Abstract: The changes of the optical and structural properties of
Bismuth-Boro-Tellurite glasses pre and post gamma irradiation were
studied. Six glass samples, with different composition [(TeO2)0.7
(B2O3)0.3]1-x (Bi2O3)x prepared by melt quenching method were
irradiated with 25kGy gamma radiation at room temperature. The
Fourier Transform Infrared Spectroscopy (FTIR) was used to explore
the structural bonding in the prepared glass samples due to exposure,
while UV-VIS Spectrophotometer was used to evaluate the changes
in the optical properties before and after irradiation. Gamma
irradiation causes profound changes in the peak intensity as shown by
FTIR spectra which is due to the breaking of the network bonding.
Before gamma irradiation, the optical band gap, Eg value decreased
from 2.44 eV to 2.15 eV with the addition of Bismuth content. The
value kept decreasing (from 2.18 eV to 2.00 eV) following exposure
to gamma radiation due to the increase of non-bridging oxygen
(NBO) and the increase of defect in the glass. In conclusion, the glass
with high content of Bi2O3 (0.30Bi) give smallest Eg and show less
changes in FTIR spectra after gamma irradiation which indicate that
this glass is more resistant to gamma radiation compared to other
glasses.
Abstract: The atmospheres in many cities along the coastal lines
in the world have been rapidly changed to coastal-industrial
atmosphere. Hence, it is vital to investigate the corrosion behavior of
steel exposed to this kind of environment. In this present study,
Electrochemical Impedance Spectrography (EIS) and film thickness
measurement were applied to monitor the corrosion behavior of
weathering steel covered with a thin layer of the electrolyte in a
wet-dry cyclic condition, simulating a coastal-industrial environment
at 25oC and 60% RH. The results indicate that in all cycles, the
corrosion rate increases during the drying process due to an increase in
anion concentration and an acceleration of oxygen diffusion enhanced
by the effect of the thinning out of the electrolyte. During the wet-dry
cyclic corrosion test, the long-term corrosion behavior of this steel
depends on the periods of exposure. Corrosion process is first
accelerated and then decelerated. The decelerating corrosion process is
contributed to the formation of the protective rust, favored by the
wet-dry cycle and the acid regeneration process during the rusting
process.
Abstract: The use of engineered nanomaterials has increased as
a result of their positive impact on many sectors of the economy,
including agriculture. Silver nanoparticles (AgNPs) are now used to
enhance seed germination, plant growth, and photosynthetic quantum
efficiency and as antimicrobial agents to control plant diseases. In
this study, we examined the effect of AgNP dosage on the seed
germination of three plant species: corn (Zea mays L.), watermelon
(Citrullus lanatus [Thunb.] Matsum. & Nakai) and zucchini
(Cucurbita pepo L.). This experiment was designed to study the
effect of AgNPs on germination percentage, germination rate, mean
germination time, root length and fresh and dry weight of seedlings
for the three species. Seven concentrations (0.05, 0.1, 0.5, 1, 1.5, 2
and 2.5 mg/ml) of AgNPs were examined at the seed germination
stage. The three species had different dose responses to AgNPs in
terms of germination parameters and the measured growth
characteristics. The germination rates of the three plants were
enhanced in response to AgNPs. Significant enhancement of the
germination percentage values was observed after treatment of the
watermelon and zucchini plants with AgNPs in comparison with
untreated seeds. AgNPs showed a toxic effect on corn root
elongation, whereas watermelon and zucchini seedling growth were
positively affected by certain concentrations of AgNPs. This study
showed that exposure to AgNPs caused both positive and negative
effects on plant growth and germination.
Abstract: Availability of different genetic tests after completion
of Human Genome Project increases the physicians’ responsibility to
keep themselves update on the potential implementation of these
genetic tests in their daily practice. However, due to numbers of
barriers, still many of physicians are not either aware of these tests or
are not willing to offer or refer their patients for genetic tests. This
study was conducted an anonymous, cross-sectional, mailed-based
survey to develop a primary data of Malaysian physicians’ level of
knowledge and perception of gene profiling. Questionnaire had 29
questions. Total scores on selected questions were used to assess the
level of knowledge. The highest possible score was 11. Descriptive
statistics, one way ANOVA and chi-squared test was used for
statistical analysis. Sixty three completed questionnaires were
returned by 27 general practitioners (GPs) and 36 medical specialists.
Responders’ age ranges from 24 to 55 years old (mean 30.2 ± 6.4).
About 40% of the participants rated themselves as having poor level
of knowledge in genetics in general whilst 60% believed that they
have fair level of knowledge; however, almost half (46%) of the
respondents felt that they were not knowledgeable about available
genetic tests. A majority (94%) of the responders were not aware of
any lab or company which is offering gene profiling services in
Malaysia. Only 4% of participants were aware of using gene profiling
for detection of dosage of some drugs. Respondents perceived greater
utility of gene profiling for breast cancer (38%) compared to the
colorectal familial cancer (3%). The score of knowledge ranged from
2 to 8 (mean 4.38 ± 1.67). Non- significant differences between score
of knowledge of GPs and specialists were observed, with score of
4.19 and 4.58 respectively. There was no significant association
between any demographic factors and level of knowledge. However,
those who graduated between years 2001 to 2005 had higher level of
knowledge. Overall, 83% of participants showed relatively high level
of perception on value of gene profiling to detect patient’s risk of
disease. However, low perception was observed for both statements
of using gene profiling for general population in order to alter their
lifestyle (25%) as well as having the full sequence of a patient
genome for the purpose of determining a patient’s best match for
treatment (18%). The lack of clinical guidelines, limited provider
knowledge and awareness, lack of time and resources to educate
patients, lack of evidence-based clinical information and cost of tests
were the most barriers of ordering gene profiling mentioned by
physicians. In conclusion Malaysian physicians who participate in
this study had mediocre level of knowledge and awareness in gene
profiling. The low exposure to the genetic questions and problems
might be a key predictor of lack of awareness and knowledge on
available genetic tests. Educational and training workshop might be useful in helping Malaysian physicians incorporate genetic profiling
into practice for eligible patients.
Abstract: The main objective of this paper is to provide a new
methodology for road safety assessment in Oman through the
development of suitable accident prediction models. GLM technique
with Poisson or NBR using SAS package was carried out to develop
these models. The paper utilized the accidents data of 31 un-signalized
T-intersections during three years. Five goodness-of-fit
measures were used to assess the overall quality of the developed
models. Two types of models were developed separately; the flow-based
models including only traffic exposure functions, and the full
models containing both exposure functions and other significant
geometry and traffic variables.
The results show that, traffic exposure functions produced much
better fit to the accident data. The most effective geometric variables
were major-road mean speed, minor-road 85th percentile speed,
major-road lane width, distance to the nearest junction, and right-turn
curb radius.
The developed models can be used for intersection treatment or
upgrading and specify the appropriate design parameters of T-intersections.
Finally, the models presented in this thesis reflect the intersection
conditions in Oman and could represent the typical conditions in
several countries in the middle east area, especially gulf countries.
Abstract: The number of persons with implanted cardiac
pacemakers (PM) has increased in Western countries. The aim of this
paper is to investigate the possible situations where persons with a
PM may be exposed to extremely low frequency (ELF) electric (EF)
and magnetic fields (MF) that may disturb their PM. Based on our
earlier studies, it is possible to find such high public exposure to EFs
only in some places near 400 kV power lines, where an EF may
disturb a PM in unipolar mode. Such EFs cannot be found near 110
kV power lines. Disturbing MFs can be found near welding
machines. However, we do not have measurement data from welding.
Based on literature and earlier studies at Tampere University of
Technology, it is difficult to find public EF or MF exposure that is
high enough to interfere with PMs.
Abstract: In this paper, the effects of fiber types and elevated
temperatures on compressive strength, modulus of rapture and the
bond characteristics of fiber reinforced concretes (FRC) are
presented. By using the three different types of fibers (steel fiber-SF,
polypropylene-PPF and polyvinyl alcohol-PVA), FRC specimens
were produced and exposed to elevated temperatures up to 800 ºC for
1.5 hours. In addition, a plain concrete (without fiber) was produced
and used as a control. Test results obtained showed that the steel fiber
reinforced concrete (SFRC) had the highest compressive strength,
modulus of rapture and bond stress values at room temperatures, the
residual bond, flexural and compressive strengths of both FRC and
plain concrete dropped sharply after exposure to high temperatures.
The results also indicated that the reduction of bond, flexural and
compressive strengths with increasing the exposed temperature was
relatively less for SFRC than for plain, and FRC with PPF and PVA.
Abstract: The textile industry plays a major role in the economy
of India and on the other side of the coin it is the major source for
water pollution. As azo dyes is the largest dye class they are
extensively used in many fields such as textile industry, leather
tanning industry, paper production, food, color photography,
pharmaceuticals and medicine, cosmetic, hair colorings, wood
staining, agricultural, biological and chemical research etc. In
addition to these, they can have acute and/or chronic effects on
organisms depending on their concentration and length of exposure
when they discharged as effluent in the environment. The aim of this
study was to assess the genotoxic and histotoxic potentials of
environmentally relevant concentrations of C. I. Reactive Red 120
(RR 120) on Catla catla, important edible freshwater fingerlings. For
this, healthy Catla catla fingerlings were procured from the
Government Fish Farm and acclimatized in 100 L capacity and
continuously aerated glass aquarium in laboratory for 15 days.
According to APHA some physic-chemical parameters were
measured and maintained such as temperature, pH, dissolve oxygen,
alkalinity, total hardness. Water along with excreta had been changed
every 24 hrs. All fingerlings were fed artificial food palates once a
day @ body weight. After 15 days fingerlings were grouped in 5 (10
in each) and exposed to various concentrations of RR 120 (Control,
10, 20, 30 and 40 mg.l-1) and samples (peripheral blood and gills,
kidney) were collected and analyzed at 96 hrs. All results were
compared with the control. Micronuclei (MN), nuclear buds (NB),
fragmented-apoptotic (FA) and bi-nucleated (BN) cells in blood
smears and in tissues (gills and kidney cells) were observed.
Prominent histopathological alterations were noticed in gills such as
aneurism, hyperplasia, degenerated central axis, lifting of gill
epithelium, curved secondary gill lamellae etc. Similarly kidney
showed some detrimental changes like shrunken glomeruli with
increased periglomerular space, degenerated renal tubules etc. Both
haematological and histopathological changes clearly reveal the toxic
potential of RR 120. This work concludes that water pollution
assessment can be done by these two biomarkers which provide
baseline to the further chromosomal or molecular work.
Abstract: Air-cooled Blast Furnace Slag Aggregate (BFSA) is
usually referred to as a material providing for unique properties of
concrete. On the other hand, negative influences are also presented in
many aspects. The freeze-thaw resistance of concrete is dependent on
many factors, including regional specifics and when a concrete mix is
specified it is still difficult to tell its exact freeze-thaw resistance due
to the different components affecting it. An important consideration
in working with BFSA is the granularity and whether slag is sorted or
not. The experimental part of the article represents a comparative
testing of concrete using both the sorted and unsorted BFSA through
the freeze-thaw resistance as an indicator of durability. Unsorted
BFSA is able to be successfully used for concretes as they are
specified for exposure class XF4 with providing that the type of
cement is precisely selected.
Abstract: Poly bag and mulch films for agricultural field caused
pose environmental problem due to the non-degradable plastics
wastes upon disposal. Thus, a degradable poly bag was designed with
hybrid sago starch (SS) and polyvinyl alcohol (PVA). Two Different
blended compositions of SS and PVA hybrid have been compounded.
Then, the hybrids blended are mixed with linear line density
polyethylene (LLDPE) resin to fabricate poly bag film through
conventional film blowing process. Samples of LLDPE, SS and PVA
hybrid film were exposed to UV light and soil burial. The weight
losses were determined during degradation process. Hybrid film by
degradation of starch was found to hydrolyze and hydroxyl groups
decrease on esterification upon exposure to soil burial and uv
radiation. It was found out that, the hybrid film for 60% of SS
composition showed greatest degradation in soil and UV radiation.
Abstract: In this study, the Compressive strength of concretes
made with Ground Granulated Blast furnace Slag (GGBS),
Pulverised Fuel Ash (PFA), Rice Husk Ash (RHA) and Waste Glass
Powder (WGP) after they were exposed 7800C (exposure duration of
around 60 minutes) and then allowed to cool down gradually in the
furnace for about 280 minutes at water binder ratio of 0.50 was
investigated. GGBS, PFA, RHA and WGP were used to replace up to
20% Portland cement in the control concrete. Test for the
determination of workability, compressive strength and tensile
splitting strength of the concretes were carried out and the results
were compared with control concrete. The test results showed that the
compressive strength decreased by an average of around 30% after
the concretes were exposed to the heating and cooling scenario.
Abstract: Concrete is found to undergo degradation when
subjected to elevated temperatures and loose substantial amount of its
strength. The loss of strength in concrete is mainly attributed to
decomposition of C-S-H and release of physically and chemically
bound water, which begins when the exposure temperature exceeds
100°C. When such a concrete comes in contact with moisture, the
cement paste is found rehydrate and considerable amount of strength
lost is found to recover. This paper presents results of an
experimental program carried out to investigate the effect of recuring
on strength gain of OPC concrete specimens subjected to elevated
temperatures from 200°C to 800°C, which were subjected to
retention time of two hours and four hours at the designated
temperature. Strength recoveries for concrete subjected to 7
designated elevated temperatures are compared. It is found that the
efficacy of recuring as a measure of strength recovery reduces with
increase in exposure temperature.
Abstract: Sound exposure effects have been investigated by
broadcasting a group of broilers with sound of Quran verses (Group
B) whereas the other group is the control broilers (Group C). The
growth rate comparisons in terms of weight and raw meat texture
measured by shear force have been investigated. Twenty-seven
broilers were randomly selected from each group on Day 24 and
weight measurement was carried out every week till the harvest day
(Day 39).Group B showed a higher mean weight on Day 24 (1.441 ±
0.013 kg) than Group C. Significant difference in the weight on Day
39 existed for Group B compared to Group C (p < 0.05). However,
there was no significant (p >0.05) difference of shear force in the
same muscles (breast and drumstick raw meat) of both groups but the
shear force of the breast meat for Group B and C broilers was lower
(p < 0.05) than that of their drumstick meat. Thus, broadcasting the
sound of Quran verses in the coop can be applied to improve the
growth rate of broilers for producing better quality poultry.
Abstract: For centuries humans have used the antimicrobial
properties of copper to their advantage. Yet, after all these years the
underlying mechanisms of copper mediated cell death in various
microbes remain unclear. We had explored the hypothesis that copper
mediated increased levels of lipid peroxidation in the membrane fatty
acids is responsible for increased killing in Escherichia coli. In this
study we show that in both gram positive (Staphylococcus aureus)
and gram negative (Pseudomonas aeruginosa) bacteria there is a
strong correlation between copper mediated cell death and increased
levels of lipid peroxidation. Interestingly, the non-spore forming
gram positive bacteria as well as gram negative bacteria show similar
patterns of cell death, increased levels of lipid peroxidation, as well
as genomic DNA degradation, however there is some difference in
loss in membrane integrity upon exposure to copper alloy surface.
Abstract: This study was developed to compare the behavior
and the ability of polymer foam composites towards sound absorption
test of Shorea leprosula wood (SL) of acid hydrolysis treatment with
particle size
Abstract: This work reports the potential of using Palm Kernel
(PK) ash and shell as a partial substitute for Portland Cement (PC)
and coarse aggregate in the development of mortar and concrete. PK
ash and shell are agro-waste materials from palm oil mills, the
disposal of PK ash and shell is an environmental problem of concern.
The PK ash has pozzolanic properties that enables it as a partial
replacement for cement and also plays an important role in the
strength and durability of concrete, its use in concrete will alleviate
the increasing challenges of scarcity and high cost of cement. In order
to investigate the PC replacement potential of PK ash, three types of
PK ash were produced at varying temperature (350-750C) and they
were used to replace up to 50% PC. The PK shell was used to replace
up to 100% coarse aggregate in order to study its aggregate
replacement potential. The testing programme included material
characterisation, the determination of compressive strength, tensile
splitting strength and chemical durability in aggressive sulfatebearing
exposure conditions. The 90 day compressive results showed
a significant strength gain (up to 26.2 N/mm2). The Portland cement
and conventional coarse aggregate has significantly higher influence
in the strength gain compared to the equivalent PK ash and PK shell.
The chemical durability results demonstrated that after a prolonged
period of exposure, significant strength losses in all the concretes
were observed. This phenomenon is explained, due to lower change
in concrete morphology and inhibition of reaction species and the
final disruption of the aggregate cement paste matrix.
Abstract: In this investigation, we have evaluated the effects of
arsenic trioxide on hepatic function in pregnant and lactating Swiss
albino mice and their suckling pups. Experiments were carried out on
female mice given 175 ppm As2O3 in their drinking water from the
14th day of pregnancy until day 14 after delivery. Our results showed
a significant decrease in plasma levels of total protein and albumin,
cholesterol and triglyceride in As2O3 treated mice and their pups. The
hyperbilirubinemia and the increased plasma total alkaline
phosphatase activity suggested the presence of cholestasis.
Transaminase activities as well as lactate deshydrogenase activity in
plasma, known as biomarkers of hepatocellular injury, were elevated
indicating hepatic cells’ damage after treatment with As2O3.
Exposure to arsenic led to an increase of liver thiobarbituric acid
reactive substances level along with a concomitant decrease in the
activities of superoxide dismutase, catalase and glutathione
peroxidase and in glutathione.
Abstract: Although, arsenic trioxide has been the subject of
toxicological research, in vitro cytotoxicity and genotoxicity studies
using relevant cell models and uniform methodology are not well
elucidated. Hence, the aim of the present study was to evaluate the
cytotoxicity and genotoxicity induced by arsenic trioxide in human
keratinocytes (HaCaT) using the MTT [3-(4, 5-dimethylthiazol-2-yl)-
2,5-diphenyltetrazolium bromide] and alkaline single cell gel
electrophoresis (Comet) assays, respectively. Human keratinocytes
were treated with different doses of arsenic trioxide for 4 h prior to
cytogenetic assessment. Data obtained from the MTT assay indicated
that arsenic trioxide significantly reduced the viability of HaCaT cells
in a dose-dependent manner, showing an IC50 value of 34.18 ± 0.6
μM. Data generated from the comet assay also indicated a significant
dose-dependent increase in DNA damage in HaCaT cells associated
with arsenic trioxide exposure. We observed a significant increase in
comet tail length and tail moment, showing an evidence of arsenic
trioxide -induced genotoxic damage in HaCaT cells. This study
confirms that the comet assay is a sensitive and effective method to
detect DNA damage caused by arsenic.
Abstract: Early detection of breast cancer saves many thousands
of lives each year via application of mammography and genetic
screening and many more lives could be saved if nurses are involved
in breast care screening practices. So, the aim of the study was to
identify nurse's role in early detection of breast cancer through
mammography and genetic screening and its impact on patient's
outcome. In order to achieve this aim, 400 women above 40 years,
asymptomatic were recruited for mammography and genetic
screening. In addition, 50 nurses and 6 technologists were involved in
the study. A descriptive analytical design was used. Five tools were
utilized: sociodemographic, mammographic examination and risk
factors, women's before, during and after mammography, items
relaying to technologists, and items related to nurses were also
obtained. The study finding revealed that 3% of women detected for
malignancy and 7.25% for fibroadenoma. Statistically significant
differences were found between mammography results and age,
family history, genetic screening, exposure to smoke, and using
contraceptive pills. Nurses have insufficient knowledge about
screening tests. Based on these findings the present study
recommended involvement of nurses in breast care which is very
important to in force population about screening practices.
Abstract: Lead being a toxic heavy metal that mankind is
exposed to the highest levels of this metal from environmental
pollutants. A total of 180 Male scalp hair samples were collected
from different environments in Greater Cairo (GC), i.e. industrial,
heavy traffic and rural areas (60 samples from each) having different
activities during the period of, 1/5/2010 to 1/11/2012. Hair samples
were collected during five stages. Data proved that the concentration
of lead in male industrial areas of Cairo ranged between 6.2847 to
19.0432 μg/g, with mean value of 12.3288 μg/g. On the other hand,
lead content of hair samples of residential-traffic areas ranged
between 2.8634 to 16.3311 μg/g with mean value of 9.7552 μg/g.
While lead concentration on the hair of the male residents living in
rural area ranged between 1.0499-9.0402μg/g with mean value of
4.7327 μg/g. The Pb concentration in scalp hair of Cairo residents of
residential-traffic and rural traffic areas was observed to follow the
same pattern. The pattern was that of decrease concentration of
summer and its increase in winter. Then, there was a marked increase
in Pb concentration of summer 2012, and this increase was
significant. These were obviously seen for the residential-traffic and
rural areas residents. Pb pollution in residents of industrial areas
showed the same seasonal pattern, but there was marked to decrease
in Pb concentration of summer 2012, and this decrease was
significant. Lead pollution in residents of GC was serious. It is worth
noting that the atmosphere is still contaminated by lead despite a
decade of using unleaded gasoline. Strong seasonal variation in
higher Pb concentration on winter than in summer was found. Major
contributions to the pollution with Pb could include industry
emissions, motor vehicle emissions and long transported dust from
outside Cairo. More attention should be paid to the reduction of Pb
content of the urban aerosol and to the Pb pollution health.