Abstract: The aim of the present study was to investigate the dissolution kinetics of ulexite in sodium dihydrogen phosphate in a mechanical agitation system and also to declare an alternative reactant to produce the boric acid. Reaction temperature, concentration of sodium dihydrogen phosphate, stirring speed, solid-liquid ratio, and ulexite particle size were selected as parameters. The experimental results were successfully correlated by using linear regression and a statistical program. Dissolution curves were evaluated in order to test the shrinking core models for solid-fluid systems. It was observed that increase in the reaction temperature and decrease in the solid/liquid ratio causes an increase in the dissolution rate of ulexite. The activation energy was found to be 36.4 kJ/mol. The leaching of ulexite was controlled by diffusion through the ash (or product) layer.
Abstract: Ulexite (Na2O.2CaO.5B2O3.16H2O) is boron mineral
that is found in large quantities in the Turkey and world. In this
study, the dissolution of this mineral in the disodium hydrogen
phosphate solutions has been studied. Temperature, concentration,
stirring speed, solid liquid ratio and particle size were selected as
parameters. The experimental results were successfully correlated by
linear regression using Statistica program. Dissolution curves were
evaluated shrinking core models for solid-fluid systems. It was
observed that increase in the reaction temperature and decrease in the
solid/liquid ratio causes an increase the dissolution rate of ulexite.
The activation energy was found to be 63.4 kJ/mol. The leaching of
ulexite was controlled by chemical reaction.
Abstract: Gypsum (CaSO4.2H2O) is a mineral that is found in
large quantities in the Turkey and in the World. In this study, the
dissolution of this mineral in the diammonium hydrogen phosphate
solutions has been studied. The dissolution and dissolution kinetics of
gypsum in diammonium hydrogen phosphate solutions will be useful
for evaluating of solid wastes containing gypsum. Parameters such as
diammonium hydrogen phosphate concentration, temperature and
stirring speed affecting on the dissolution rate of the gypsum in
diammonium hydrogen phosphate solutions were investigated. In
experimental studies have researched effectiveness of the selected
parameters. The dissolution of gypsum were examined in two parts at
low and high temperatures. The experimental results were
successfully correlated by linear regression using Statistica program.
Dissolution curves were evaluated shrinking core models for solidfluid
systems. The activation energy was found to be 34.58 kJ/mol
and 44.45 kJ/mol for the low and the high temperatures. The
dissolution of gypsum was controlled by chemical reaction both low
temperatures and high temperatures.