Abstract: Ductile iron samples alloyed with 2.5% Si, 0.78% Cu, 0.421% Mo and 0.151% Ni were austempered at 345 °C and 380 °C for 150 and 180 mins and then tested for wear strength. Ductile iron was also included in the study for comparison purposes. A pin-on-disc machine was employed for wear study. The investigations were carried out for a speed of 3 m/s, under the contact load of 29.43 N with varying sliding distances ranging from 1000 m to 5000 m. The experimental outcome indicates that ADI austempered at 345 °C is more wear resistant than the one austempered at 380 °C. Also for only a sliding distance of 3000 m, both exhibited almost same wear resistance. SEM analysis indicates running sliding marks more or less parallel to one another. Spalled layers and large voids which resemble delamination were observed on worn surface of ADI380. This indicated the occurrence of severe wear. Dark patches observed indicate oxidized surface.
Abstract: The sintering step in powder metallurgy (P/M) processes is very sensitive as it determines to a large extent the properties of the final component produced. Spark plasma sintering over the past decade has been extensively used in consolidating a wide range of materials including metallic alloy powders. This novel, non-conventional sintering method has proven to be advantageous offering full densification of materials, high heating rates, low sintering temperatures, and short sintering cycles over conventional sintering methods. Ti6Al4V has been adjudged the most widely used α+β alloy due to its impressive mechanical performance in service environments, especially in the aerospace and automobile industries being a light metal alloy with the capacity for fuel efficiency needed in these industries. The P/M route has been a promising method for the fabrication of parts made from Ti6Al4V alloy due to its cost and material loss reductions and the ability to produce near net and intricate shapes. However, the use of this alloy has been largely limited owing to its relatively poor hardness and wear properties. The effect of sintering temperature on the densification, hardness, and wear behaviors of spark plasma sintered Ti6Al4V powders was investigated in this present study. Sintering of the alloy powders was performed in the 650–850°C temperature range at a constant heating rate, applied pressure and holding time of 100°C/min, 50 MPa and 5 min, respectively. Density measurements were carried out according to Archimedes’ principle and microhardness tests were performed on sectioned as-polished surfaces at a load of 100gf and dwell time of 15 s. Dry sliding wear tests were performed at varied sliding loads of 5, 15, 25 and 35 N using the ball-on-disc tribometer configuration with WC as the counterface material. Microstructural characterization of the sintered samples and wear tracks were carried out using SEM and EDX techniques. The density and hardness characteristics of sintered samples increased with increasing sintering temperature. Near full densification (99.6% of the theoretical density) and Vickers’ micro-indentation hardness of 360 HV were attained at 850°C. The coefficient of friction (COF) and wear depth improved significantly with increased sintering temperature under all the loading conditions examined, except at 25 N indicating better mechanical properties at high sintering temperatures. Worn surface analyses showed the wear mechanism was a synergy of adhesive and abrasive wears, although the former was prevalent.
Abstract: Al6061 alloy base matrix, reinforced with particles of
silicon carbide (10 wt %) and Graphite powder (1wt%), known as
hybrid composites have been fabricated by liquid metallurgy route
(stir casting technique) and optimized at different parameters like
applied load, sliding speed and sliding distance by taguchi method. A
plan of experiment generated through taguchi technique was used to
perform experiments based on L27 orthogonal array. The developed
ANOVA and regression equations are used to find the optimum
coefficient of friction and wear under the influence of applied load,
sliding speed and sliding distance. On the basis of “smaller the best”
the dry sliding wear resistance was analysed and finally confirmation
tests were carried out to verify the experimental results.
Abstract: Composite pins of rubber dust collected from tyre
retreading centres of trucks, cars and buses etc.and epoxy with
weight percentages of 10. 15, and 20 % of rubber (weight fractions of
9, 13 and 17 % respectively) have been prepared in house with the
help of a split wooden mould. The pins were tested in a pin-on-disc
wear monitor to determine the co-efficient of friction and weight
losses with varying speeds, loads and time. The wear volume and
wear rates have also been found out for all these three specimens.. It
is observed that all the specimens have exhibited very low coefficient
of friction and low wear rates under dry sliding condition. Out of the
above three samples tested, the specimen with 10 % rubber dust by
weight has shown lowest wear rates. However a peculiar result i.e
decreasing trend has been obtained with 20% reinforcement of rubber
in epoxy while rubbed against steel at varying speeds. This might
have occurred due to high surface finish of the disc and formation of
a thin transfer layer from the composite