Abstract: Commercially SA 516 Grade 70 is frequently used for the manufacturing of pressure vessels, boilers and storage tanks etc. in fabrication industry. Heat input is the major parameter during welding that may bring significant changes in the microstructure as well as the mechanical properties. Different welding technique has different heat input rate per unit surface area. Materials with large thickness are dealt with different combination of welding techniques to achieve required mechanical properties. In the present research two schemes: Scheme 1: SMAW (Shielded Metal Arc Welding) & GTAW (Gas Tungsten Arc Welding) and Scheme 2: SMAW & SAW (Submerged Arc Welding) of hybrid welding techniques have been studied. The purpose of these schemes was to study hybrid welding effect on the microstructure and mechanical properties of the weldment, heat affected zone and base metal area. It is significant to note that the thickness of base plate was 12 mm, also welding conditions and parameters were set according to ASME Section IX. It was observed that two different hybrid welding techniques performed on two different plates demonstrated that the mechanical properties of both schemes are more or less similar. It means that the heat input, welding techniques and varying welding operating conditions & temperatures did not make any detrimental effect on the mechanical properties. Hence, the hybrid welding techniques mentioned in the present study are favorable to implicate for the industry using the plate thickness around 12 mm thick.
Abstract: A series of Ti based shape memory alloys with
composition of Ti50Ni49Cr1, Ti50Ni47Cr3 and Ti50Ni45Cr5 were
developed by vacuum arc-melting under a purified argon atmosphere.
The histometric and corrosion evaluation of Ti-Ni-Cr shape memory
alloys have been considered in this research work. The alloys were
developed by vacuum arc melting and implanted subcutaneously in
rabbits for 4, 8 and 12 weeks. Metallic implants were embedded in
order to determine the outcome of implantation on histometric and
corrosion evaluation of Ti-Ni-Cr metallic strips. Encapsulating
membrane formation around the alloys was minimal in the case of all
materials. After histomorphometric analyses it was possible to
demonstrate that there were no statistically significant differences
between the materials. Corrosion rate was also determined in this
study which is within acceptable range. The results showed the Ti-
Ni-Cr alloy was neither cytotoxic, nor have any systemic reaction on
living system in any of the test performed. Implantation shows good
compatibility and a potential of being used directly in vivo system.