Abstract: The dominant judgment for earthquake damaged reinforced concrete (RC) structures is to rebuild them with the new ones. Consequently, this paper estimates if there is chance to repair earthquake RC beams and obtain economical contribution to modern day society. Therefore, the totally damaged (damaged in shear under cyclic load) reinforced concrete (RC) beams repaired and strengthened by externally bonded carbon fibre reinforced polymer (CFRP) strips in this study. Four specimens, apart from the reference beam, were separated into two distinct groups. Two experimental beams in the first group primarily tested up to failure then appropriately repaired and strengthened with CFRP strips. Two undamaged specimens from the second group were not repaired but strengthened by the identical strengthening scheme as the first group for comparison. This study studies whether earthquake damaged RC beams that have been repaired and strengthened will validate similar strength and behavior to equally strengthened, undamaged RC beams. Accordingly, a strength correspondence according to strengthened specimens was acquired for the repaired and strengthened specimens. Test results confirmed that repair and strengthening, which were estimated in the experimental program, were effective for the specimens with the cracking patterns considered in the experimental program.
Abstract: A numerical study is presented on buckling and post
buckling behaviour of laminated carbon fiber reinforced plastic
(CFRP) thin-walled cylindrical shells under axial compression using
asymmetric meshing technique (AMT). Asymmetric meshing
technique is a perturbation technique to introduce disturbance without
changing geometry, boundary conditions or loading conditions.
Asymmetric meshing affects predicted buckling load, buckling mode
shape and post-buckling behaviour. Linear (eigenvalue) and nonlinear
(Riks) analyses have been performed to study the effect of
asymmetric meshing in the form of a patch on buckling behaviour.
The reduction in the buckling load using Asymmetric meshing
technique was observed to be about 15%. An isolated dimple formed
near the bifurcation point and the size of which increased to reach a
stable state in the post-buckling region. The load-displacement curve
behaviour applying asymmetric meshing is quite similar to the curve
obtained using initial geometric imperfection in the shell model.
Abstract: The use of externally bonded Carbon Fiber
Reinforced Polymer (CFRP) reinforcement has proven to be an
effective technique to strengthen steel structures. An experimental
study on CFRP bonded steel plate with double strap joint has been
conducted and specimens are tested under tensile loadings. An
empirical model has been developed using stress-based approach to
predict ultimate capacity of the CFRP bonded steel structure. The
results from the model are comparable with the experimental result
with a reasonable accuracy.
Abstract: In this present study, experimental work was
conducted to study the effectiveness of newly innovated steel-CFRP
composite (CFRP laminates sandwiched between two steel strips) as
stirrups. A total numbers of eight concrete beams were tested under
four point loads. Each beam measured 1600 mm long, 160mm width
and 240 mm depth. The beams were reinforced with different shear
reinforcements; one without stirrups, one with steel stirrups and six
with different types and numbers of steel-CRFR stirrups. Test results
indicated that the steel-CFRP stirrups had enhanced the shear
strength capacity of beams. Moreover, the tests revealed that steel-
CFRP stirrups reached to their ultimate tensile strength unlike FRP
stirrups which rupture at much lower level than their ultimate
strength as werereported in various researches.
Abstract: The machining of Carbon Fiber Reinforced Plastics
has come to constitute a significant challenge for many fields of
industry. The resulting surface finish of machined parts is of primary
concern for several reasons, including contact quality and impact on
the assembly. Therefore, the characterization and prediction of
roughness based on machining parameters are crucial for costeffective
operations. In this study, a PCD tool comprised of two
straight flutes was used to trim 32-ply carbon fiber laminates in a bid
to analyze the effects of the feed rate and the cutting speed on the
surface roughness. The results show that while the speed has but a
slight impact on the surface finish, the feed rate for its part affects it
strongly. A detailed study was also conducted on the effect of fiber
orientation on surface roughness, for quasi-isotropic laminates used
in aerospace. The resulting roughness profiles for the four-ply
orientation lay-up were compared, and it was found that fiber angle is
a critical parameter relating to surface roughness. One of the four
orientations studied led to very poor surface finishes, and
characteristic roughness profiles were identified and found to only
relate to the ply orientations of multilayer carbon fiber laminates.