Abstract: In this paper, snow samples containing dust particles
from several sampling points around the city of Ostrava were
analyzed. The pH values of sampled snow were measured and solid
particles analyzed. Particle size, zeta potential and content of selected
heavy metals were determined in solid particles. The pH values of
most samples lay in the slightly acid region. Mean values of particle
size ranged from 290.5 to 620.5 nm. Zeta potential values varied
between -5 and -26.5 mV. The following heavy metal concentration
ranges were found: copper 0.08-0.75 mg/g, lead 0.05-0.9 mg/g,
manganese 0.45-5.9 mg/g and iron 25.7-280.46 mg/g. The highest
values of copper and lead were found in the vicinity of busy
crossroads, and on the contrary, the highest levels of manganese and
iron were detected close to a large steelworks. The proportion
between pH values, zeta potentials, particle sizes and heavy metal
contents was established. Zeta potential decreased with rising pH
values and, simultaneously, heavy metal content in solid particles
increased. At the same time, higher metal content corresponded to
lower particle size.
Abstract: Metallic foams have good potential for lightweight
structures for impact and blast mitigation. Therefore it is important to
find out the optimized foam structure (i.e. cell size, shape, relative
density, and distribution) to maximise energy absorption. In this
paper, quasistatic compression and microstructural characterization
of closed-cell aluminium foams of different pore size and cell
distributions have been carried out. We present results for two
different aluminium metal foams of density 0.49-0.51 g/cc and 0.31-
0.34 g/cc respectively that have been tested in quasi-static
compression. The influence of cell geometry and cell topology on
quasistatic compression behaviour has been investigated using optical
microscope and computed tomography (micro-CT) analysis. It is
shown that the deformation is not uniform in the structure and
collapse begins at the weakest point.
Abstract: In this paper, the effect of WC-12Co particle
temperature in HVOF thermal spraying process on the coating
thickness has been studied. The statistical results show that the spray
distance and oxygen-to-fuel ratio are effective factors on particle
characterization and thickness of HVOF thermal spraying coatings.
Spray Watch diagnostic system, scanning electron microscopy
(SEM), X-ray diffraction and thickness measuring system were used
for this purpose.