Abstract: Severe damages may occur during the drilling of carbon fiber reinforced plastics (CFRP). In practice, this damage is limited by adding a backup support to the drilled parts. For some aeronautical parts with curvatures, backing up parts is a demanding process. In order to simplify the operation, this research studies the effect of using a configurable setup to support parts on the resulting quality of drilled holes. The test coupons referenced in this study are twenty four-plies unidirectional laminates made of carbon fibers and epoxy resin. Different signals were measured during the drilling process for these laminates, including the thrust force, the displacement and the acceleration. The processing of these signals demonstrated that the damage is due to the combination of two main factors: the spring-back of the thin part and the thrust force. The results found were confirmed for different feeds and speeds. When the distance between supports is increased, it is observed that the spring-back increases but the thrust force decreases. The study proves the feasibility of unsupported drilling of thin CFRP laminates without creating any observable damage.
Abstract: The machining of Carbon Fiber Reinforced Plastics
has come to constitute a significant challenge for many fields of
industry. The resulting surface finish of machined parts is of primary
concern for several reasons, including contact quality and impact on
the assembly. Therefore, the characterization and prediction of
roughness based on machining parameters are crucial for costeffective
operations. In this study, a PCD tool comprised of two
straight flutes was used to trim 32-ply carbon fiber laminates in a bid
to analyze the effects of the feed rate and the cutting speed on the
surface roughness. The results show that while the speed has but a
slight impact on the surface finish, the feed rate for its part affects it
strongly. A detailed study was also conducted on the effect of fiber
orientation on surface roughness, for quasi-isotropic laminates used
in aerospace. The resulting roughness profiles for the four-ply
orientation lay-up were compared, and it was found that fiber angle is
a critical parameter relating to surface roughness. One of the four
orientations studied led to very poor surface finishes, and
characteristic roughness profiles were identified and found to only
relate to the ply orientations of multilayer carbon fiber laminates.