Phase Formation of Ba(Ce1-xZrx)0.90Y0.1O3-δ Prepared by a Modified Sol-Gel Method

The powders of Ba(Ce1-xZrx)0.90Y0.1O3-δ (BCZY) with 0.2 ≤ x ≤ 0.6 have been prepared by a modified sol-gel method. Triethylenetetramine (TETA) was employed as chelating agent. Phase formation of calcined powders at 1100oC and sintered pellets at 1400oC of BCZY were examined by an X-ray diffractrometer (XRD). XRD results showed the calcined powder and sintered pellet formed a single perovskite phase over the entire range of x values. As the amount of zirconium substitution (x values) increase, the main peaks are shifted to the higher 2theta values which suggest a complete substitution of zirconium into cerium sites. All the obtained calcined powders and sintered pellets possess cubic structure (Pm-3m) at all x values.

Cutting Tools in Finishing Operations for CNC Rapid Manufacturing Processes: Experimental Studies

This paper reports an advanced approach in the application of CNC machining for rapid manufacturing processes (CNC-RM). The aim of this study is to improve the quality of machined parts by introducing different cutting tools during finishing operations. As the cutting is performed in different directions, the surfaces presented on part can be classified into several categories. Therefore, suitable cutting tools are assigned to machine particular surfaces and to improve the quality. Experimental studies have been carried out by fabricating several parts based on the suggested approach. The results provide further support for implementing this approach in rapid machining processes.

Effect of Heat Treatment on the Phase Formation of La0.6Sr0.4CoO3-α

Powder of La0.6Sr0.4CoO3-α (LSCO) was synthesized by a combined citrate-EDTA method. The as-synthesized LSCO powder was calcined, respectively at temperatures of 800, 900 and 1000 °C with different heating/cooling rates which are 2, 5, 10 and 15 °C min-1. The effects of heat treatments on the phase formation of perovskite phase of LSCO were investigated by powder X-ray diffraction (XRD). The XRD patterns revealed that the rate of 5 °C min-1 is the optimum heating/cooling rate to obtain a single perovskite phase of LSCO with calcination temperature of 800 °C. This result was confirmed by a thermogravimetric analysis (TGA) as it showed a complete decomposition of intermediate compounds to form oxide material was also observed at 800 °C.