Abstract: Semisolid metal processing uses solid–liquid slurries
containing fine and globular solid particles uniformly distributed in a
liquid matrix, which can be handled as a solid and flow like a liquid.
In the recent years, many methods have been introduced for the
production of semisolid slurries since it is scientifically sound and
industrially viable with such preferred microstructures called
thixotropic microstructures as feedstock materials. One such process
that needs very low equipment investment and running costs is the
cooling slope. In this research by using a mechanical stirrer slurry
maker constructed by the authors, the effects of mechanical stirring
parameters such as: stirring time, stirring temperature and stirring
Speed on micro-structure and mechanical properties of A360
aluminum alloy in semi-solid forming, are investigated. It is
determined that mold temperature and holding time of part in
temperature of 580ºC have a great effect on micro-structure and
mechanical properties(stirring temperature of 585ºC, stirring time of
20 minutes and stirring speed of 425 RPM). By optimizing the
forming parameters, dendrite microstructure changes to globular and
mechanical properties improves. This is because of breaking and
globularzing dendrites of primary α-AL.
Abstract: ZnS nanoparticles of different size have been
synthesized using a colloidal particles method. Zns nanoparticles
prepared with capping agent (mercaptoethanol) then were
characterized using X-ray diffraction (XRD) and UV-Vis
spectroscopy. The particle size of the nanoparticles calculated from
the XRD patterns has been found in the range 1.85-2.44nm.
Absorption spectra have been obtained using UV-Vis
spectrophotometer to find the optical band gap and the obtained
values have been founded to being range 3.83-4.59eV. It was also
found that energy band gap increase with the increase in molar
capping agent solution.
Abstract: Horizontal continuous casting is widely used to
produce semi-finished non-Ferrous products. Homogeneity in the
metallurgical characteristics and mechanical properties for this
product is vital for industrial application. In the present work, the
microstructure and mechanical properties of a horizontal continuous
cast two-phase brass billet have been studied. Impact strength and
hardness variations were examined and the phase composition and
porosity studied with image analysis software. Distinct differences in
mechanical properties were observed between the upper, middle and
lower parts of the billet, which are explained in terms of the
morphology and size of the phase in the microstructure. Hardness
variation in the length of billet is higher in upper area but impact
strength is higher in lower areas.