Abstract: The present study evaluates the properties of class F fly ash as a replacement of natural materials in civil engineering construction industry. The low-lime flash similar to class F is the prime variety generated in India, although it has significantly smaller volumes of high-lime fly ash as compared to class C. The chemical and physical characterization of the sample is carried out with the number of experimental approaches in order to investigate all relevant features present in the samples. For chemical analysis, elementary quantitative results from point analysis and scanning electron microscopy (SEM)/dispersive spectroscopy (EDS) techniques were used to identify the element images of different fractions. The physical properties found very close to the range of common soils. Furthermore, the fly ash-based bricks were prepared by the same sample of class F fly ash and the results of compressive strength similar to that of Standard Clay Brick Grade 1 available in the local market of India.
Abstract: This paper presents the effects of mixing procedures
on mechanical properties of flyash-based geopolymer matrices
containing nanosilica (NS) at 0.5%, 1.0%, 2.0%, and 3.0% by weight.
Comparison is made with conventional mechanical dry-mixing of NS
with flyash and wet-mixing of NS in alkaline solutions. Physical and
mechanical properties are investigated using X-Ray Diffraction
(XRD) and Scanning Electron Microscope (SEM). Results show that
generally the addition of NS particles enhanced the microstructure
and improved flexural and compressive strengths of geopolymer
nanocomposites. However, samples, prepared using dry-mixing
approach, demonstrate better physical and mechanical properties
comparing to wet-mixing samples.
Abstract: This paper presents the results of an experimental
investigation carried out to evaluate the shrinkage of High Strength
Concrete. High Strength Concrete is made by partially replacement of
cement by flyash and silica fume. The shrinkage of High Strength
Concrete has been studied using the different types of coarse and fine
aggregates i.e. Sandstone and Granite of 12.5 mm size and Yamuna
and Badarpur Sand. The Mix proportion of concrete is 1:0.8:2.2 with
water cement ratio as 0.30. Superplasticizer dose @ of 2% by weight
of cement is added to achieve the required degree of workability in
terms of compaction factor.
From the test results of the above investigation it can be concluded
that the shrinkage strain of High Strength Concrete increases with
age. The shrinkage strain of concrete with replacement of cement by
10% of Flyash and Silica fume respectively at various ages are more
(6 to 10%) than the shrinkage strain of concrete without Flyash and
Silica fume. The shrinkage strain of concrete with Badarpur sand as
Fine aggregate at 90 days is slightly less (10%) than that of concrete
with Yamuna Sand. Further, the shrinkage strain of concrete with
Granite as Coarse aggregate at 90 days is slightly less (6 to 7%) than
that of concrete with Sand stone as aggregate of same size. The
shrinkage strain of High Strength Concrete is also compared with that
of normal strength concrete. Test results show that the shrinkage
strain of high strength concrete is less than that of normal strength
concrete.