Abstract: Restoration of endodontically treated teeth is a
common problem in dentistry, related to the fractures occurring in
such teeth and to concentration of forces little information regarding
variation of basic preparation guidelines in stress distribution has
been available. To date, there is still no agreement in the literature
about which material or technique can optimally restore
endodontically treated teeth. The aim of the present study was to
evaluate the influence of the core height and restoration materials on
corono-radicular restored upper first premolar. The first step of the
study was to achieve 3D models in order to analyze teeth, dowel and
core restorations and overlying full ceramic crowns. The FEM model
was obtained by importing the solid model into ANSYS finite
element analysis software. An occlusal load of 100 N was conducted,
and stresses occurring in the restorations, and teeth structures were
calculated. Numerical simulations provide a biomechanical
explanation for stress distribution in prosthetic restored teeth. Within
the limitations of the present study, it was found that the core height
has no important influence on the stress generated in coronoradicular
restored premolars. It can be drawn that the cervical regions
of the teeth and restorations were subjected to the highest stress
concentrations.
Abstract: Cast metal inlays can be used on molars requiring a
class II restoration instead amalgam and offer a durable alternative.
Because it is known that class II inlays may increase the
susceptibility to fracture, it is important to ensure optimal
performance in selection of the adequate preparation design to reduce
stresses in teeth structures and also in the restorations. The aim of the
study was to investigate the influence of preparation design on stress
distribution in molars with different class II preparations and in cast
metal inlays. The first step of the study was to achieve 3D models in
order to analyze teeth and cast metal class II inlays. The geometry of
the intact tooth was obtained by 3D scanning using a manufactured
device. With a NURBS modeling program the preparations and the
appropriately inlays were designed. 3D models of first upper molars
of the same shape and size were created. Inlay cavities designs were
created using literature data. The geometrical model was exported
and the mesh structure of the solid 3D model was created for
structural simulations. Stresses were located around the occlusal
contact areas. For the studied cases, the stress values were not
significant influenced by the taper of the preparation. it was
demonstrated stresses are higher in the cast metal restorations and
therefore the strength of the teeth is not affected.
Abstract: Simulation of occlusal function during laboratory
material-s testing becomes essential in predicting long-term
performance before clinical usage. The aim of the study was to assess
the influence of chamfer preparation depth on failure risk of heat
pressed ceramic crowns with and without zirconia framework by
means of finite element analysis. 3D models of maxillary central
incisor, prepared for full ceramic crowns with different depths of the
chamfer margin (between 0.8 and 1.2 mm) and 6-degree tapered
walls together with the overlying crowns were generated using
literature data (Fig. 1, 2). The crowns were designed with and
without a zirconia framework with a thickness of 0.4 mm. For all
preparations and crowns, stresses in the pressed ceramic crown,
zirconia framework, pressed ceramic veneer, and dentin were
evaluated separately. The highest stresses were registered in the
dentin. The depth of the preparations had no significant influence on
the stress values of the teeth and pressed ceramics for the studied
cases, only for the zirconia framework. The zirconia framework
decreases the stress values in the veneer.
Abstract: Minor problems arising from optimizations by
welding of fixed prostheses frameworks can be identified by
macroscopic and microscopic visual inspection. The purpose of this
study was to highlight the visible discontinuities present in the laser
welds of dental Ni-Cr alloys. Ni-Cr base metal alloys designated for
fixed prostheses manufacture were selected for the experiments.
Using cast plates, preliminary tests were conducted by laser welding.
Macroscopic visual inspection was done carefully to assess the
defects of the welding rib. Electron microscopy images allowed
visualization of small discontinuities, which escapes visual
inspection. Making comparison to Ni-Cr alloys taken in the
experiment and laser welded, after visual analysis, the best welds
appear for Heraenium NA alloy.