Abstract: This research was to evaluate a technical feasibility of
making single-layer experimental particleboard panels from bamboo
waste (Dendrocalamus asper Backer) by converting bamboo into
strips, which are used to make laminated bamboo furniture. Variable
factors were density (600, 700 and 800 kg/m3) and temperature of
condition (25, 40 and 55 °C). The experimental panels were tested for
their physical and mechanical properties including modulus of
elasticity (MOE), modulus of rupture (MOR), internal bonding
strength (IB), screw holding strength (SH) and thickness swelling
values according to the procedures defined by Japanese Industrial
Standard (JIS). The test result of mechanical properties showed that
the MOR, MOE and IB values were not in the set criteria, except the
MOR values at the density of 700 kg/m3 at 25 °C and at the density
of 800 kg/m3 at 25 and 40 °C, the IB values at the density of 600
kg/m3, at 40 °C, and at the density of 800 kg/m3 at 55 °C. The SH
values had the test result according to the set standard, except with
the density of 600 kg/m3, at 40 and 55 °C. Conclusively, a valuable
renewable biomass, bamboo waste could be used to manufacture
boards.
Abstract: This research studied the appropriate factors and conditions for laminated bamboo bending by Design of Experiments (DOE). The interested factors affecting the spring back in laminates bamboo were (1) time, (2) thickness, and (3) frequency. This experiment tested the specimen by using high frequency machine and measured its spring back immediately and next 24 hours for comparing the spring back ratio. Results from the experiments showed that significant factors having major influence to bending of laminates bamboo were thickness and frequency. The appropriate conditions of thickness and frequency were 4 mm. and 1.5 respectively.
Abstract: A new generation product made from bamboo strips,
known as laminated bamboo, has gained importance. The objective
of this research was to experiment the effect of three factors on the
mechanical property of laminated bamboo. The interested factors for
experimental design were (A) four bamboo species, namely Bambusa
blumeana Schultes (Pai See Suk), Dendrocalamus asper Backer (Pai
Tong), Dendrocalamus hamiltonii Nees (Pai Hok) and
Dendrocalamus sericeus Munro (Pai Sang Mon), (B) two types of
glue adhesive, polyvinyl acetate emulsion (PVAC) fortified with
urea-formaldehyde (UF) and urea-formaldehyde (UF) to make
parallel-oriented bamboo strips laminates and (C) glue weight per
strip area, 150 g/m2 and 190 g/m2. Experimental results showed that
Dendrocalamus asper Backer (Pai Tong) and Dendrocalamus
sericeus Munro (Pai Sang Mon) were best used for manufacturing
due to their highest MOR and MOE. The amount of glue weight 150
g/m2 yielded higher MOR and MOE than the amount of glue weight
190 g/m2. At the conclusion, the laminated bamboo manufacturers
can benefit from this research in order to select right materials
according to strength, cost and accessibility.