Abstract: Machining of Metal Matrix Composites (MMCs) is very significant process and has been a main problem that draws many researchers to investigate the characteristics of MMCs during different machining process. The poor machining properties of hard particles reinforced MMCs make drilling process a rather interesting task. Unlike drilling of conventional materials, many problems can be seriously encountered during drilling of MMCs, such as tool wear and cutting forces. Cutting tool wear is a very significant concern in industries. Cutting tool wear not only influences the quality of the drilled hole, but also affects the cutting tool life. Prediction the cutting tool life during drilling is essential for optimizing the cutting conditions. However, the relationship between tool life and cutting conditions, tool geometrical factors and workpiece material properties has not yet been established by any machining theory. In this research work, fuzzy subtractive clustering system has been used to model the cutting tool life in drilling of Al2O3 particle reinforced aluminum alloy composite to investigate of the effect of cutting conditions on cutting tool life. This investigation can help in controlling and optimizing of cutting conditions when the process parameters are adjusted. The built model for prediction the tool life is identified by using drill diameter, cutting speed, and cutting feed rate as input data. The validity of the model was confirmed by the examinations under various cutting conditions. Experimental results have shown the efficiency of the model to predict cutting tool life.
Abstract: Metal matrix composites (MMCs) attract considerable
attention as a result from its ability in providing a high strength, high
modulus, high toughness, high impact properties, improving wear
resistance and providing good corrosion resistance compared to
unreinforced alloy. Aluminium Silicon (Al/Si) alloy MMC has been
widely used in various industrial sectors such as in transportation,
domestic equipment, aerospace, military, construction, etc.
Aluminium silicon alloy is an MMC that had been reinforced with
aluminium nitrate (AlN) particle and become a new generation
material use in automotive and aerospace sector. The AlN is one of
the advance material that have a bright prospect in future since it has
features such as lightweight, high strength, high hardness and
stiffness quality. However, the high degree of ceramic particle
reinforcement and the irregular nature of the particles along the
matrix material that contribute to its low density is the main problem
which leads to difficulties in machining process. This paper examined
the tool wear when milling AlSi/AlN Metal Matrix Composite using
a TiB2 (Titanium diboride) coated carbide cutting tool. The volume
of the AlN reinforced particle was 10% and milling process was
carried out under dry cutting condition. The TiB2 coated carbide
insert parameters used were at the cutting speed of (230, 300 and
370m/min, feed rate of 0.8, Depth of Cut (DoC) at 0.4m). The
Sometech SV-35 video microscope system used to quantify of the
tool wear. The result shown that tool life span increasing with the
cutting speeds at (370m/min, feed rate of 0.8mm/tooth and DoC at
0.4mm) which constituted an optimum condition for longer tool life
lasted until 123.2 mins. Meanwhile, at medium cutting speed which
at 300m/m, feed rate of 0.8mm/tooth and depth of cut at 0.4mm we
found that tool life span lasted until 119.86 mins while at low cutting
speed it lasted in 119.66 mins. High cutting speed will give the best
parameter in cutting AlSi/AlN MMCs material. The result will help
manufacturers in machining process of AlSi/AlN MMCs materials.
Abstract: Metal matrix composites (MMCs) have gained a
considerable interest in the last three decades. Conventional powder
metallurgy production route often involves the addition of reinforcing
phases into the metal matrix directly, which leads to poor wetting
behavior between ceramic phase and metal matrix and the
segregation of reinforcements. The commonly used elements for
ceramic phase formation in iron based MMCs are Ti, Nb, Mo, W, V
and C, B. The aim of the present paper is to investigate the effect of
sintering temperature and V-B addition on densification, phase
development, microstructure, and hardness of Fe–V-B composites
(Fe-(5-10) wt. %B – 25 wt. %V alloys) prepared by powder
metallurgy process. Metal powder mixes were pressed uniaxial and
sintered at different temperatures (ranging from 1300 to 1400ºC) for
1h. The microstructure of the (V, B) Fe composites was studied with
the help of high magnification optical microscope and XRD.
Experimental results show that (V, B) Fe composites can be produced
by conventional powder metallurgy route.
Abstract: This paper reports the optimal process conditions for machining of three different types of MMC’s 65vol%SiC/A356.2; 10vol%SiC-5vol%quartz/Al and 30vol%SiC/A359 using PMEDM process. MRR, TWR, SR and surface integrity were evaluated after each trial and contributing process parameters were identified. The four responses were then collectively optimized using TOPSIS and optimal process conditions were identified for each type of MMC. The density of reinforced particles shields the matrix material from spark energy hence the high MRR and SR was observed with lowest reinforced particle. TWR was highest with Cu-Gr electrode due to disintegration of the weakly bonded particles in the composite electrode. Each workpiece was examined for surface integrity and ranked as per severity of surface defects observed and their rankings were used for arriving at the most optimal process settings for each workpiece.