Abstract: In the present work the internal sulfate attack on
pastes made from pure clinker phases was studied. Two binders were
produced: (a) a binder with 2% C3A and 18% C4AF content; (b) a
binder with 10% C3A and C4AF content each. Gypsum was used as
the sulfate bearing compound, while calcium carbonate added to
differentiate the binders produced. The phases formed were identified
by XRD analysis. The results showed that ettringite was the
deterioration phase detected in the case of the low C3A content
binder. Carbonation occurred in the specimen without calcium
carbonate addition, while portlandite was observed in the one
containing calcium carbonate. In the case of the high C3A content
binder, traces of thaumasite were detected when calcium carbonate
was not incorporated in the binder. A solid solution of thaumasite and
ettringite was found when calcium carbonate was added. The amount
of C3A had not fully reacted with sulfates, since its corresponding
peaks were detected.