonding is of great concern because it
not only severely affects the stiffness but also modifies the dynamic
behaviour of the structure. Generally it is seen that the majority of
research carried out has been concerned about the delamination of
laminated structures whereas skin-core debonding has received
relatively minor attention. Furthermore it is observed that research
done on composite slabs having multiple skin-core debonding is very
limited. To address this gap, a comprehensive research investigating
dynamic behaviour of composite panels with single and multiple
debonding is presented. The study uses finite-element modelling and
analyses for investigating the influence of debonding on free
vibration behaviour of single and multilayer composite sandwich
panels. A broad parametric investigation has been carried out by
varying debonding locations, debonding sizes and support conditions
of the panels in view of both single and multiple debonding.
Numerical models were developed with Strand7 finite element
package by innovatively selecting the suitable elements to diligently
represent their actual behavior. Three-dimensional finite element
models were employed to simulate the physically real situation as
close as possible, with the use of an experimentally and numerically
validated finite element model. Comparative results and conclusions
based on the analyses are presented. For similar extents and locations
of debonding, the effect of debonding on natural frequencies appears
greatly dependent on the end conditions of the panel, giving greater
decrease in natural frequency when the panels are more restrained.
Some modes are more sensitive to debonding and this sensitivity
seems to be related to their vibration mode shapes. The fundamental
mode seems generally the least sensitive mode to debonding with
respect to the variation in free vibration characteristics. The results
indicate the effectiveness of the developed three dimensional finite
element models in assessing debonding damage in composite
sandwich panels.
Abstract: The FOSDT (the First Order Shear Deformation
Theory) is taking into consideration to study the static behavior of a
bimorph beam, with a delamination zone between the upper and the
lower layer. The effect of limit conditions and lengths of the
delamination zone are presented in this paper, with a PVDF
piezoelectric material application. A FEM “Finite Element Method”
is used to discretize the beam. In the axial displacement, a
displacement field appears in the debonded zone with inverse effect
between the upper and the lower layer was observed.
Abstract: In rapid industrial development, the demand for
high-strength and lightweight materials have been increased. Thus,
various CFRP (Carbon Fiber Reinforced Plastics) with composite
materials are being used. The design variables of CFRP are its
lamination direction, order and thickness. Thus, the hardness and
strength of CFRP depends much on their design variables. In this
paper, the lamination direction of CFRP was used to produce a
symmetrical ply [0°/0°, -15°/+15°, -30°/+30°, -45°/+45°, -60°/+60°,
-75°/+75° and 90°/90°] and an asymmetrical ply [0°/15°, 0°/30°,
0°/45°, 0°/60° 0°/75° and 0°/90°]. The bending flexure stress of the
CFRP specimen was evaluated through a bending test. Its thermal
property was measured using an infrared camera. The symmetrical
specimen and the asymmetrical specimen were analyzed. The results
showed that the asymmetrical specimen increased the bending loads
according to the increase in the orientation angle; and from 0°, the
symmetrical specimen showed a tendency opposite the asymmetrical
tendency because the tensile force of fiber differs at the vertical
direction of its load. Also, the infrared camera showed that the thermal
property had a trend similar to that of the mechanical properties.
Abstract: Fiber Bragg optic sensor is embedded in composite
material to detect and monitor the damage that occurs in composite
structures. In this paper, we deal with the mode-Ι delamination to
determine the material strength to crack propagation, using the
coupling mode theory and T-matrix method to simulate the FBGs
spectrum for both uniform and non-uniform strain distribution. The
double cantilever beam test is modeled in FEM to determine the
longitudinal strain. Two models are implemented, the first is the
global half model, and the second is the sub-model to represent the
FBGs with higher refined mesh. This method can simulate damage in
composite structures and converting strain to a wavelength shifting in
the FBG spectrum.
Abstract: The prepreg process among the CFRP (Carbon Fiber
Reinforced Plastic) forming methods is the short term of
‘Pre-impregnation’, which is widely used for aerospace composites
that require a high quality property such as a fiber-reinforced woven
fabric, in which an epoxy hardening resin is impregnated the reality.
However, that this process requires continuous researches and
developments for its commercialization because the delamination
characteristically develops between the layers when a great weight is
loaded from outside to supplement such demerit, three lamination
methods among the prepreg lamination methods of CFRP were
designed to minimize the delamination between the layers due to
external impacts. Further, the newly designed methods and the
existing lamination methods were analyzed through a mechanical
characteristic test, Interlaminar Shear Strength test. The Interlaminar
Shear Strength test result confirmed that the newly proposed three
lamination methods, i.e. the Roll, Half and Zigzag laminations,
presented more excellent strengths compared to the conventional Ply
lamination. The interlaminar shear strength in the roll method with
relatively dense fiber distribution was approximately 1.75% higher
than that in the existing ply lamination method, and in the half method,
it was approximately 0.78% higher.
Abstract: The design of an optimised horizontal axis 5-meter-long wind turbine rotor blade in according with IEC 61400-2 standard is a research and development project in order to fulfil the requirements of high efficiency of torque from wind production and to optimise the structural components to the lightest and strongest way possible. For this purpose, a research study is presented here by focusing on the structural characteristics of a composite wind turbine blade via finite element modelling and analysis tools. In this work, first, the required data regarding the general geometrical parts are gathered. Then, the airfoil geometries are created at various sections along the span of the blade by using CATIA software to obtain the two surfaces, namely; the suction and the pressure side of the blade in which there is a hat shaped fibre reinforced plastic spar beam, so-called chassis starting at 0.5m from the root of the blade and extends up to 4 m and filled with a foam core. The root part connecting the blade to the main rotor differential metallic hub having twelve hollow threaded studs is then modelled. The materials are assigned as two different types of glass fabrics, polymeric foam core material and the steel-balsa wood combination for the root connection parts. The glass fabrics are applied using hand wet lay-up lamination with epoxy resin as METYX L600E10C-0, is the unidirectional continuous fibres and METYX XL800E10F having a tri-axial architecture with fibres in the 0,+45,-45 degree orientations in a ratio of 2:1:1. Divinycell H45 is used as the polymeric foam. The finite element modelling of the blade is performed via MSC PATRAN software with various meshes created on each structural part considering shell type for all surface geometries, and lumped mass were added to simulate extra adhesive locations. For the static analysis, the boundary conditions are assigned as fixed at the root through aforementioned bolts, where for dynamic analysis both fixed-free and free-free boundary conditions are made. By also taking the mesh independency into account, MSC NASTRAN is used as a solver for both analyses. The static analysis aims the tip deflection of the blade under its own weight and the dynamic analysis comprises normal mode dynamic analysis performed in order to obtain the natural frequencies and corresponding mode shapes focusing the first five in and out-of-plane bending and the torsional modes of the blade. The analyses results of this study are then used as a benchmark prior to modal testing, where the experiments over the produced wind turbine rotor blade has approved the analytical calculations.
Abstract: Material damages dynamic analysis is difficult to deal with different material geometry and mechanism. In addition, it is difficult to measure the dynamic behavior of cracks, debond and delamination inside the material. Different simulation methods are developed in recent years for different physical features of mechanical systems like vibration and acoustic. Nonlinear fractures are analyzed and identified for different locations in this paper. The main idea of this work is to perform dynamic analysis on different types of materials (from normal homogeneous material to complex composite laminates). Technical factors like cracks, voids, interfaces and the damages’ locations are evaluated. In this project the modal analysis is performed on different types of materials. The results could be helpful in finding modal frequencies, natural frequencies, Time domain and fast Fourier transform (FFT) in industrial applications.
Abstract: This paper presents the results of an experimental characterization of a glass fibre-epoxy composite. The behavior of the traditional two-phase composite has been compared with the one of a new three-phase composite where the epoxy matrix was modified by addition of a 3% weight fraction of montmorillonite nano-particles. Two different types of nano-clays, Cloisite® 30B and RXG7000, produced by Southern Clay Products Inc., have been considered. Three-point bending tests, both monotonic and cyclic, were carried out. A strong reduction of the ultimate flexural strength upon nano-modification has been observed in quasi-static tests. Fatigue tests yielded a smaller strength loss. In both quasi-static and fatigue tests a more pronounced tendency to delamination has been noticed in three-phase composites, especially in the case of 30B nano-clay, with respect to the standard two-phase glass fiber composite.
Abstract: The study focuses to investigate the thermal response of delaminations and develop mathematical models using numerical results to obtain the optimum heat requirement and time to identify delaminations in GLARE type of Fibre Metal Laminates (FML) in both reflection mode and through-transmission (TT) mode of step pulsed active thermography (SPAT) method in the type of nondestructive testing and evaluation (NDTE) technique. The influence of applied heat flux and time on various sizes and depth of delaminations in FML is analyzed to investigate the thermal response through numerical simulations. A finite element method (FEM) is applied to simulate SPAT through ANSYS software based on 3D transient heat transfer principle with the assumption of reflection mode and TT mode of observation individually.
The results conclude that the numerical approach based on SPAT in reflection mode is more suitable for analysing smaller size of near-surface delaminations located at the thermal stimulator side and TT mode is more suitable for analysing smaller size of deeper delaminations located far from thermal stimulator side or near thermal detector/Infrared camera side. The mathematical models provide the optimum q and T at the required MRTD to identify unidentified delamination 7 with 25015.0022W/m2 at 2.531sec and delamination 8 with 16663.3356 W/m2 at 1.37857sec in reflection mode. In TT mode, the delamination 1 with 34954W/m2 at 13.0399sec, delamination 2 with 20002.67W/m2 at 1.998sec and delamination 7 with 20010.87 W/m2 at 0.6171sec could be identified.
Abstract: The finite element analysis is adopted in this primary study. Using the Tsai-Wu criterion and delamination criterion, the stacking sequence [45/04/-454/904]s is the final optimal design for the wheelchair frame. On the contrary, the uni-directional laminates, i.e. [9013]s, [4513]s and [-4513]s, are bad designs due to the higher failure indexes.
Abstract: Occurrence of popcorn in IC packages while assembling them onto the PCB is a well known moisture sensitive reliability issues, especially for surface mount packages. Commonly reflow soldering simulation process is conducted to assess the impact of assembling IC package onto PCB. A strain gauge-based instrumentation is developed to investigate the popcorn effect in surface mount packages during reflow soldering process. The instrument is capable of providing real-time quantitative information of the occurrence popcorn phenomenon in IC packages. It is found that the popcorn occur temperatures between 218 to 241°C depending on moisture soak condition, but not at the peak temperature of the reflow process. The presence of popcorn and delamination are further confirmed by scanning acoustic tomography as a failure analysis.
Abstract: Sandwich plates are finding an increasing range of application in the aircraft industry. The inspection of honeycomb composite structure by conventional ultrasonic technique is complex and very time consuming. The present study demonstrates a technique using guided Lamb waves at low frequencies to predict de-bond defects in aluminum skin-honeycomb core sandwich structure used in aeronautics. The numerical method was investigated for drawing the dispersion and displacement curves of ultrasonic Lamb wave propagated in Aluminum plate. An experimental study was carried out to check the theoretical prediction. The detection of unsticking between the skin and the core was tested by the two first modes for a low frequency. It was found that A0 mode is more sensitive to delamination defect compared to S0 mode.
Abstract: In this paper, the optimum weight and cost of a laminated composite plate is seeked, while it undergoes the heaviest load prior to a complete failure. Various failure criteria are defined for such structures in the literature. In this work, the Tsai-Hill theory is used as the failure criterion. The theory of analysis was based on the Classical Lamination Theory (CLT). A newly type of Genetic Algorithm (GA) as an optimization technique with a direct use of real variables was employed. Yet, since the optimization via GAs is a long process, and the major time is consumed through the analysis, Radial Basis Function Neural Networks (RBFNN) was employed in predicting the output from the analysis. Thus, the process of optimization will be carried out through a hybrid neuro-GA environment, and the procedure will be carried out until a predicted optimum solution is achieved.
Abstract: This paper describes the design and modeling
procedure of a novel 5-phase segment type switched reluctance motor
(ST-SRM) under simultaneous two-phase (bipolar) excitation of
windings. The rotor cores of ST-SRM are embedded in an aluminum
block as well as to improve the performance characteristics. The
magnetic circuit of the produced ST-SRM is constructed so that the
magnetic flux paths are short and exclusive to each phase, thereby
minimizing the commutation switching and eddy current losses in the
laminations. The design and simulation principles presented apply
primarily to conventional SRM and ST-SRM. It is proved that the
novel 5-phase switched reluctance motor under two-phase excitation
is superior among the criteria used in comparison. The purposed
model is particularly well suited for high torque and weight
constrained applications such as automobiles, aerospace and military
applications.
Abstract: In this paper, the optimum weight and cost of a laminated composite plate is seeked, while it undergoes the heaviest load prior to a complete failure. Various failure criteria are defined for such structures in the literature. In this work, the Tsai-Hill theory is used as the failure criterion. The theory of analysis was based on the Classical Lamination Theory (CLT). A newly type of Genetic Algorithm (GA) as an optimization technique with a direct use of real variables was employed. Yet, since the optimization via GAs is a long process, and the major time is consumed through the analysis, Radial Basis Function Neural Networks (RBFNN) was employed in predicting the output from the analysis. Thus, the process of optimization will be carried out through a hybrid neuro-GA environment, and the procedure will be carried out until a predicted optimum solution is achieved.
Abstract: In this paper delamination phenomenon in
Carbon-Epoxy laminated composite material is investigated
numerically. Arcan apparatus and specimen is modeled in ABAQUS
finite element software for different loading conditions and crack
geometries. The influence of variation of crack geometry on
interlaminar fracture stress intensity factor and energy release rate for
various mixed mode ratios and pure mode I and II was studied. Also,
correction factors for this specimen for different crack length ratios
were calculated. The finite element results indicate that for loading
angles close to pure mode-II loading, a high ratio of mode-II to
mode-I fracture is dominant and there is an opposite trend for loading
angles close to pure mode-I loading. It confirms that by varying the
loading angle of Arcan specimen pure mode-I, pure mode-II and a
wide range of mixed-mode loading conditions can be created and
tested. Also, numerical results confirm that the increase of the mode-
II loading contribution leads to an increase of fracture resistance in
the CF/PEI composite (i.e., a reduction in the total strain energy
release rate) and the increase of the crack length leads to a reduction
of interlaminar fracture resistance in the CF/PEI composite (i.e., an
increase in the total interlaminar strain energy release rate).