Abstract: The mesoporous MoO3/γ-Al2O3 catalyst was prepared
by incipient wetness impregnation method aiming to investigate the
effect of drying method and molybdenum content on the catalyst
property and performance towards the oxidation of benzothiophene
(BT), dibenzothiophene (DBT) and 4,6-dimethyle dibenzothiophene
(4,6-DMDBT) with H2O2 for deep oxidative desulfurization of diesel
fuel. The catalyst was characterized by XRD, BET, BJH and SEM
method. The catalyst with 10wt.% and 15wt.% Mo content represent
same optimum performance for DBT and 4,6-DMDBT removal, but
a catalyst with 10wt.% Mo has higher efficiency than 15wt.% Mo for
BT conversion. The SEM images show that use of rotary evaporator
in drying step reaches a more homogenous impregnation. The
oxidation reactivity of different sulfur compounds was studied which
followed the order of DBT>4,6-DMDBT>>BT.
Abstract: Titanium gels doped with water-soluble cationic porphyrin were synthesized by the sol–gel polymerization of Ti (OC4H9)4. In this work we investigate the spectroscopic properties along with SEM images of tetra carboxyl phenyl porphyrin when incorporated into porous matrix produced by the sol–gel technique.
Abstract: Highly ordered TiO2 nanotube (TNT) arrays were
fabricated onto a pre-treated titanium foil by anodic oxidation with a
voltage of 20V in phosphoric acid/sodium fluoride electrolyte. A pretreatment
of titanium foil involved washing with acetone,
isopropanol, ethanol and deionized water. Carbon doped TiO2
nanotubes (C-TNT) was fabricated 'in-situ' with the same method in
the presence of polyvinyl alcohol and urea as carbon sources. The
affects of polyvinyl alcohol concentration and oxidation time on the
composition, morphology and structure of the C-TN were studied by
FE-SEM, EDX and XRD techniques. FESEM images of the
nanotubes showed uniform arrays of C-TNTs. The density and
microstructures of the nanotubes were greatly affected by the content
of PVA. The introduction of the polyvinyl alcohol into the electrolyte
increases the amount of C content inside TiO2 nanotube arrays
uniformly. The influence of carbon content on the photo-current of
C-TNT was investigated and the I-V profiles of the nanotubes were
established. The preliminary results indicated that the 'in-situ'
doping technique produced a superior quality nanotubes compared to
post doping techniques.
Abstract: A composite made of plasma functionalized multiwall
carbon nanotubes (MWNTs) coated with SnO2 was synthesized by
sonochemical precipitation method. Thick layer of this
nanocomposite material was used as ethanol sensor at low
temperatures. The composite sensitivity for ethanol has increased by
a factor of 2 at room temperature and by a factor of 13 at 250°C in
comparison to that of pure SnO2. SEM image of nanocomposite
material showed MWNTs were embedded in SnO2 matrix and also a
higher surface area was observed in the presence of functionalized
MWNTs. Greatly improved sensitivity of the composite material to
ethanol can be attributed to new gas accessing passes through
MWNTs and higher specific surface area.