Abstract: Corrosion behaviour of hypereutectic Al-19Si automotive alloy in different pH=1, 3, 5, 7, 9, 11, and 13 environments was carried out using conventional gravimetric measurements and was complemented by resistivity, optical micrograph, scanning electron microscopy (SEM) and X-ray analyzer (EDX) investigations. Gravimetric analysis confirmed that the highest corrosion rate is shown at pH 13 followed by pH 1. Minimum corrosion occurs in the pH range of 3.0 to 11 due to establishment of passive layer on the surface. The highest corrosion rate at pH 13 is due to the presence of sodium hydroxide in the solution which dissolves the surface oxide film at a steady rate. At pH 1, it can be attributed that the presence of aggressive chloride ions serves to pick up the damage of the passive films at localized regions. With varying exposure periods by both, the environment complies with the normal corrosion rate profile that is an initial steep rise followed by a nearly constant value of corrosion rate. Resistivity increases in case of pH 1 solution for the higher pit formation and decreases at pH 13 due to formation of thin film. The SEM image of corroded samples immersed in pH 1 solution clearly shows pores on the surface and in pH 13 solution, and the corrosion layer seems more compact and homogenous and not porous.
Abstract: This paper aims to study the corrosion property of aluminum matrix nanocomposite of an aluminum alloy (Al-6061) reinforced with zirconium dioxide (ZrO2) particles. The zirconium dioxide particles are synthesized by solution combustion method. The nanocomposite materials are prepared by mechanical stir casting method, varying the percentage of n-ZrO2 (2.5%, 5% and 7.5% by weight). The corrosion behavior of base metal (Al-6061) and Al/ZrO2 nanocomposite in seawater (3.5% NaCl solution) is measured using the potential control method. The corrosion rate is evaluated by Tafel extrapolation technique. The corrosion potential increases with the increase in wt.% of n-ZrO2 in the nanocomposite which means the decrease in corrosion rate. It is found that on addition of n-ZrO2 particles to the aluminum matrix, the corrosion rate has decreased compared to the base metal.
Abstract: Corrosion of concrete sewer pipes induced by
sulphuric acid attack is a recognised problem worldwide, which is not
only an attribute of countries with hot climate conditions as thought
before. The significance of this problem is by far only realised when
the pipe collapses causing surface flooding and other severe
consequences. To change the existing post-reactive attitude of
managing companies, easy to use and robust models are required to
be developed which currently lack reliable data to be correctly
calibrated. This paper focuses on laboratory experiments of
establishing concrete pipe corrosion rate by submerging samples in to
0.5pH sulphuric acid solution for 56 days under 10ºC, 20ºC and 30ºC
temperature regimes. The result showed that at very early stage of the
corrosion process the samples gained overall mass, at 30ºC the
corrosion progressed quicker than for other temperature regimes,
however with time the corrosion level for 10ºC and 20ºC regimes
tended towards those at 30ºC. Overall, at these conditions the
corrosion rates of 10 mm/year, 13,5 mm/year and 17 mm/year were
observed.
Abstract: Schiff base (E)-2-methyl-N-(tetrazolo[1,5-a]quinolin-4-ylmethylene)aniline (QMA) was synthesized, and its inhibitive effect for mild steel in 1N HCl solution was investigated by weight loss measurement and electrochemical tests. From the weight loss measurements and electrochemical tests, it was observed that the inhibition efficiency increases with the increase in the Schiff base concentration and reaches a maximum at the optimum concentration. This is further confirmed by the decrease in corrosion rate. It is found that the system follows Langmuir adsorption isotherm.
Abstract: Study on corrosion propensity of welded mild steel- bar in soil media around the coastal area of University of Lagos has been carried out using gravimetric method. Six (6) samples each for welded and unwelded mild steels were cut, their initial weights were recorded and buried in two selected soil. The weight losses of these coupons were measured at regular intervals for a period of six months (180 days).
The corrosiveness of the soil media varied widely depending on the potency level of its constituents. The results revealed that soil in the studied area have marked variations in composition and contents. Soil medium with a lower pH and higher chloride ion concentration aggressively attacked the coupons with the welded steel coupon corroding faster than unwelded one. The medium resistivity to the flow of current is another strong factor affecting corrosion rate.
Abstract: There was a high rate of corrosion in Pyrolysis
Gasoline Hydrogenation (PGH) unit of Arak Petrochemical Company
(ARPC), and it caused some operational problem in this plant. A
commercial chemical had been used as anti-corrosion in the
depentanizer column overhead in order to control the corrosion rate.
Injection of commercial corrosion inhibitor caused some
operational problems such as fouling in some heat exchangers. It was
proposed to replace this commercial material with another more
effective trouble free, and well-known additive by R&D and
operation specialists.
At first, the system was simulated by commercial simulation
software in electrolytic system to specify low pH points inside the
plant. After a very comprehensive study of the situation and technical
investigations ,ammonia / monoethanol amine solution was proposed
as neutralizer or corrosion inhibitor to be injected in a suitable point
of the plant. For this purpose, the depentanizer column and its
accessories system was simulated again in case of this solution
injection.
According to the simulation results, injection of new anticorrosion
substance has no any side effect on C5 cut product and
operating conditions of the column. The corrosion rate will be
cotrolled, if the pH remains at the range of 6.5 to 8 . Aactual plant
test run was also carried out by injection of ammonia / monoethanol
amine solution at the rate of 0.6 Kg/hr and the results of iron content
of water samples and corrosion test coupons confirmed the
simulation results.
Now, ammonia / monoethanol amine solution is injected to a
suitable pint inside the plant and corrosion rate has decreased
significantly.