Abstract: Chromium bearing Austempered Ductile Iron (ADI) has been recently in the news for its improved wear performance over the ADI. The work presented below was taken up to study the effect of different austenitisation temperatures on the microstructure and wear performance of the Carbidic Austempered Ductile Iron (CADI). In this investigation Cr bearing ductile iron was subjected to austempering treatment to obtain an ausferritic microstructure. Two different austenitisation temperatures were selected whereas, the austempering temperature and time was kept unchanged. Microstructure and wear performance of this alloy, austenitized at two different temperatures was studied.
Abstract: The aim of this investigation is to study the
performance of the new generation of the PVD coated grade and to
map the influence of cutting conditions on the tool life in milling of
ADI (Austempered Ductile Iron). The results show that chipping is
the main wear mechanism which determines the tool life in dry
condition and notch wear in wet condition for this application. This
due to the different stress mechanisms and preexisting cracks in the
coating. The wear development shows clearly that the new PVD
coating (C20) has the best ability to delay the chipping growth. It
was also found that a high content of Al in the new coating (C20)
was especially favorable compared to a TiAlN multilayer with lower
Al content (C30) or CVD coating. This is due to fine grains and low
compressive stress level in the coating which increase the coating
ability to withstand the mechanical and thermal impact. It was also
found that the use of coolant decreases the tool life with 70-80%
compare to dry milling.