Abstract: This paper reports the production of uranium-molybdenum alloys, which have been considered promising fuel for test and research nuclear reactors. U-Mo alloys were produced in three molybdenum contents: 5 wt.%, 7 wt.%, and 10 wt.%, using an electric vacuum induction furnace. A boron nitride-coated graphite crucible was employed in the production of the alloys and, after melting, the material was immediately poured into a boron nitride-coated graphite mold. The incorporation of carbon was observed, but it happened in a lower intensity than in the case of the non-coated crucible/mold. It is observed that the carbon incorporation increased and alloys density decreased with Mo addition. It was also noticed that the increase in the carbon or molybdenum content did not seem to change the as-cast structure in terms of granulation. The three alloys presented body-centered cubic crystal structure (g phase), after solidification, besides a seeming negative microsegregation of molybdenum, from the center to the periphery of the grains. There were signs of macrosegregation, from the base to the top of the ingots.
Abstract: Considering palm oil as non-drying oil owing to its
low iodine value, an attempt was taken to increase the unsaturation in
the fatty acid chains of palm oil for the preparation of alkyds. To
increase the unsaturation in the palm oil, sulphuric acid (SA) and
para-toluene sulphonic acid (PTSA) was used prior to alcoholysis for
the dehydration process. The iodine number of the oil samples was
checked for the unsaturation measurement by Wijs method. Alkyd
resin was prepared using the dehydrated palm oil by following
alcoholysis and esterification reaction. To improve the film properties
0.5wt.% multi-wall carbon nano tubes (MWCNTs) were used to
manufacture polymeric film. The properties of the resins were
characterized by various physico-chemical properties such as density,
viscosity, iodine value, saponification value, etc. Structural
elucidation was confirmed by Fourier transform of infrared
spectroscopy and proton nuclear magnetic resonance; surfaces of the
films were examined by field-emission scanning electron microscope.
In addition, pencil hardness and chemical resistivity was also
measured by using standard methods. The effect of enhancement of
the unsaturation in the fatty acid chain found significant and
motivational. The resin prepared with dehydrated palm oil showed
improved properties regarding hardness and chemical resistivity
testing. The incorporation of MWCNTs enhanced the thermal
stability and hardness of the films as well.