Abstract: The objective of this research was to study influence
parameters affecting to mechanical property of austenitic stainless
steel grade 304 (AISI 304) with Gas Metal Arc Welding (GMAW).
The research was applying factorial design experiment, which have
following interested parameters: welding current at 80, 90, and 100
Amps, welding speeds at 250, 300, and 350 mm/min, and shield gas
of 75% Ar + 25% CO2, 70% Ar + 25% CO2 + 5% O2 and 69.5% Ar +
25% CO2 + 5% O2 + 0.5% He gas. The study was done in following
aspects: ultimate tensile strength and elongation. A research study of
ultimate tensile strength found that main factor effect, which had the
highest strength to AISI 304 welding was shield gas of 70% Ar +
25% CO2 + 5% O2 at average of 954.81 N/mm2. Result of the highest
elongation was showed significantly different at interaction effect
between shield gas of 69.5%Ar+25%CO2+5%O2+.5%He and
welding speed at 250 mm/min at 47.94%.
Abstract: In this study, some physical and mechanical properties
of jujube fruits, were measured and compared at constant moisture
content of 15.5% w.b. The results showed that the mean length, width
and thickness of jujube fruits were 18.88, 16.79 and 15.9 mm,
respectively. The mean projected areas of jujube perpendicular to
length, width, and thickness were 147.01, 224.08 and 274.60 mm2,
respectively. The mean mass and volume were 1.51 g and 2672.80
mm3, respectively. The arithmetic mean diameter, geometric mean
diameter and equivalent diameter varied from 14.53 to 20 mm, 14.5
to 19.94 mm, and 14.52 to 19.97 mm, respectively. The sphericity,
aspect ratio and surface area of jujube fruits were 0.91, 0.89 and
926.28 mm2, respectively. Whole fruit density, bulk density and
porosity of jujube fruits were measured and found to be 1.52 g/cm3,
0.3 g/cm3 and 79.3%, respectively. The angle of repose of jujube fruit
was 14.66° (±0.58°). The static coefficient of friction on galvanized
iron steel was higher than that on plywood and lower than that on
glass surface. The values of rupture force, deformation, hardness and
energy absorbed were found to be between 11.13-19.91N, 2.53-
4.82mm, 3.06-5.81N mm and 20.13-39.08 N/mm, respectively.
Abstract: A hardware efficient, multi mode, re-configurable
architecture of interleaver/de-interleaver for multiple standards,
like DVB, WiMAX and WLAN is presented. The interleavers
consume a large part of silicon area when implemented by using
conventional methods as they use memories to store permutation
patterns. In addition, different types of interleavers in different
standards cannot share the hardware due to different construction
methodologies. The novelty of the work presented in this paper is
threefold: 1) Mapping of vital types of interleavers including
convolutional interleaver onto a single architecture with flexibility
to change interleaver size; 2) Hardware complexity for channel
interleaving in WiMAX is reduced by using 2-D realization of the
interleaver functions; and 3) Silicon cost overheads reduced by
avoiding the use of small memories. The proposed architecture
consumes 0.18mm2 silicon area for 0.12μm process and can
operate at a frequency of 140 MHz. The reduced complexity helps
in minimizing the memory utilization, and at the same time
provides strong support to on-the-fly computation of permutation
patterns.
Abstract: Gold coated silica core nanoparticles have an optical
response dictated by the plasmon resonance. The wavelength at
which the resonance occurs depends on the core and shell sizes,
allowing nanoshells to be tailored for particular applications. The
purposes of this study was to synthesize and use different
concentration of gold nanoshells as exogenous material for skin
tissue soldering and also to examine the effect of laser soldering
parameters on the properties of repaired skin. Two mixtures of
albumin solder and different concentration of gold nanoshells were
prepared. A full thickness incision of 2×20 mm2 was made on the
surface and after addition of mixtures it was irradiated by an 810nm
diode laser at different power densities. The changes of tensile
strength σt due to temperature rise, number of scan (Ns), and scan
velocity (Vs) were investigated. The results showed at constant laser
power density (I), σt of repaired incisions increases by increasing the
concentration of gold nanoshells, Ns and decreasing Vs. It is therefore
important to consider the trade off between the scan velocity and the
surface temperature for achieving an optimum operating condition. In
our case this corresponds to σt =1610 gr/cm2 at I~ 60 Wcm-2, T ~
65ºC, Ns =10 and Vs=0.2mms-1.
Abstract: We present a dextran modified silicon microring
resonator sensor for high density antibody immobilization. An array
of sensors consisting of three sensor rings and a reference ring was
fabricated and its surface sensitivity and the limit of detection were
obtained using polyelectrolyte multilayers. The mass sensitivity and
the limit of detection of the fabricated sensor ring are 0.35 nm/ng
mm-2 and 42.8 pg/mm2 in air, respectively. Dextran modified sensor
surface was successfully prepared by covalent grafting of oxidized
dextran on 3-aminopropyltriethoxysilane (APTES) modified silicon
sensor surface. The antibody immobilization on hydrogel dextran
matrix improves 40% compared to traditional antibody
immobilization method via APTES and glutaraldehyde linkage.
Abstract: Some physical properties of musk lime (Citrus
microcarpa) were determined in this study. The average moisture
content (wet basis) of the fruit was found to be 85.10 (±0.72) %. The
mean of length, width and thickness of the fruit was 26.36 (±0.97),
26.40 (±1.04) and 25.26 (±0.94) mm respectively. The average value
for geometric mean diameter, sphericity, aspect ratio, mass, surface
area, volume, true density, bulk density and porosity was 26.00
(±0.82) mm, 98.67 (±2.04) %, 100.23 (±3.28) %, 10.007 (±0.878) g,
2125.07 (±133.93) mm2, 8800.00 (±731.82) mm3, 1002.87 (±39.16)
kgm-3, 501.70 (±22.58) kgm-3 and 49.89 (±3.15) % respectively.
The coefficient of static friction on four types of structural surface
was found to be varying from 0.238 (±0.025) for glass to 0.247
(±0.024) for steel surface.
Abstract: Laser soldering is based on applying some soldering material (albumin) onto the approximated edges of the cut and heating the solder (and the underlying tissues) by a laser beam. Endogenous and exogenous materials such as indocyanine green (ICG) are often added to solders to enhance light absorption. Gold nanoshells are new materials which have an optical response dictated by the plasmon resonance. The wavelength at which the resonance occurs depends on the core and shell sizes, allowing nanoshells to be tailored for particular applications. The purposes of this study was use combination of ICG and different concentration of gold nanoshells for skin tissue soldering and also to examine the effect of laser soldering parameters on the properties of repaired skin. Two mixtures of albumin solder and different combinations of ICG and gold nanoshells were prepared. A full thickness incision of 2×20 mm2 was made on the surface and after addition of mixtures it was irradiated by an 810nm diode laser at different power densities. The changes of tensile strength σt due to temperature rise, number of scan (Ns), and scan velocity (Vs) were investigated. The results showed at constant laser power density (I), σt of repaired incisions increases by increasing the concentration of gold nanoshells in solder, Ns and decreasing Vs. It is therefore important to consider the tradeoff between the scan velocity and the surface temperature for achieving an optimum operating condition. In our case this corresponds to σt =1800 gr/cm2 at I~ 47 Wcm-2, T ~ 85ºC, Ns =10 and Vs=0.3mms-1.
Abstract: This paper describes a low-voltage and low-power
channel selection analog front end with continuous-time low pass
filters and highly linear programmable gain amplifier (PGA). The
filters were realized as balanced Gm-C biquadratic filters to achieve a
low current consumption. High linearity and a constant wide
bandwidth are achieved by using a new transconductance (Gm) cell.
The PGA has a voltage gain varying from 0 to 65dB, while
maintaining a constant bandwidth. A filter tuning circuit that requires
an accurate time base but no external components is presented.
With a 1-Vrms differential input and output, the filter achieves
-85dB THD and a 78dB signal-to-noise ratio. Both the filter and PGA
were implemented in a 0.18um 1P6M n-well CMOS process. They
consume 3.2mW from a 1.8V power supply and occupy an area of
0.19mm2.
Abstract: According to the masonry standard the compressive
strength is basically dependent on factors such as the mortar strength
and the relative values of unit and mortar strength. However
interlocking brick has none or less use of mortar. Therefore there is a need to investigate the behavior of masonry walls using interlocking
bricks. In this study a series of tests have been conducted; physical
properties and compressive strength of brick units and masonry walls
were constructed from interlocking bricks and tested under constant
vertical load at different eccentricities. The purpose of the
experimental investigations is to obtain the force displacement curves, analyze the behavior of masonry walls. The results showed
that the brick is categorized as common brick (BS 3921:1985) and severe weathering grade (ASTM C62). The maximum compressive stress of interlocking brick wall is 3.6 N/mm2 and fulfilled the requirement of standard for residential building.
Abstract: To compare Healing Effects of an
Ayurvedic Preparation and Silver Sulfadiazine on burn wounds in
Albino Rats.
Methods: Albino rats– 30 male / female rats weighing between
150-200 g were used in the study. They were individually housed and
maintained on normal diet and water ad libitum. Partial thickness
burn wounds were inflicted, on overnight-starved animals under
pentobarbitone (30mg/kg, i.p.) anaesthesia, by pouring hot molten
wax at 80oC into a plastic cylinder of 300 mm2 circular openings
placed on the shaven back of the animal. Apart from the drugs under
investigation no local/ systemic chemotherapeutic cover will be
provided to animals. All the animals were assessed for the percentage
of wound contraction, signs of infection, scab formation and
histopathological examination.
Results: Percentage of wound healing was significantly better in
the test ointment group compared to the standard. Signs of infection
were observed in more animals in the test ointment group compared
to the standard. Scab formation also took place earlier in the test
ointment group compared to standard. Epithelial regeneration and
healing profile was better in the test ointment compared to the
standard. Moreover the test ointment group did not show any raised
margins in the wound or blackish discoloration as was observed in
silver sulfadiazine group.
Conclusion: The burn wound healing effect of the ayurvedic
ointment under study is better in comparison to standard therapy of
silver sulfadiazine. The problem of infection encountered with the
test ointment can be overcome by changing the concentrations and
proportions of the ingredients in the test ointment which constitutes
the further plan of the study.