Abstract: The rapid depletion of high-grade iron ore (Fe2O3) has gained attention on the use of other sources of iron ore. Titaniferous magnetite ore (TMO) is a special type of magnetite ore having high titania content (23.23% TiO2 present in this case). Due to high TiO2 content and high density, TMO cannot be treated by the conventional smelting reduction. In this present work, the TMO has been collected from high-grade metamorphic terrain of the Precambrian Chotanagpur gneissic complex situated in the eastern part of India (Shaltora area, Bankura district, West Bengal) and the hematite ore has been collected from Visakhapatnam Steel Plant (VSP), Visakhapatnam. At VSP, iron ore is received from Bailadila mines, Chattisgarh of M/s. National Mineral Development Corporation. The preliminary characterization of TMO and hematite ore (HMO) has been investigated by WDXRF, XRD and FESEM analyses. Similarly, good quality of coal (mainly coking coal) is also getting depleted fast. The basic purpose of this work is to find how lean grade coal can be utilised along with TMO for smelting to produce pig iron. Lean grade coal has been characterised by using TG/DTA, proximate and ultimate analyses. The boiler grade coal has been found to contain 28.08% of fixed carbon and 28.31% of volatile matter. TMO fines (below 75 μm) and HMO fines (below 75 μm) have been separately agglomerated with lean grade coal fines (below 75 μm) in the form of briquettes using binders like bentonite and molasses. These green briquettes are dried first in oven at 423 K for 30 min and then reduced isothermally in tube furnace over the temperature range of 1323 K, 1373 K and 1423 K for 30 min & 60 min. After reduction, the reduced briquettes are characterized by XRD and FESEM analyses. The best reduced TMO and HMO samples are taken and blended in three different weight percentage ratios of 1:4, 1:8 and 1:12 of TMO:HMO. The chemical analysis of three blended samples is carried out and degree of metallisation of iron is found to contain 89.38%, 92.12% and 93.12%, respectively. These three blended samples are briquetted using binder like bentonite and lime. Thereafter these blended briquettes are separately smelted in raising hearth furnace at 1773 K for 30 min. The pig iron formed is characterized using XRD, microscopic analysis. It can be concluded that 90% yield of pig iron can be achieved when the blend ratio of TMO:HMO is 1:4.5. This means for 90% yield, the maximum TMO that could be used in the blend is about 18%.
Abstract: The fuel potential of six tropical hardwood species
namely: Triplochiton scleroxylon, Ceiba pentandra, Aningeria
robusta, Terminalia superba, Celtis mildbreadii and Piptadenia
africana were studied. Properties studied included species density,
gross calorific value, volatile matter, ash content, organic carbon and
elemental composition. Fuel properties were determined using
standard laboratory methods. The result indicates that the gross
calorific value (GCV) of the species ranged from 20.16 to 22.22
MJ/kg and they slightly varied from each other. Additionally, the
GCV of the biomass materials were higher than that of other biomass
materials like; wheat straw, rice straw, maize straw and sugar cane.
The ash and volatile matter content varied from 0.6075 to 5.0407%,
and 75.23% to 83.70% respectively. The overall rating of the
properties of the six biomass materials suggested that Piptadenia
africana has the best fuel property to be used as briquettes and
Aningeria robusta the worse. This study therefore suggests that a
holistic assessment of a biomass material needs to be done before
selecting it for fuel purpose.