Abstract: During the interim storage or final disposal of low level waste, migration/diffusion of radionuclides can occur when the waste comes in contact with water. The long-term leaching behaviour into surrounding fluid (demineralized water) of 137Cs, 60Co and 152Eu radionuclides, artificially incorporated in mortar matrices made from natural aggregates (river sand) and recycled radioactive concrete was studied. Results presented in this work are obtained in two years of mortar testing and will be used for the safety increasing in the storage of low level radioactive waste. The study involved the influence of curing time, type and size distribution of the aggregates on leaching behaviour. The mortar samples were immersed in distilled water for 30 days. The leached activity of the mortar samples was measured on samples from the immersing water and analyzed through a gamma-ray spectrometry method using an HPGe detector with a GESPECOR code for efficiency evaluation. The long-term leaching behaviour of the radionuclides was evaluated from the leaching data calculating the apparent diffusion coefficient.
Abstract: The morphology, mineralogical and chemical
composition of a low-grade nickel ore from Mpumalanga, South
Africa, were studied by scanning electron microscope (SEM), X-ray
diffraction (XRD) and X-ray fluorescence (XRF), respectively. The
ore was subjected to atmospheric agitation leaching using sulphuric
acid to investigate the effects of acid concentration, leaching
temperature, leaching time and particle size on extraction of nickel
and cobalt. Analyses results indicated the ore to be a saprolitic nickel
laterite belonging to the serpentine group of minerals. Sulphuric acid
was found to be able to extract nickel from the ore. Increased acid
concentration and temperature only produced low amounts of nickel
but improved cobalt extraction. As high as 77.44% Ni was achieved
when leaching a -106+75μm fraction with 4.0M acid concentration at
25oC. The kinetics of nickel leaching from the saprolitic ore were
studied and the activation energy was determined to be 18.16kJ/mol.
This indicated that nickel leaching reaction was diffusion controlled.