Abstract: In this study the mixed mode fracture mechanics
parameters were investigated for high tensile steel butt welded joint
based on modified Arcan test and finite element analysis was used to
evaluate the effect of crack length on fracture criterion. The nondimensional
stress intensity factors, strain energy release rates and Jintegral
energy on crack tip were obtained for various in-plane
loading combinations on Arcan specimen starting from pure mode-I
to pure mode-II loading conditions. The specimen and apparatus were
modeled by finite element method and analyzed under various
loading angles (between 0 to 90 degrees with 15 degree interval) to
simulate the pure mode-I, II and mixed mode fracture. Since the
analytical results are independent from elasticity modules for
isotropic materials, therefore the results in elastic fields can be used
for Arcan specimens. The main objective of this study was to
evaluate the geometric calibration factors for modified Arcan test
specimen in order to obtain fracture toughness under mixed mode
loading conditions.
Abstract: In the crack growth analysis, the Stress Intensity
Factor (SIF) is a fundamental prerequisite. In the present study, the
mode I stress intensity factor (SIF) of three-dimensional penny-
Shaped crack is obtained in an isotropic elastic cylindrical medium
with arbitrary dimensions under arbitrary loading at the top of the
cylinder, by the semi-analytical method based on the Rayleigh-Ritz
method. This method that is based on minimizing the potential
energy amount of the whole of the system, gives a very close results
to the previous studies. Defining the displacements (elastic fields) by
hypothetical functions in a defined coordinate system is the base of
this research. So for creating the singularity conditions at the tip of
the crack the appropriate terms should be found.
Abstract: In recent years, a new numerical method has been
developed, the extended finite element method (X-FEM). The
objective of this work is to exploit the (X-FEM) for the treatment of
the fracture mechanics problems on 3D geometries, where we
showed the ability of this method to simulate the fatigue crack
growth into two cases: edge and central crack. In the results we
compared the six first natural frequencies of mode shapes uncracking
with the cracking initiation in the structure, and showed the stress
intensity factor (SIF) evolution function as crack size propagation
into structure, the analytical validation of (SIF) is presented. For to
evidence the aspects of this method, all result is compared between
FEA and X-FEM.
Abstract: In pressure vessels contain hydrogen, the role of
hydrogen will be important because of hydrogen cracking problem. It
is difficult to predict what is happened in metallurgical field spite of a
lot of studies have been searched. The main role in controlling the
mass diffusion as driving force is related to stress. In this study, finite
element analysis is implemented to estimate material-s behavior
associated with hydrogen embrittlement. For this purpose, one model
of a pressure vessel is introduced that it has definite boundary and
initial conditions. In fact, finite element is employed to solve the
sequentially coupled mass diffusion with stress near a crack front in a
pressure vessel. Modeling simulation intergrarnular fracture of AISI
4135 steel due to hydrogen is investigated. So, distribution of
hydrogen and stress are obtained and they indicate that their
maximum amounts occur near the crack front. This phenomenon is
happened exactly the region between elastic and plastic field.
Therefore, hydrogen is highly mobile and can diffuse through crystal
lattice so that this zone is potential to trap high volume of hydrogen.
Consequently, crack growth and fast fracture will be happened.
Abstract: Multi-site damage (MSD) has been a challenge to
aircraft, civil and power plant structures. In real life components are subjected to cracking at many vulnerable locations such as the bolt
holes. However, we do not consider for the presence of multiple cracks. Unlike components with a single crack, these components are
difficult to predict. When two cracks approach one another, their
stress fields influence each other and produce enhancing or shielding effect depending on the position of the cracks. In the present study,
numerical studies on fracture analysis have been conducted by using
the developed code based on the modified virtual crack closure integral (MVCCI) technique and finite element analysis (FEA) software ABAQUS for computing SIF of plates with multiple cracks.
Various parametric studies have been carried out and the results have
been compared with literature where ever available and also with the solution, obtained by using ABAQUS. By conducting extensive
numerical studies expressions for SIF have been obtained for collinear cracks and non-aligned cracks.
Abstract: The damage tolerance behavior of integrally and
conventional stiffened panel is investigated based on the fracture
mechanics and finite element analysis. The load bearing capability
and crack growth characteristic of both types of the stiffened panels
having same configuration subjected to distributed tensile load is
examined in this paper. A fourteen-stringer stiffened panel is
analyzed for a central skin crack propagating towards the adjacent
stringers. Stress intensity factors and fatigue crack propagation rates
of both types of the stiffened panels are then compared. The analysis
results show that integral stiffening causes higher stress intensity
factor than conventional stiffened panel as the crack tip passes
through the stringer and the integrally stiffened panel has less load
bearing capability than the riveted stiffened panel.
Abstract: Environment-assisted cracking (EAC) is one of the most serious causes of structural failure over a broad range of industrial applications including offshore structures. In EAC condition there is not a definite relation such as Paris equation in Linear Elastic Fracture Mechanics (LEFM). According to studying and searching a lot what the researchers said either a material has contact with hydrogen or any other corrosive environment, phenomenon of electrical and chemical reactions of material with its environment will be happened. In the literature, there are many different works to consider fatigue crack growing and solve it but they are experimental works. Thus, in this paper, authors have an aim to evaluate mathematically the pervious works in LEFM. Obviously, if an environment is more sour and corrosive, the changes of stress intensity factor is more and the calculation of stress intensity factor is difficult. A mathematical relation to deal with the stress intensity factor during the diffusion of sour environment especially hydrogen in a marine pipeline is presented. By using this relation having and some experimental relation an analytical formulation will be presented which enables the fatigue crack growth and critical crack length under cyclic loading to be predicted. In addition, we can calculate KSCC and stress intensity factor in the pipeline caused by EAC.