Abstract: Sand cast samples of the as-received 66/34Mg-Al alloy were first homogenized at 4900C and then divided into three groups on which annealing, normalising and artificial ageing were respectively carried out. Thermal ageing of the samples involved treatment at 5000C, soaked for 4 hours and quenched in water at ambient temperature followed by tempering at 2000C for 2 hours. Test specimens were subjected to microstructure and mechanical analyses and the results compared. Precipitation of significant volume of stable Mg17Al12 crystals in the aged specimen’s matrix conferred superior mechanical characteristics compared with the annealed, normalized and as-cast specimens. The ultimate tensile strength was 93.4MPa with micro-hardness of 64.9HRC and impact energy (toughness) of 4.05J. In particular, its Young modulus was 10.4GPa which compared well with that of cortical (trabecule) bone’s modulus that varies from 12-17GPa.
Abstract: Heavy metals have bad effects on environment and
soils and it can uptake by natural HAP .natural Hap is an inexpensive
material that uptake large amounts of various heavy metals like Zn
(II) .Natural HAP (N-HAP), extracted from bovine cortical bone ash,
is a good choice for substitution of commercial HAP. Several
experiments were done to investigate the sorption capacity of Zn (II)
to N-HAP in various particles sizes, temperatures, initial
concentrations, pH and reaction times. In this study, the sorption of
Zinc ions from a Zn solution onto HAP particles with sizes of 1537.6
nm and 47.6 nm at three initial pH values of 4.50, 6.00 and 7.50 was
studied. The results showed that better performance was obtained
through a 47.6 nm particle size and higher pH values. The
experimental data were analyzed using Langmuir, Freundlich, and
Arrhenius equations for equilibrium, kinetic and thermodynamic
studies. The analysis showed a maximum adsorption capacity of NHAP
as being 1.562 mmol/g at a pH of 7.5 and small particle size.
Kinetically, the prepared N-HAP is a feasible sorbent that retains Zn
(II) ions through a favorable and spontaneous sorption process.
Abstract: Bone material is treated as heterogeneous and hierarchical in nature therefore appropriate size of bone specimen is required to analyze its tensile properties at a particular hierarchical level. Tensile properties of cortical bone are important to investigate the effect of drug treatment, disease and aging as well as for development of computational and analytical models. In the present study tensile properties of buffalo as well as goat femoral and tibiae cortical bone are analyzed using sub-size tensile specimens. Femoral cortical bone was found to be stronger in tension as compared to the tibiae cortical bone and the tensile properties obtained using sub-size specimens show close resemblance with the tensile properties of full-size cortical specimens. A two dimensional finite element (FE) modal was also applied to simulate the tensile behavior of sub-size specimens. Good agreement between experimental and FE model was obtained for sub-size tensile specimens of cortical bone.