Abstract: This in vitro study focused on investigating the fatigue resistance of veneered zirconia molar crowns with different veneering ceramic thicknesses, simulating the relative wear depths under simulated cyclic loading. A mandibular first molar was prepared and then scanned using computer-aided design/computer-aided manufacturing (CAD/CAM) technology to fabricate 32 zirconia copings of uniform 0.5 mm thickness. The manufactured copings then veneered with 1.5 mm, 1.0 mm, 0.5 mm, and 0.0 mm representing 0%, 33%, 66%, and 100% relative wear of a normal ceramic thickness of 1.5 mm. All samples were thermally aged to 6000 thermo-cycles for 2 minutes with distilled water between 5 ˚C and 55 ˚C. The samples subjected to cyclic fatigue and fracture testing using SD Mechatronik chewing simulator. These samples are loaded up to 1.25x10⁶ cycles or until they fail. During fatigue, testing, extensive cracks were observed in samples with 0.5 mm veneering layer thickness. Veneering layer thickness 1.5-mm group and 1.0-mm group were not different in terms of resisting loads necessary to cause an initial crack or final failure. All ceramic zirconia-based crown restorations with varying occlusal veneering layer thicknesses appeared to be fatigue resistant. Fracture load measurement for all tested groups before and after fatigue loading exceeded the clinical chewing forces in the posterior region. In general, the fracture loads increased after fatigue loading and with the increase in the thickness of the occlusal layering ceramic.
Abstract: Two Lithium Disilicate (LD) glass ceramics based on
SiO2-Li2O-K2O-Al2O3 system were prepared through a glass melting
method. The glass rods were then fabricated into dental crowns via a
hot pressing at 900˚C and 850˚C in order to study the effect of the
pressing temperatures on the phase formation and microstructure of
the glasses. Different samples of as cast glass and heat treated
samples (600˚C and 700˚C) were used to press for investigating the
effect of an initial microstructure on the hot pressing technique. Xray
diffraction (XRD) and scanning electron microscopy (SEM) were
performed to determine the phase formation and microstructure of the
samples, respectively. XRD results show that the main crystalline
structure was Li2Si2O5 by having Li3PO4, Li0.6Al0.6Si2O6, Li2SiO3,
Ca5 (PO4)3F and SiO2 as minor phases. Glass compositions with
different heat treatment temperatures exhibited a difference phase
formations but have less effect during pressing. SEM micrographs
showed the microstructure of Li2Si2O5 as lath-like shape in all
glasses. With increasing the initial heat treatment temperature, the
longer the lath-like crystals of lithium disilicate were increased
especially when using glass heat treatment at 700˚C followed by
pressing at 900˚C. This could be suggested that LD1 heat treatment at
700˚C which pressing at 900˚C presented the best formation by the
hot pressing and compiled microstructure.
Abstract: The introduction of mass-customization has enabled
new ways to treat patients within medicine. However, the
introduction of industrialized treatments has also meant new
obstacles. The purpose of this study was to introduce and
theoretically test a method for improving dental crown fit. The
optimization method allocates support points in order to check the
final variation for dental crowns. Three different types of geometries
were tested and compared. The three geometries were also divided
into three sub-geometries: Current method, Optimized method and
Feasible method. The Optimized method, using the whole surface for
support points, provided the best results. The results support the
objective of the study. It also seems that the support optimization
method can dramatically improve the robustness of dental crown
treatments.