Abstract: Well-defined 2D Eu+3 co-doped ZrO2: Gd+3 nanoparticles were successfully synthesized by microwave assisted solution combustion technique for luminescent applications. The present investigation reports the rapid and effective method for the synthesis of the Eu+3 co-doped ZrO2:Gd+3 nanoparticles and study of the luminescence behavior of Eu+3 ion in ZrO2:Gd+3 nanostructures. The optical properties of the prepared nanostructures were investigated by using UV-visible spectroscopy and photoluminescence spectra. The phase formation and the morphology of the nanoplatelets were studied by XRD, FESEM and HRTEM. The average grain size was found to be 45-50 nm. The presence of Gd3+ ion increases the crystallinity of the material and hence acts as a good nucleating agent. The ZrO2:Gd3+ co-doped with Eu+3 nanoplatelets gives an emission at 607 nm, a strong red emission under the excitation wavelength of 255 nm.
Abstract: This paper aims to study the corrosion property of aluminum matrix nanocomposite of an aluminum alloy (Al-6061) reinforced with zirconium dioxide (ZrO2) particles. The zirconium dioxide particles are synthesized by solution combustion method. The nanocomposite materials are prepared by mechanical stir casting method, varying the percentage of n-ZrO2 (2.5%, 5% and 7.5% by weight). The corrosion behavior of base metal (Al-6061) and Al/ZrO2 nanocomposite in seawater (3.5% NaCl solution) is measured using the potential control method. The corrosion rate is evaluated by Tafel extrapolation technique. The corrosion potential increases with the increase in wt.% of n-ZrO2 in the nanocomposite which means the decrease in corrosion rate. It is found that on addition of n-ZrO2 particles to the aluminum matrix, the corrosion rate has decreased compared to the base metal.
Abstract: In this work, obtaining methods of ultrafine alumina
powdery composites and high temperature pressing technology of
matrix ceramic composites with different compositions have been
discussed. Alumina was obtained by solution combustion synthesis
and sol-gel methods. Metal carbides containing powdery composites
were obtained by homogenization of finishing powders in nanomills,
as well as by their single-step high temperature synthesis .Different
types of matrix ceramics composites (α-Al2O3-ZrO2-Y2O3, α-Al2O3-
Y2O3-MgO, α-Al2O3-SiC-Y2O3, α-Al2O3-WC-Co-Y2O3, α-Al2O3-
B4C-Y2O3, α-Al2O3- B4C-TiB2 etc.) were obtained by using OXYGON
furnace. Consolidation of powders were carried out at 1550-
1750°C (hold time - 1 h, pressure - 50 MPa). Corundum ceramics
samples have been obtained and characterized by high hardness and
fracture toughness, absence of open porosity, high corrosion
resistance. Their density reaches 99.5-99.6% TD. During the work,
the following devices have been used: High temperature vacuum
furnace OXY-GON Industries Inc (USA), Electronic Scanning
Microscopes Nikon Eclipse LV 150, Optical Microscope NMM-
800TRF, Planetary mill Pulverisette 7 premium line, Shimadzu
Dynamic Ultra Micro Hardness Tester DUH-211S, Analysette 12
Dynasizer.
Abstract: Ni-based catalysts with different amounts of Na as
promoter from 2 to 6 wt % were prepared by solution combustion
method. The catalytic activity was investigated in syngas methanation
reaction. Carbon oxides conversion and methane selectivity are greatly
influenced by sodium loading. Adding 2 wt% Na remarkably improves
catalytic activity and long-term stability, attributed to its smaller mean
NiO particle size, better distribution, and milder metal-support
interaction. However, excess addition of Na results in deactivation
distinctly due to the blockage of active sites.